The results showed that the fracture toughness of the weld of HFW pipe was lowest.The value of absorbed energy of HFW weld was closely related to the heat treatment process.But the fracture toughness of fusion zone of submerged-arc welded jointer,its microstructure was coarse granular bainite,and was lower than the other locations of heat affected zone;and with the increasing of steel strength,the effect of welding heat cycles on the pipeline steel became stronger,and form coarse microstructure in fusion zone leading to decrease fracture toughness.

结果表明，高钢级管线钢高频焊接焊缝处的断裂韧性最低，其冲击功大小与热处理工艺密切相关；而埋弧焊接热影响区断裂韧性在熔合线处最低，其主要原因是此处的组织为粗大的粒状贝氏体，而且强度越高焊接热循环对管线钢的作用越强，在熔合线附近更容易产生粗大组织，使断裂韧性降低。

Based on the system of Na2O-Al2O3-SiO2 and both the crystal nucleus agent and complex fining agent,nepheline glass-ceramics in prepared though high temperature meltiong and two steps of heat treatment,and it possesses high compressive strength and high bending resistance.

本文以Na2O－Al2O3－SiO2系统为基础，引入晶核剂和复合澄清剂，经高温熔制和两步热处理制备的霞石微晶玻璃，具有较高的抗压和抗折强度。

The strengthening effect is attributed to recrystallization and the shape of pores during heat-treatment at 1800℃.

在1800℃真空热处理过程中发生的碳化硅再结晶以及气孔形状的变化，是其强度较高的主要原因。

Its mechanism strength and hot stability big city ratio commonness flat plate glass high,inspite of fracture know clearly,fragment submit analogy alveolate obtuse angle smallness grain,not easy injury human,it is versus his heat treatment to it was application compare expand'one strain security glass that so .modern times produce craft prime,but his operate refuse be out of condition to ConTRoL,effort of both especially yes uniformity be heated and celerity cooling.

它的机械强度和热稳定性都比普通平板玻璃高，即使破碎了，碎片呈类似蜂窝状的钝角小颗粒，不易伤人，所以是应用较广的一种安全玻璃。现代生产工艺主要是对其热处理，但其操作却不好控制，尤其是均匀受热和快速冷却。

The coarse needle-like or nubby Al9FeNi phase existed in the cast microstructure of high content Fe and Ni alloy 2618(2#). After hot extrusion, it was broken into coarse multi-angle Al9FeNi particles. The contents of Fe and Ni have no effect on aging characteristic and the hardness of the alloy after aging.

含锆的高铁、镍2618合金经熔体高温过热处理后(4#)，在合金铸态组织中获得均匀细小的针片状Al_9FeNi相，热挤压后获得均匀细小的颗粒Al_9FeNi相；弥散Al_3Zr粒子的存在可使2618合金得到细小的再结晶晶粒组织，该合金既可获得较高的高温强度，还可获得较高的延伸率。

Was investigated.The result shows that for thin plates,The strength of the plates decrease and the plasticity increase with anneal temperatare rising,while thick plates is not so sensitive to anneal temperature.The variation of heat-treatment parametar has less effect on the microstructure of TA15 plate.Thin plates have higher strength and lower plasticity longitudinally and transversally, and lower strength ...

结果表明，对于薄板而言提高退火温度材料强度降低、塑性提高，而对厚板这种现象不明显；热处理参数的变化对TA15合金板材的显微组织影响不大；薄板沿纵向和横向强度值较高，塑性值偏低，而45°方向强度值偏低，塑性较好；厚板横向强度值较纵向、45°方向的要高。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。