Potentiodynamic polarization and electrochemical impedance spectroscopy techniques were applied to investigate the corrosion behavior of LY12CZ in 3% NaCl aqueous solution. The effects of stress to anodic polarization behavior, free corrosion potential, breakdown potential, polarization resistance and double-layer capacitance of LY12CZ were summarized.

利用动电位极化和电化学阻抗谱技术对应力加载下的LY12CZ铝合金在3% NaCl水溶液中的腐蚀行为进行了研究，考察了应力作用对LY12CZ在3% NaCl水溶液中的阳极极化行为、自腐蚀电位和破裂电位以及极化电阻和双电层电容大小的影响。

By means of electrochemical measurements,XRD and surface morphology analysis,the influence of saccharin brightener on electroless plating nickel coating was studied.

通过电化学和XRD以及表面形貌分析等方法，研究了光亮剂糖精对化学镀镍层耐腐蚀性能的影响及其机理，结果表明，糖精可以提高化学镀镍层在盐酸、硫酸、氯化钠中的耐蚀性能，但在氢氧化钠中耐腐蚀性能下降

The microstructure of ZL102 alloy was observed after annealing at different temperature by metallography microscope. The rule of hardness changing along with annealing temperature was obtained, the corrosion resistance was compared by all soaks, the corrosion appearance was observed.

中文摘要：利用金相显微镜观察经不同温度退火处理的ZL102合金的显微组织，通过测量硬度得出其随退火温度的变化规律；并通过全浸腐蚀试验比较其耐腐蚀性，观察其在不同温度下的腐蚀形貌。

The extent of the decrease is influenced by the type of corrosion medium.

选用2种双相不锈钢在1200℃固溶后，760℃分别时效不同时间，研究其相结构、硬度与在几种典型腐蚀介质中的电化学腐蚀行为。

The results showed that there are higher grey ralational grade and canonical correlation coefficient between the grey distribution of metallic samples and uniform corrosion lost-weight, localized corrosion depth.

使用灰色关联及典型相关技术分析了试片扫描灰度值与实海平均腐蚀失重、局部腐蚀深度的关系。

The EIS only behaves capacitive reactance character.KI makes the corrosion process of carbon steel change from single active polarization to active polarization and concentration polarization.

单独的KI会影响A3钢在盐酸中的腐蚀控制特征，KI加入后，A3钢在盐酸中的腐蚀由单一的活化极化控制转变为活化极化和浓差极化混合控制。

The coating's protective efficiency and hydrophobicity were investigated by water absorption by capillarity and contact angle respectively.

使用毛细管吸收量评价防护涂料的保护程度，使用接触角评价防护涂料的疏水性，使用离子色谱测定石灰岩腐蚀层中形成的硫酸盐，根据硫酸盐的量决定石灰岩的腐蚀程度。

The prepared microemulsion diesel oil have favourable cold endurance which is better than 0(superscript #) diesel oil. It can be held for 205~424 days in ambient temperature. And the cautery is 1A which doesn't cauterize the diesel.

结果表明，制备出的柴油微乳液具有较低的运动粘度，比0柴油具有更优异的耐低温性能；室温稳定时间为205~424d；各样品的腐蚀度均为1A级，不会对内燃机造成腐蚀。

It is believed the corrosion processes of bronze could be divided into two stag es:at the first stage,cuprite,malachite and tenorite were formed;cassiterite ,cerussite and relic copper,lead and tin were formed in the second stage,which c an be found in the outer layer of bronze.

在上述模拟结果基础上，建立了青铜器腐蚀的化学作用过程，即青铜器的腐蚀大致可分为两个阶段：第一阶段生成黑铜矿和孔雀石，第二阶段生成白铅矿和锡石等矿物。

The relativity between image feature and pit distribution characteristic of corroded surface is studied.

采用图像分维探讨了腐蚀图像特征与表面腐蚀坑分布特征的关系。