The in-plane equivalent elastic modulus and tensile strength of stitched composite laminates are studied, and its found that the in-plane equivalent elastic modulus decreases with the increase of stitch density, stitch thread diameter, maximal misalignment angle and the distortion width, and the range is about 5%. The tensile strength of stitched composite laminate increases with the increase of stitch step and decreases with the stitch space.

研究结果表明：随着缝纫密度、缝纫线直径、最大纤维偏转角和缝纫变形区宽度的增加，缝纫复合材料层合板面内等效模量逐渐降低，最大降幅一般在5%左右；缝纫复合材料层合板的拉伸强度随缝纫针距的增加而增大，随缝纫行距的增加而降低，因此缝纫密度对拉伸强度的影响程度要看具体的缝纫针距和行距。

The results showed that the linear expansivity and apparent porosity of the samples increased with increasing the percentage of matrix materials and aggregate size.

结果表明，随着基质料含量的增加和骨料粒度的增大，试样的线变化率和显气孔率逐渐增大；随着成型压力的增加，试样的显气孔率明显减小，线变化率增加。

Having investigated composites of EP coating ultramicro iron using ATPU as surface agent, results showed that with increasing amount of ATPU, density , complex permittivity and complex permeability of composites decreased, and retentivity and coercivity increased.ε"μ"

用ATPU作表面活性剂制备核壳结构复合粒子时，随着复合时ATPU用量的增加，复合粒子的密度、复介电常数和复磁导率逐渐减小，剩磁与矫顽力逐渐增大。

The results show that nitrite-N in the soil profile decreases gradually with increase of soil layer depth.

结果表明，随土层增加，土壤剖面硝态氮逐渐下降；长期连作烤烟，0~100 cm土层硝态氮含量明显高于玉米，在烤烟生长过程中，随着气温的升高，土壤硝态氮含量明显增加。

At the edge of a gap the coverage and species of shrub were the greatest; as the distance getting farther from the center of a gap, the height, coverage and species of herbage decrease; with the litter of falling stem getting rot, the number of gap renovation increased.

灌木种数呈少－多－少的变化过程。在林隙边缘地带，灌木盖度最大、种类最多；从林隙中心到林内随着距离增加，草本高度、盖度、种数逐渐变小；随着林隙内枯倒木腐烂程度增加，林隙更新株数有增多趋势。

The climate change led to an increase in drought events, in particular in midsummer in 1990s. The frequency of the rainstorm process decreased from 1980s, and significantly in 1990. From early 1980s, the first frost date advanced, but the late frost date was slightly late by 1.3 days each 10 years. The active accumulated temperature of ≥10℃ steadily increased. The frostless season had gradually extended since 1970s.

进一步分析发现：气候变化导致盛夏农业干旱事件发生的频次增多，90年代几乎每年盛夏出现干旱事件；暴雨过程次数从80年代起逐渐减少，90年代减少明显；80年代初开始终霜冻日期提前，初霜冻日期推迟；70年代起无霜期逐渐延长；稳定≥10℃的活动积温随年代增加。

The mode of OH- band and the intensity decrease linearly with the increase of pressure, i.e., y=-0.3402 x+3617.8 and R2=0.9662, and the mode disappears at 18 GPa, which is assumed to be the maximum pressure for the dehydration of phengite at room temperature.

羟基3618cm^-1谱峰则随压力增加向低频方向移动，谱峰的降低与压力的增加呈明显的线性关系变化（y=-0.3402X＋3617.8，R^2=0.9662），并且强度随着压力的增加也在逐渐减弱，在压力达18GPa时开始消失，推测该压力可能为多硅白云母在常温下脱羟基的极限压力。

Upon the addition of CdS into the GeS2-Ga2S3 system, the number of the metal-metal bonds and edge-shared GaS4/2 tetrahedra decreases, resulting in the formation of corner-shared tetrahedra with non-bridging sulfurs.

随着CdS逐渐加入到GeS_2-Ga_2S_3玻璃中，金属-金属键和共边连接的GaS_(4／2)四面体逐渐减少，导致相应共角连接四面体和非桥硫的出现和增加。

This indicates the addition of ion monomer actually has no impact on the type of liquid crystal; however, to the same length of polymer chains, their liquid crystal properties gradually disappear as the increasing of addition of ion monomers, T and T of each liquid crystalline ionomers are increased with adding ionomers, but T is reduced.

对于同一链段长度的聚合物，当引入离子单体的含量增加时，液晶性逐渐消失；各液晶离聚物的介晶转变温度T和熔点T随着离子加入量的增加略有增加，但T降低。

Additionally, with the increasing of V/Ti atomic ratio, on one hand, morphology ofC particles transformed from irregular to spherical; on the other hand,C particles evidently minishing at first and then growth were observed.

随着V／Ti原子比的增加，硬质相颗粒的形态由不规则状逐渐趋于球状；硬质相颗粒的尺寸先随着V／Ti原子比的增加而减小，当V／Ti原子比大于0.2，随着V／Ti原子比的增加，硬质相颗粒尺寸增大。

This one mode pays close attention to network credence foundation of the businessman very much.

这一模式非常关注商人的网络信用基础。

Cell morphology of bacterial ghost of Pasteurella multocida was observed by scanning electron microscopy and inactivation ratio was estimated by CFU analysi.

扫描电镜观察多杀性巴氏杆菌细菌幽灵和菌落形成单位评价遗传灭活率。