By means of electrochemical measurements,XRD and surface morphology analysis,the influence of saccharin brightener on electroless plating nickel coating was studied.

通过电化学和XRD以及表面形貌分析等方法，研究了光亮剂糖精对化学镀镍层耐腐蚀性能的影响及其机理，结果表明，糖精可以提高化学镀镍层在盐酸、硫酸、氯化钠中的耐蚀性能，但在氢氧化钠中耐腐蚀性能下降

In general, the corrosion rate for the alumina and chrome refractory in the iron phosphate melts was no higher than their corrosion rate in the DWPF melt now used at the Savannah River Site.

同时，氧化铝和氧化铬耐火材料在铁磷熔体中的腐蚀速度小于它们在硼硅酸盐熔体DWPF中的腐蚀速度。

In this paper the classification of corrosion factors and the selection of key parameters in corrosion modeling were studied.

研究了腐蚀因素的分类以及腐蚀模型中关键参数的选择等问题。

Put 2 of them on a unit that is being damaged more than 1 Corruptor can handle.

如果一个单位受到的伤害超过一个腐蚀者的能力那么放两个腐蚀者上去。

Put 2 of them on a unit that . being damaged more than 1 Corruptor can handle.

如果一个单位遭到的伤害超过一个腐蚀者的能力那么放两个腐蚀者上去。

Now that you know the basics of the Corruptor, I shall now talk about how you can make effective use the Corruptor and the Devourer Tank in combination with each other.

现在你知道了关于腐蚀者的基本知识，我应该告诉你如何有效的混合编组利用腐蚀者和毁灭者坦克。

The inner layer of the dual-layers steel crucible is corroded badly when involved in the process of the liquid Mg. This paper talks about the experiment of immersing to find a better material, comparing the property of 2Cr13 and Q235 in liquid Mg alloy.

针对复合钢板坩埚在镁合金生产过程中，内层被镁合金液腐蚀严重的现象，设计了浸泡试验，对2Cr13与Q235的耐镁合金液腐蚀性能进行了比较。

The electrolysis corrosion rates in the cryolite molten salt under different current densities were measured and the corrosion mechanism was preliminarily discussed.

用X射线衍射和扫描电子显微镜对材料的组成和微观结构进行了研究，测量了样品在冰晶石熔盐中不同电流密度下的电解腐蚀速率，并对其腐蚀机理作了初步探讨。

Proper etchants were chosen to etch different planes of KDP crystal.

利用化学腐蚀法对KDP晶体的不同晶面进行了腐蚀，得到了清晰的位错蚀坑。

The coating corrosion mechanism for the overall/partial fallen coatings of bottom plates is analyzed. It suggestes that the impressed current CP be used to protect the bottom plates,the dehydrator be reformed,and the corrosion inhibitor be added to the water.

分析了防腐层完全脱落区域钢板的腐蚀机理，及防腐层未完全脱落部分坑点的腐蚀机理，并在此基础上提出采用外加电流阴极保护法保护罐底板、改造油罐脱水设施结构、在存水中加注缓蚀剂等建议。

Shop assistant: Please check at the door.

店员：请您到门口柜台交费。

In the end, transportation of PAHs in the environmental matrix was preliminarily investigated and discussed according to PAHs data of soils and sediments from a certain region in Shanghai. The result indicated that there are two or more pathways on PAHs transportation in the environmental matrix.

最后，对上海特定地区内PAHs在环境介质中的迁移径途进行了分析讨论，结果表明上海市土壤和沉积物等环境介质中PAHs的迁移存在多种途径。