The composites were tested by X-Ray Diffraction, Scanning Electron Microscopy, Thermal Expansion Coefficient and flexural strength. In these ways, the synthesization of leucite crystal and the preparation of Zro2-KAlSi2O6 Ceramic powder are systemically investigated.

本研究以钾长石、纳米氧化锆和碳酸钾为原料，采用固相反应合成氧化锆-白榴石基烤瓷粉，借助XRD、SEM、TEC和弯曲强度等分析测试方法，对白榴石晶体的合成及氧化锆-白榴石基烤瓷粉的制备进行了较为系统的研究。

The better condition synthesizing the assorted minerals of zirconolite and sphene doping neodymium is holding 30 min at 1230℃, and the better formula is nCa(subscript 1-x/2-y/4 Zr(subscript 1-y/4);Al(subscript x/2) Ti(subscript 2-x/2O7): nCa(subscript 1-x NdAl Ti(subscript 1-x)SiO5[4/(4-y)]:1. Nd(superscript 3+) can enter crystal lattices of ite and sphene. Sphene can immobilize Zr(subscript 4+), Al(subscript 3+) and Nd(subscript 3+); Zr(subscript 4+) and Nd(subscript 3+) replace Ca(subscript 2+), and Al(subscript 3+) replaces Ti(subscript 4+). Zirconolite can immobilize Al(subscript 3+) and Nd(subscript 3+) Nd(subscript 3+) replaces Ca(subscript 2+) and Zr(subscript 4+), and Al(subscript 3+) and replaces Ti(subscript 4+).

研究表明：钙钛锆石和榍石组合矿物固化体较佳的合成条件是在1230℃条件下保温30min，较佳配方的摩尔比为nCa(下标 1-x/2-y/4 Nd(下标 x+y/2)Zr(下标 1-y/4)Al(下标 x/2)Ti(下标 2-x/2) O7：nCa(下标 1-x Nd Ti(下标 1-x)-SiO5=[4/(4-y)]：1；Nd(上标 3+)能够进入钙钛锆石和榍石晶格，榍石能够固溶Zr(上标 4+)、Al(上标 3+)、Nd(上标 3+)，Zr(上标 4+)和Nd(上标 3+)取代Ca(上标 2+)位，Al(上标 3+)占据Ti(上标 4+)位，钙钛锆石能够固溶Al(上标 3+)、Nd(上标 3+)，Nd(上标 3+)进入Ca(上标 2+)位和Zr(上标 3+)位，Al(上标 3+)占据Ti(上标 4+)位。

Main specifications of the zirconium oxide ceramic casing, zirconia ceramic casing is optical fiber communications link with the core components, its products of high accuracy (1 micron), the stability of zirconia finished the demanding, complex processing technology.

主营各种规格的氧化锆陶瓷套管，氧化锆陶瓷套管是光纤通信的连接器的核心部件，其产品精度高（1微米），氧化锆成品稳定性要求严格，加工工艺复杂。

CL imaging has identified two types of zircon that are metamorphically new growth and recrystallized detrital grains, respectively.

中文摘要：大别-苏鲁造山带大理岩中榴辉岩包体的锆石有两种类型，为变质增生锆石和变质重结晶的残留碎屑锆石。

CL imaging has identified two types of zircon that are metamorphically new growth and recrystallized detrital grains, respectively.

文章摘要：大别-苏鲁造山带大理岩中榴辉岩包体的锆石有两种类型，为变质增生锆石和变质重结晶的残留碎屑锆石。

The results show that, by the way of optimizing preparation condition, the spherical zirconia powders with suitable particle size distribution are prepared using chemical precipitation method. Using heterogeneous chemical precipitation coating technique, the sph, erical nickel coated zirconia powders are prepared and the heterogeneous nucleation can be done on the surface of spherical zirconia powders. The thickness of coated layer, homogeneous degree and crack of surface can be controlled by the way of controlling powder concentration, adding rate of reactants feeding and adding surface active agent.

研究表明，采用化学沉淀法，通过优化制备工艺条件，可以制备粒径分布较均匀的球形氧化锆粉体；利用非均相化学沉淀包裹技术制备的金属镍包裹氧化锆微球粉体，球形氧化锆颗粒表面作为异相成核的场所，通过控制颗粒浓度、加料速度以及添加表面活性剂等工艺条件，可以调控包裹层厚度、表面均匀度以及表面裂纹等。

There are two kind of zicons in amphibolite from the Haiyangsuo area,eastern Shandong Province:(1)Xenocrysts,they give 207Pb/208Pb age of 2149Ma,which suggests an early proterozoic basement in this area;(2)Magmatic euhedral zircons,they give an upper intercept age of 1784±11Ma and lower intercept age of 448±13Ma.

中文摘要：胶东海阳所胶南群斜长角闪岩中的锆石有2类：（1）捕掳晶锆石，它给出2149Ma 的207Pb/206Pb 年龄，证明该区存在有早元古基底；（2）岩浆结晶锆石，它的不一致线上下交点年龄分别为1784±11Ma和448±13Ma。

The feldspars of topaz-lepidolite granite in Yashan late stage are P-rich albite and Kfeldspar, and the phosphorus goes into feldspar structure in the form of PAlSi〓 substitution. The phosphorus contents of feldspars vary according to their crystal habitus. In general, the feldspars of later generation have the higher average phosphorus content than that of earlier generation, and the albite contains higher phosphorus than the K-feldspar in the same generation. The zircon is highly rich in Hf, U, P and Al. The phosphorus enters the zircon structure mainly by the form of〓P〓〓Si〓, Al〓P〓Si〓 or P〓Al〓Si〓, Zr〓 substitution. The P-rich zircon is the production of the highly evolved magma, and it might be one of the important characteristic minerals of the high-P subtype granite. The manganocolumbite, manganotantalite, wodginite and titanowodginite are the main niobium and tantalum minerals.

雅山晚阶段黄玉锂云母花岗岩的长石矿物是富磷长石，磷以PAlSi〓替换方式进入长石结构中，并且在长石中的分布很不均一，一般是晚结晶的长石比早结晶的长石的磷含量高，同期结晶的钠长石比钾长石的磷含量高；锆石矿物为高度富铪、铀、磷和铝的锆石，磷主要以(Y， HREE， Fe)〓P〓〓〓Si〓〓、Al〓P〓Si〓〓、P〓Al〓Si〓〓Zr〓〓等替换方式进入锆石晶格中，富磷锆石是岩浆高度演化的结果，是高磷花岗岩的特征矿物之一；雅山含有丰富的磷锂铝石，是高磷花岗岩的主要磷酸盐矿物；铌—钽矿物主要有铌锰矿—钽锰矿、锡锰钽矿—钛锰钽矿、细晶石等。

Currently, the main opacifier is zircon. Zircon crystals which formed in vitrified tiles have different refractive with glass caused light scattering, it makes vitrified tiles whiteness.

目前，玻化砖中乳浊剂主要采用的是锆英石，其增白机理是在玻化砖中形成硅酸锆晶体，利用硅酸锆晶体与玻璃相之间的折射率差使可见光发生散射，从而产生增白效果。

Zirconia/graphite compound mold core was prepared by the coating, in which the silicon sol was used as binder and zirconia was used as refractory materials. The application feasibility of metal particles as a coolant in the solidification process was studied, and the application of metal particles as subsidiary coolant in the liquid metal cooling of directional solidification were analyzed and studied in this investigation. The conclusions can be drawn as follows: 1 The zireonia/graphite compound cores fabricated by brushing coating which was prepared by making silicon sol agglutinated zirconia as a refractory material were casteded at 800℃and 1000℃respectively, and the results show that the strength of the mold core is strong enough to meet the requirement of practical casting.

本文研究了以硅溶胶为粘结剂，氧化锆为耐火材料来制备氧化锆／石墨复合型芯的制备工艺；并分析了金属颗粒作为冷却剂在金属凝固过程中应用的可行性、金属颗粒的冷却能力以及金属颗粒作为辅助冷却剂在定向凝固的液态金属冷却法中的应用，得出以下结论：(1)以硅溶胶为粘结剂，氧化锆为耐火材料来配制涂料，采用刷涂石墨型芯的方法来制备的氧化锆／石墨复合型芯经800℃和1000℃实际浇铸实验，结果证明型芯的强度足够满足实际浇铸要求。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。