Experimentally, in order to increase the coercivity of the hybrid recording media for increasing the area density, the influences of the magnetron sputtering parameters on the magnetic properties of TbCo films have been investigated.

实验上，围绕着光磁混合记录介质需要具有高的矫顽力，以提高介质记录面密度的问题，采用控制变量法，研究了制膜工艺参数对TbCo薄膜矫顽力的影响，得到了TbCo薄膜获得高矫顽力的最佳制膜工艺条件。

The results demonstrated that the Ag-TiO2 film own the revertible ability between visible light and UV light.

由此可以证明TiO2-Ag薄膜可藉由可见光及紫外光的激发效能，让薄膜具有可逆性的能力。

According to thin film polarization effect and eigenmatrix,the Fresnel retarder s achromatic width is expanded by evaporating dielectric membrane in two total-reflection surfaces of the rhomb.

根据薄膜的偏振效应，从薄膜的特征矩阵出发，通过在菱体的两个全反射面蒸镀光学介质膜的方法拓宽了菲涅耳菱体型相位延迟的消色差宽度。

Conventional plastics packaging rotogravure business card printing and membership card production, plastic film is the ultimate business card printing and membership card making prints while the new decoration gravure business card printing and membership card production, plastic film is business card printing and membership card making ink patterns and in such manner through a variety of transfer, the ultimate business card printing and membership card making to flat or curved surfaces of objects.

传统的塑料包装凹版制卡和会员卡制作中，塑料薄膜是最终的制卡和会员卡制作承印品，而新兴的装饰凹版制卡和会员卡制作中，塑料薄膜是制卡和会员卡制作油墨图案的载体，通过各种转移的方式，最终制卡和会员卡制作到平面或曲面的物件上去。

The results indicate that the rutile begins to appear at 750 ℃ in the films prepared by the non-hydrolytic sol-gel.

结果表明：非水解溶胶-凝胶法制备的TiO2薄膜开始出现金红石相的温度为750℃，高于传统水解溶胶-凝胶法制备的薄膜。

TiN film is prepared by using multi-arc ion plating technique on the stainless steel substrate. The microhardness is measured by the Hv sclerometer.

采用电弧离子镀技术在不锈钢基片上沉积了TiN薄膜，利用显微硬度计测量了薄膜的表面硬度。

The frictional behavior of samples was determined before and after sputtering, cohesion strength of samples was checked by scratch test.

结果表明在工具钢表面溅射镀BN薄膜后摩擦因数明显降低，从原来的0.8下降到0.6，具有良好的减摩效果；BN薄膜和T10钢基材之间有一定的结合强度。

Scratch test revealed that the adhesion strength between the GLC film and UHMWPE substrate was as high as 90N. The volume wear rate of GLC coated UHMWPE was 1.6×10^(-17)m^3/, which is 19 times reduced.

结果表明：磁控溅射法制备的GLC薄膜与基体结合力大于90 N，且对表面粗糙度没有影响；表面镀覆GLC薄膜的体积磨损率为1.6×10^(-17)立方公尺/，是UHMWPE的1/19。

X-ray diffraction was used to analyze the crystal structure and the field-emission scanning electron microscopy inspected the surface and cross-sectional morphology. X-ray photoelectron spectroscopy is used to determine the film composition. The optical transmittance, electric resistance, Hall Effect, and Seebeck coefficient were measured. It was found in XRD patterns that all samples possess In2O3 structure.

在特性量测方面，分别以X光绕射分析其晶体结构，场发射扫瞄式电子显微镜分析其表面及断面型态，以X光电子能谱分析仪分析薄膜成份，并搭配光穿透率、电阻率、霍尔效应及Seebeck系数等特性分析，探讨经热处理之后薄膜的热电特性变化。

The composition of the SiGe thin films were controlled by changing the ratio of the area of silicon and germanium. By changing the parameters of substrate temperature and annealing temperature, we examined the microstructure, composition, crystallinity, electrical and thermoelectric properties by field emission scanning electron microscope, X-ray photoelectric spectroscopy, secondary ion mass spectrometer, X-ray diffraction, Hall effect and Seebeck coefficient measurement.

利用改变矽锗靶材面积比例进行薄膜成份的控制，并藉由改变基板温度以及退火温度之制程参数，利用场发射扫描式电子显微镜、化学分析电子能谱仪、二次离子质谱仪、X光绕射仪、霍尔效应量测仪以及自组装之热电量测系统作为分析仪器，分别量测薄膜表面形貌、横截面、成分、结晶性质、电性以及Seebeck系数等特性。

By the time of its fall, most of the prisoners were writers who had written against the corruptions of the government.

到它被攻陷的时候，里面多数的犯人是写了反对政府贪污文章的作家。

The most obvious variation to ovum morphological character was that the color was changed from light green to sepiaceous in embryonic development, and all the ovums were almost hatched after 96h.

在胚胎发育过程中卵的形态特征最明显的变化是颜色从淡绿到深褐色，卵在发育96h后卵基本全部孵化。