The surface voltage of electret film have relationships with charging boltage, temperature, distances between electrodes and charging time,and will attenuate in index.

驻极体薄膜的表面电位与充电电压、温度、极间距离、充电时间有关，电晕充电法形成的薄膜驻极体的表面电位呈e指数衰减。

The result of tensile test indicated that the residual γ-butyrolactone content in casting PVF film was an important influencing factor on the succeeding uni/bi-axially orientation stretch of the

通过拉伸测试可知，流延薄膜中γ-丁内酯的剩余含量是影响薄膜能否进一步拉伸的关键因素。

It was revealed that the film was constituted mainly by Zr-C, C=C (s^2) and C-C(sp^3) bonds; structure of the films was crystalline ZrCN embedded in an amorphous carbon and carbonitride matrix. With increasing flow rate, film Zr content decreased, but C and N contents increased.

实验结果表明薄膜结构是由ZrCN晶粒镶嵌在无定形碳和碳氮化合物基体中；膜中的化合键主要以Zr-C，C=C(sp^2)和C-C(sp^3)形式存在；随着混合气体流量的增加，薄膜的锆原子分数减小，而N和C的原子分数逐渐增大。

Quite difference was observed by surface photovoltage spectrograph between the original and the cathodically polarized WO〓 thin films, which supported above result.

表面光电压谱表明极化处理后的WO〓薄膜与初始薄膜之间在表面态密度分布方面存在显著差别。

Based on the results of tungsten oxide films measured by slow positron beam, a new chromism was brought forward to interpret the tungsten oxide films' chromogenic performance successfully on the electronic structure view. Meanwhile, the surface's absorption effects were verified.

根据慢正电子束流在WO〓薄膜变色过程中测量结果，从电子结构角度提出了新的变色机理，成功的解释了不同结构WO〓薄膜变色性能的优劣，同时也证实了膜表面的吸附作用。

The dielectric properties of homogenous BSZT and compositionally graded BSZT thin films were characterized by measuring the dielectric constant and dielectric loss as a function of applied electric field, temperature and frequency.

结果表明，通过合理设计梯度薄膜的成分分布，不仅可以实现对薄膜介电常数的调控，使其保持较高的调谐率，还可获得良好的介电常数温度稳定性。

In this work, the homogenous Ba0.90Sr0.10ZrxTi1-xO3(x=0~0.40) and compositionally graded BSZT thin films was prepared by sol gel processing.

采用溶胶-凝胶法在Pt(111)/Ti/SiO2/Si衬底上制备了Ba0.90Sr0.10ZrxTi1-xO3(x=0~0.40)组分及其成分梯度薄膜，研究了各组分及梯度薄膜的相结构，显微结构以及在外加电场作用下的介电特性。

The stable transparent sol of SrAl 2O 4 was successfully prepared for the first time by using cheap inorganic materials as precursors. The uniform and crackless photoluminescent thin films and the needle like nano powders were synthesized at a rather low temperature in reduced atmosphere.

研究了溶胶-凝胶工艺制备SrAl2O4∶Eu2+， Dy3+高效长余辉发光薄膜及粉体的工艺条件，以无机盐为原料，成功制备了均一、稳定、透明的SrAl2O4溶胶，并在较低温度下制备了均匀、无裂纹的发光薄膜和颗粒均匀的针状纳米发光粉体。

The effect of annealing temperature and different substrates on film crystallographic quality and surface morphology was investigated.

对sol-gel法制备的PbTiO3薄膜采用不同晶化工艺进行晶化，研究了晶化温度和基片对薄膜晶化的影响。

Therefore, for easy moisture of filmogen dampproof, be sure to note before using nylon membrane and post-using shall promptly foil wrapped it.

因此，对于易吸湿的薄膜材料一定要注意防潮，尼龙薄膜在使用前和使用后应当及时用铝箔将其包裹好。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。