Zinc metallurgy is developing rapidly in china and has been the biggest county with zinc metallurgy production. Now the pyrometallurgy in zinc metallurgy techniques was being washed out because of more power consumption and serious pollution. Zinc hydrometallurgy is get zinc from zinc ore concentrate, which contains roasting-leaching-purify-electrolytic deposit in sequence.

我国锌冶金发展迅速，已经发展成为全球最大的锌生产国，但现有的锌冶金生产工艺中火法冶金存在能耗大，污染严重，逐渐被淘汰，而湿法炼锌是将锌精矿经焙烧-浸出-净化-电积获得金属锌。

Therefore, we carried out the theoretical and experimental study on reducing sphalerite of hi...

因此我们开展了真空下还原剂直接还原高铁闪锌矿工艺的热力学分析和实验研究，该方法实现了高铁闪锌矿的直接熔炼处理，具有能单独处理铁闪锌矿、流程短、无污染、金属回收率高、综合利用好等优点，且针对我国丰富的难处理锌资源一高铁闪锌矿，转变铁闪锌矿资源优势为经济优势，应用前景广阔。

The circinal cavities were found in calcium alginate beads and the cylinder holes were observed in zinc alginate beads from the SEM,which indicated that the volume of fraction of zinc alginate polymer was relatively bigger and the zinc alginate polymer chain was more rigid than that of calcium alginate .

凝胶的SEM照片可见，海藻酸钙的冷冻干燥颗粒内为较大的圆孔，海藻酸锌凝胶内为较小的长孔，表明海藻酸锌高分子链在凝胶颗粒中的体积分率相对较大同时刚性较强；卵清蛋白从海藻酸凝胶颗粒中释放的试验结果表明，由于上述海藻酸锌凝胶的特性，导致海藻酸锌对卵清蛋白扩散阻滞作用相对较强；根据试验数据计算得卵清蛋白在海藻酸钙、海藻酸锌凝胶颗粒中的扩散系数分别为1.19×10-7、0.07×10-7cm2/s，利用阻滞模型计算得海藻酸锌高分子链在凝胶颗粒中体积分率约为海藻酸钙高分子链在凝胶颗粒中体积分率的1.7倍。

When the concentration of zinc nitrite is lower than 0.1 M,(002) is the prior face for zinc oxide. As the concentration raise, the other kinds of crystal face would appear. Among those data,(002) grows the best when the concentration of zinc nitrite is 0.06 M. We add lactic acid and citric acid respectively; there is an carboxyl group on the lactic acid and three carboxyl groups on the citric acid. The monodentate of lactic acid helps the growth of zinc oxide, compared to the tridentate of citric acid which can only produce zinc oxide film under very low concentration, but the growth of (002) face is not that stable as adding the lactic acid and zinc will electrodeposit to substrate.

实验中，当硝酸锌浓度低於0.1 M 时，氧化锌以(002)面为优选位相，当浓度提高，其他晶面将会出现，当硝酸锌为0.06 M，(002)晶面成长最佳，分别加入乳酸和柠檬酸，乳酸结构上有一羧基团而柠檬酸有三个羧基团，单芽基的乳酸有助於氧化锌成长，对照於三芽基的柠檬酸，则必须在极低的浓度下才能制备氧化锌薄膜，但(002)面成长却没有添加乳酸来的稳定而金属锌也会电沉积到基板上。

According to the property of mud of gas of plum steel blast furnace, undertook to its zincic experiment studies receiving iron to fall, no matter use magnetic separation,the result makes clear or classification the law all can reclaim from which content of major iron ore and purify is major zinc, stock of will tall zinc, low zinc undertakes effective depart, iron concentrate yield and grade all achieve 52% above, iron metal reclaims rate 70%, take off zinc to lead 50% above.

梗概： 介绍了梅钢高炉瓦斯泥的性质、试验情况及结果，国内外处理使用含锌高炉瓦斯泥的方法。根据梅钢高炉瓦斯泥的性质，对其进行了收铁降锌的试验探究，结果表明无论用磁选还是分级法均能从中回收大部分铁矿物并去除大部分锌，将高锌、低锌物料进行有效分离，铁精矿产率和品位均达到52%以上，铁金属回收率70%，脱锌率50%以上。

Adopting cathode protection of the zinc materials as an effective protection method, which already applied more and more in many field. For example, Hot-dip galvanisation, galvanization, electric arc spray zinc 、sherardizing, etc. But that method are with lots of shortcomings. For example, hard to apply

采用锌材料阴极防护的方式，作为一种有效的钢铁防护手段，已经得到越来越多的应用，诸如热浸镀锌、电镀锌、电弧喷锌、热喷锌等工艺手段，但鉴于这些工艺存在施工难度大、环境污染重、能耗高、锌层受损难修复等弊端，使得发展受限。

A thermodynamics and dynamics study is made about the mechanism of Zinc powder displace Cobalt during purifing Zinc Sulphate solution.

对硫酸锌溶液净化过程中锌粉置换钴的机理进行了热力学和动力学研究，通过不同粒度的锌粉、自产锌粉和合金锌粉的对比试验，结果表明：使用Pb-Sb-Zn合金锌粉有利于降低净化过程的锌粉消耗，现已应用于生产实践，降低了生产成本。

The impedance spectra are analyzed using an equivalent circuit containing two Nerstain diffusion terms. The simulated data are also discussed. Those additives can decrease the charge-transfer resistance and oxygen diffusion resistance.As to button zinc-air battery, we improve its zinc anode structure through granulation process.

扣式电池主要对锌阳极的结构进行了改善，采用将锌粉造粒的工艺，对不同种类锌粉放电测试，结果表明这种锌粉的结构对锌粉的利用率的提高有着积极的贡献，锌粉利用率最高可达90％。

The company's operating range: 1, barrel plating white zinc, color zinc, blue zinc, black zinc, yellow zinc,üzinc, nickel-plated roller, Qing-hong Gu, roll on behalf of chromium, etc.; 2, linked to light-plated nickel, bright chrome, sand nickel, pearl nickel, pearl envelope, Tsing ancient, red ancient, imitation gold, K gold, alluvial gold sweep, pearl silver, etc.; 3, plastic (ABS, PC, PC + ABS, PE, etc.), resin plating; 4, aluminum alloy oxidation, coloring; 5, printed circuit board plating, electronic plating (tin, tin aluminum, gold, etc.); 6, plating for customers to develop new varieties; 7, metal, injection molding.

荣丰公司的经营范围：1、滚镀白锌、彩锌、蓝锌、黑锌、黄锌、军绿锌、滚镀镍、青红古、滚代铬等；2、挂镀光镍、光亮铬、沙镍、珍珠镍、珍珠络、青古、红古、仿金、K金、扫沙金、珍珠银等；3、塑胶（ABS、PC、PC+ABS、PE等）、树脂电镀；4、铝合金氧化、着色；5、印制电路板电镀、电子电镀；6、为客户开发新电镀品种；7、五金、注塑加工。

A method for the analysis of zinc oxide phase content in sulfide ore was studied. On the basis of the characteristics of each phase component, the sulfide ore sample was leached twice with NaOH and acetic acid-ascorbic acid, respectively, so that the oxide mineral and zinc oxide were dissolved completely. The leaching rate of zinc oxide phase was up to 98 Vo. Moreover, the dissolution of zinc sulfide phase was effectively inhibited, solving the problems of selective leaching and determination for zinc oxide.

研究了硫化矿中氧化锌相含量的分析方法，根据硫化矿中各物相组分特点，提出了用氢氧化钠溶液和乙酸－抗坏血酸溶液二次浸取硫化矿，使锌氧化矿、氧化锌充分溶解，氧化锌相的浸取率达到98%以上，同时有效地抑制了硫化锌相的溶解，较好地解决了氧化锌相选择溶解测定的问题。

This one mode pays close attention to network credence foundation of the businessman very much.

这一模式非常关注商人的网络信用基础。

Cell morphology of bacterial ghost of Pasteurella multocida was observed by scanning electron microscopy and inactivation ratio was estimated by CFU analysi.

扫描电镜观察多杀性巴氏杆菌细菌幽灵和菌落形成单位评价遗传灭活率。