Such specimens could not be remedied by the usual quench andtemper treatment, and re-solution treatment at high temperatures (980-1050℃)followed by rapid cooling to room temperature was necessary to modify the sizeand distribution of the boron-containing phase, with the consequence of improvingproperties and eliminating the shell-shaped fracture.

对于出现&壳层状硼脆断口&的50B钢，正常的调质处理不能恢复其性能。但在980—1050℃重新固溶处理并以较快速率冷却到室温则可以改变硼相的析出形态，并改变相应的断口形态，相应地性能也恢复或有所提高。

This paper introduced X70 and X80 HRC with heavy thickness which were designed by low carbon, high niobium acicular ferrite microstructure , and developed on medium thickness slab continuous casting production line in Ansteel.

介绍了鞍钢股份有限公司采用低碳高铌针状铁素体组织设计、在中等厚度连铸坯连铸连轧生产线上研制开发特厚规格X70和X80级管线钢热轧卷板的情况。

Moreover, the electromagnetic flux density and meniscus height increase in the form of chequerboard with increasing of slit number. The numerical results can exactly illuminate some experimental phenomena, and enrich the theoretical foundation of soft-contact continuous casting technology. In practice, a softcontact mold with slit number of 16 or 24 is recommended, the suggested frequency is around 20kHz, and the slit width is about 1mm.

结果表明：钢液对结晶器内的电磁场分布有很大影响；发现了磁感应强度和弯月面高度随电源频率增加而增大的频率范围、磁感应强度和弯月面高度随切缝数目增加呈&锯齿状&增大的规律；研究结果合理地解释了一些实验现象，完善了软接触结晶器电磁连铸技术的理论基础；建议在实际应用中采用分瓣数为16或24分瓣数的结晶器，电源频率应控制在20kHz左右，切缝宽度应控制在1mm左右。

The results showed that the micro-character of the transverse cracks embedded in the S355 steel plate was severe band structure.

研究发现钢中存在严重的带状组织，裂纹附近有密集的点状内氧化，还有大量的包状晶网络。

The concept of equivalent rotationally rigidity is offered and the formula of rotationally rigidity is obtained.

主要做了如下几个方面的工作：对伸臂位于顶部的单层框架—筒体模型进行分析，提出了等效转动约束的概念和转动约束刚度的表达式。

Male cats normally do not need aftercare with the exception of the night after the anesthetic.

男猫通常不需要善后除了晚上的麻醉。