铬鞣的

With only 2% chromium powder, the nano-composite tanning agent can thicken the leather by 124.5%, the shrinkage temperature reaches to 95 DEG C.; compared with a chrome tanned leather, a leather tanned by the nano-composite tanning agent has a tensile strength, peeling strength and elongation at break improved by 51.8%, 8.2% and 13.3% respectively, has no obvious stratification or sedimentation during over 12 months of storage period.

所述复合鞣剂只需配入2％的铬粉，就可使皮革增厚高达124.5％，收缩温度达到95℃以上；其鞣革相较于铬鞣革，革的抗张、撕裂强度分别提高了51.8％和8.2％，断裂伸长率也提高了13.3％，存放期12个月以上无明显分层和沉淀。

Among all tanning agents, chrome tanning agent is the best one which has good performance that the others can not compete to it. hi a long time in the future, chrome tannage is still the most important tanning method.

在各种鞣剂中，鞣制效果最好的当属铬鞣剂，它有着其它鞣剂无法比拟的优越性能，在相当长的一段时间内，铬鞣法仍然是最主要的鞣制方法。

Among all tanning agents, chrome tanning agentis the best one which has good performance that the others can not compete to it. In along time in the future, chrcme tannage is still the most important tanning method.

在各种鞣剂中，鞣制效果最好的当属铬鞣剂，它有着其它鞣剂无法比拟的优越性能，在相当长的一段时间内，铬鞣法仍然是最主要的鞣制方法。

Collagen has been treated with DHTPA and then tanned with chromium complexes,and the effect of DHTPA on chrome tanning properties has been investigated by determining the chrome absorptivity and fixation as well as the physical properties of the crust.

用DHTPA对胶原改性后进行铬鞣，通过铬的吸收率、铬的固定率、坯革物理机械性能等指标的测定，研究了DHTPA对胶原铬鞣性能的影响。

It included enzyme unhairing,sodium hydroxide based fibre opening and pickle and basification-free chrome tanning process.

介绍了一种三步铬鞣山羊面革的加工方法，即：酶脱毛，NaOH打开皮纤维和无浸酸、无提碱铬鞣。

Hi a long time in the future, chrome tannage is still the most important tanning method.

在各种鞣剂中，鞣制效果最好的当属铬鞣剂，它有着其它鞣剂无法比拟的优越性能，在相当长的一段时间内，铬鞣法仍然是最主要的鞣制方法。

To solve this problem,one of the routes with good potential for success is to treat collagen with special modifier to implement high exhaustion chrome tannage by simply providing additional cross-linking sites or binding sites for chromium.

解决这一问题的一条有效途径就是在铬鞣前采用改性剂对胶原进行改性，通过给胶原分子上引入附加交联点和结合点以实现高吸收铬鞣。

The results of research on the factors affecting titanium tannage show that high concentration NaCl medium has larger negative effect on titanium tannage. When the NaCl concentration exceeds 5%, the titanium tanning action is reduced rapiddly. Traditional NaCl pickling is unsuitable for titanium tannage, tanning in water medium directly, the best tanning effect can be obtained, so titanium tanning can not only eliminate chrome pollution, but also diminish salt pollution. The optimum tanning conditions for HPZ-Ti tan liquor are pH3. 5, TiO〓 offer of 7. 5%(based on the weight of 65% moisture pelt), the best Bascity of tan liquor is between 30% and 50%.

以HPZ—Ti鞣液为基础，研究了不同鞣制介质，鞣制pH值，鞣剂用量和浓度，鞣液的碱度，不同提碱剂，不同的预处理和后处理等因素对钛鞣的影响，结果表明：高浓度的NaCl溶液介质对钛鞣有很大的负面作用，当介质NaCl浓度超过5%，革内钛的结合量和革的Ts明显降低，传统的高浓度NaCl浸酸工艺不适合于钛鞣，在水介质中直接鞣制效果最好，所以钛鞣不仅消除了铬污染而且大大降低了盐的污染。

Through the comparison, the method of directive recycling use of the used chrome liquor is more suitable than the one of chrome recovery from the used chrome liquor for tannery.

对目前国内外铬鞣废液的回收利用研究及方法进行了综述与比较，铬鞣废液的直接循环使用较回收铬的方法更易在制革厂实

Through orthogonal test, chrome-free tanning technology of goatskin shoe upper leather with chrome-free tanning agents such as modified glutaraldehyde,modified vegetable tannin and syntans was studied.

采用改性戊二醛、改性栲胶、合成鞣剂等无铬鞣剂，通过正交试验，优化出了多种鞣剂结合鞣制山羊鞋面革的无铬鞣制工艺。