Several common problems in alkaline tin plating on copper foil were listed, for example, the golden yellow passivation film on anode becomes thin, black, and even disappears; the deposit is dark-gray and spongy, and so on.

列举了紫铜箔碱性镀锡过程中出现的几种常见问题，如：阳极表面金黄色钝化膜变淡甚至变黑，镀层呈暗灰色海绵状等。

Nursery bed design, Manufacture and installation, greenhouse material used hot dip galvanized steel pipe, spare parts, as hot-dip galvanized or plastic packet processing, and prolong the service life.

育苗床的设计、制造安装，温室大棚材料采用热浸镀锌钢管，零配件经热浸镀锌或包塑处理，从而延长了使用寿命。

During the process of acidic potassium chloride zinc plating for iron workpiece,the deposit obtained at low current density was shown to be foggy with white spots,and the phenomena failed to disappear even after bright dipping and passivation in nitric acid.

在对某铁件制品进行酸性氯化钾镀锌过程中，镀层出现低位发雾，而且有白斑，在硝酸出光及钝化后依然存在。

When used in superabrasive grits synthesizing, especially in the case of cubic boron nitride, the consumption of anvils can be decreased effectively; and the quality and yield of CBN can he improved.

在超硬材料合成中，尤其是立方氮化硼合成中，能有效降低锤耗，同时可提高立方氮化硼的合成品质及产量；超硬材料表面镀钛及钛合金后，能实现镀层和结合剂的冶金结合，工具寿命提高30%以上；钛对许多氧化物质和还原物质具有极好的耐腐蚀性，适用于人造金刚石的批量电解提纯工序。

The study of plating process showed the influences of bath components, such as complexing agent and reducing agent, and operation conditions, such as pH value and temperature, on deposition rate.

对镁合金化学镀镍工艺的研究表明，镀液组成如配体浓度、还原剂浓度和操作条件如pH值、温度等影响镀液的沉积速度。

Fresh Alocrom 1200 coatings may be removed without seriously etching the aluminium by immersing in 50% nitric acid or in the Deoxidiser bath.

刚做的ALCOCROM 1200镀层可以浸没在50%的硝酸里或者脱氧剂Deoxidiser浴缸里去除镀层，而不会明显地腐蚀铝材。

Surface Treatment and Finishing Technology, Raw materials and Equipment: Cleaning, Lapping, Deburring, Polishing and Burnishing, Sand blasting, Shot blasting, Ball blast, Conversion coatings, Electroplating, Thermal spray, Anti-Rust, Anti-Corrosion, Brush-plating, Vapor deposition, Hot dipping, Surface strengthening, Surface modification, Pre-treatment, Electrophoretic coatings, Anode oxidation, Plastic plating, Vacuum plating, Special coating, Depainting and Degreasing equipmentand Raw materials.

产品表面处理和精饰技术、原材料和设备：清洗、研磨、去毛刺、磨光和抛光、喷砂、喷丸、抛丸、转化膜、电镀、热喷涂、防锈、防腐蚀、刷镀、气象沉积、热浸镀、表面强化、表面改性、预处理、电泳涂装、阳极氧化、塑胶电镀、真空电镀、特种涂层、脱漆脱脂设备和原材料

Through test,adopt zinc vapour pressure to evaporate and refine the hot -dip galvanizing dregs to prepare the zinc powders directly was certificated;confirmed the evaporation-condensation method depurated hot-dip galvanizing dregs and used it to prepare zinc powders was feasible

通过试验验证了采用锌蒸气压蒸发提纯热浸镀锌渣冷凝后可以直接形成金属锌粉，说明热浸镀锌渣制备金属锌粉的工艺理论是可行的

The structure formed is FeNi〓and γ after diffusion. Owing to diffusion, the Ni distribution across the layer is gradient after heat-treatment at 600℃ for 1h.

扩散后形成了FeNi〓相以及γ相，镀层经600℃×1h的热处理后，由于扩散的影响，在镀层内部Ni含量呈现梯度分布。

Company production line Bridge Department main products are: trough, tray-style, the cascade-style, modular and large span steel combustion system tray and organic, inorganic fire series of bridge; surface is divided into treatment: galvanized, spray, passivated, hot dip zinc, zinc and nickel.

公司生产的汇线桥架主要产品有：槽式、托盘式、梯级式、组合式及大跨距钢制桥架和有机燃、无机防火系列桥架；表面处理分为：镀锌、喷塑、钝化、热浸锌、镀锌镍等。

The split between the two groups can hardly be papered over.

这两个团体间的分歧难以掩饰。

This approach not only encourages a greater number of responses, but minimizes the likelihood of stale groupthink.

这种做法不仅鼓励了更多的反应，而且减少跟风的可能性。