First of all, this study will be multi-walled carbon nanotubes by chemical oxidation process purified so it can be modified to deal with than the purification of purity before the modified 5 wt%, more than 1.89 times the surface area to increase the surface potential decrease of about 10 ~ 20 mV and the surface functional base (-COOH and-OH) to increase 1.45 times, and then the control technology of electroless preparation parameters include: analysis of plating time, plating analysis of temperature, metal ions in solution than the (Fe2+/ Ni2+), bath pH and the added value of dispersion Agent and other research towards Fe-Ni particles to increase the iron content and Fe-Ni particles spread in the MWCNT upper fixed targets,the results found that when the parameters for the preparation of 50 ℃, pH10, do not add dispersant, metal ions than the solution (Fe2 +/ Ni2 +) 7, the highest iron content can be Fe = 40.55 at%(flat iron content 111.17 mg / g) of nanocomposites Fe-Ni/CNT, then for a series of the nature of its analysis, the final evaluation Fe-Ni/CNT nanocomposites were processed on the effectiveness of the application of mixed pollutants, the results showed that in 120 minutes at the same time when Adsorption of heavy metal ions lead nitrate 10 ppm, selenium heavy metal ion degradation of 1 ppm and orange azo dye AO7 50 ppm standard of effluents, and after a total Fe-Ni nano-particles to SEM / EDS analysis of more than 50% still remaining.

本研究首先将多壁奈米碳管以化学氧化法做纯化改质处理能使其纯度较纯化改质前提高5 wt％、比表面积提高1.89倍、表面电位下降约10~20 mV以及表面官能基提高1.45倍，再控制无电镀技术之制备参数包括：析镀时间、析镀温度，镀液中金属离子比(Fe2+/Ni2+)、镀液pH值及是否添加分散剂等，研究朝提高Fe-Ni粒子的含铁量与Fe-Ni粒子散布固定在MWCNT上等目标进行，研究结果发现当制备参数为50 ℃、pH10、不添加分散剂、镀液金属离子比(Fe2+/Ni2+)7时，可得到最高铁含量Fe = 40.55 at％(单位铁含量111.17 mg/g)之奈米复合材料Fe-Ni/CNT，接著对其作一系列性质分析，最后评估奈米复合材料Fe-Ni/CNT对共处理混合污染物之应用效益，结果显示其在120分钟时能够同时吸附重金属硝酸铅离子10 ppm、重金属硒酸根离子1 ppm及降解偶氮橘色染料AO7 50 ppm达放流水标准，且共处理后奈米Fe-Ni粒子以SEM/EDS分析仍剩余50 %以上。

Concentration of silver behenate solution affects the morphology and packing density of silver. The thin silver film of spherical silver particles, with an average diameter of 160 nm has been fabricated by a millimolar solution of silver behenate. The thick silver film is consisting of the regular silver particles with triangular or truncated triangular shape, which is formed at high concentration.

山嵛酸银分散液的浓度影响银薄膜中银粒子的堆积密度和形态，在很低浓度下可以得到银粒子均匀分散的金属银薄膜，球形银粒子平均粒径为160nm；而高浓度的山嵛酸银分散液得到较厚的金属银薄膜，薄膜中含有规则的三角形和截三角形银颗粒。

It may imply that there are close relation between the enhancement of electric field in nearby particles and dipolar interaction.

基底上正电荷所诱导的金属纳米粒子的偶极的形成减弱了从金属纳米粒子到PATP分子的电荷转移，碘离子的共吸附使得金属纳米粒子表面的电荷重新分布。

The metallic nanoparticle-semiconductor composite thin films are considered as the only photoemissive material that can be used to detect the ultrashort laser pulses.

金属纳米粒子／半导体介质复合薄膜在近红外-可见-近紫外波段的选择性光吸收主要由金属纳米粒子体内导带电子的表面等离子激元共振吸收引起。

The invention discloses anti-collision elastic material, which mainly consists of epoxy resin, polybasic amine curing agent, metal powder and slate powder enhanced particle, and the weight proportion of each component is as follows: epoxy resin of 25 to 30 parts, polybasic amine curing agent of 10 to 16 parts, metal powder of 42 to 45 parts and slate powder enhanced particle of 54 to 58 parts.

本发明公开了一种防撞击的弹性材料，其主要成分有环氧树脂和多元胺类固化剂，以及金属粉和石粉增强粒子，各组分的重量配比是：环氧树脂25～30，多胺类固化剂10～16，金属粉42～45，石粉增强粒子54～58。

In this paper, several coloring pigments were synthesized and the sheet metal powders were coated by these pigments with the technology of super powder preparing and particle compositing. The coated composite particles were prepared by these, and the metallic luster of the metal powders were defiladed. The mechanism and the processing conditions of composite particles were researched.

本论文以超细粉体制备及粒子复合技术为基础，在金属粉表面包覆一层红外透明性较好的着色颜料，遮盖金属粉的金属光泽，制备出包覆式复合粒子，对复合粒子的制备的机理及工艺条件进行了研究。

Two new methods about preparation of nano-inorganic coated polymer microsphere have been found. The research mainly focused on controlled precipitation of inorganic precurdors onto the polymer microspheres, technique of preparation and size distribution of transition metal oxides and sulfides emulsion particles, nano-paticles''surface modification and the HLB values adjustment, emulsification of oil-soluble monomer in inorganic colloid and emulsion stability, emulsion polymerization that inorganic particles act as medi-phase, the preparation of inorganic nano-particle/polymer hybrid microspheres, preparation of hybrid materials in inverse emulsion, inverse emulsion polymerization of acrylamide and its phase behavior. Inorganic nano-particles we studied concerning TiO2、SiO2、Fe3O4、ZnO、ZnS、Ag and black carbon. Also we studied the morphology and capability of the hybrid materials.

主要内容有：无机物在高分子乳胶模板体系的界面定位沉积研究；过渡金属氧化物、硫化物纳米胶体粒子的制备工艺与胶粒尺寸分布研究；纳米粒子的表面修饰及其亲水亲油平衡值的调制；油溶性单体在无机胶体中的乳化行为与乳液稳定性研究；以无机纳米粒子做中介相的乳液聚合与无机纳米粒子/高分子复合微球制备研究；反相体系中杂化材料的制备；丙烯酰胺水溶液反相乳液聚合、相行为与稳定性；丙烯酰胺反相体系中无机粒子的制备研究；涉及到TiO2、SiO2、Fe3O4、ZnO、ZnS、Ag、碳黑等纳米无机物，系统考察了相关材料的形态与性能，为其应用开发奠定了基础。

The strip is made of plastic coated with metallic particles magnetized to form a pattern that stores the card's numerical data.

磁条是塑料制成，外加一层磁化的金属粒子，排列组合后用来存储卡上的数字信息。

The strip is made of plastic coated with metallic particles magnetized to form a pattern that stores the card's numerical data.

磁条是塑料制成，外加一层磁化的金属粒子，排列组合后来储存卡上的数字信息。

The absorption bandedge redshifts were discussed in terms of Rayleigh scattering. The intensity decrease was caused by nonradiation energy transfer and transform between Co nanopticles and AAO template or metal nanoparticles absorb photon.

分析认为，光吸收带边红移主要是Co纳米粒子瑞利散射引起的消光现象；强度的减弱是由于沉积在AAO模板中的Co纳米粒子和模板之间发生了非辐射能量的传递和转换，或金属纳米粒子对光子具有吸收和传导作用所致。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。