The carbonyl group tend to align in the direction of the electric field of the polarized laser, resultantly, the molecular chain were found to tend to align perpendicular to the electric field of the polarized laser, that is to say, the molecular chain inclined to align perpendicular to the direction of LIPSS.

聚酰亚胺分子中的羰基在偏振激光电场的作用下，沿电场方向取向排列，而使整个分子链沿垂直于电场的方向取向排列。

Due to the key challenge for complicated techniques and preparation, there were few reports about ternary systems. A series of polyimide/SiO_2-TiO_2 hybrid films with different contents of inorganic particle were fabricated using tetraethoxyl silicane and tetrabutyl titanate as precursor in situ with sol-gel method and both phases in situ. Chemical structure and micro-morphology of hybrid films were studied by means of IR, SEM and XRD.

本文以正硅酸乙酯和钛酸四丁酯为前驱体，采用原位溶胶-凝胶法和两相原位同步法制备了一系列不同含量的聚酰亚胺/SiO_2-TiO_2杂化薄膜，利用红外光谱、扫描电镜和XRD观察了薄膜的化学结构和微观结构，并测试了薄膜的热稳定性、电击穿场强和耐电晕性。

A series of polyimide/SiO2-TiO2 hybrid films with different contents and weight ratio of inorganic particle were fabricated using tetraethoxyl silicane and tetrabutyl titanate as precursor by situ method. Chemical structure, micro-morphology and thermal stability of hybrid films was studied by means of SEM, IR and XRD, TGA was also tested.

以正硅酸乙酯和钛酸四丁酯为前驱体，采用两相原位同步法制备一系列不同含量及重量比的聚酰亚胺／SiO2-TiO2杂化薄膜，利用红外光谱、扫描电镜和XRD观察了薄膜的化学结构和微观结构，并测试了薄膜的热稳定性。

A series of polyimide/SiO2-TiO2 hybrid films with different contents and weight ratio of inorganic particle were fabricated using tetraethoxyl silicane and tetrabutyl titanate as precursor by situ method .

以正硅酸乙酯和钛酸四丁酯为前驱体，采用两相原位同步法制备一系列不同含量及重量比的聚酰亚胺/SiO2-TiO2杂化薄膜，利用红外光谱、扫描电镜和XRD观察了薄膜的化学结构和微观结构，并测试了薄膜的热稳定性。

The negatively charged sulfonic acid groups was readily introduced through the reaction of the terminal anhydride groups of the anhydride-terminated hyperbranched poly precursor with the amino groups of sulfanilic acid before chemical imidization.

研究表明，在聚合过程的聚酰胺酸阶段，采用过量的邻苯二甲酸酐或苯胺对超支化聚酰亚胺的端氨基或端酸酐基团进行的封端改性切实可行，改性反应可进行地相当彻底。

Disclosed is a polyimide resin having a glass transition temperature of 200-320 DEG C and containing a siloxane diamine residue, a fluorene diamine residue and a specific tetracarboxylic acid dianhydride residue at certain ratios.

本发明提供玻璃化转变温度为200～320℃，以特定比例含有硅氧烷系二胺残基、芴系二胺残基和特定四羧酸二酐残基的聚酰亚胺树脂。

PI-1 and PI-2 polyimide films were prepared from 3,3′,4,4′-benzophenone tetracarboxylic dianhydride and ODA确良by two-step polymerization under the thermal and mixed imidization procedures.

采用两步法首先合成聚酰胺酸，然后经热酰亚胺化和混合酰亚胺化工艺制备了BTDA/ODA型的PI-1 和PI-2两种聚酰亚胺薄膜。

A series of polys based on pyromellitic dianhydride, biphenylyl tetracarboxylic dianhydride, thiodiphthalic dianhydride bis benzene dianhydride and oxydiphthalic dianhydride were prepared in different solvents.

以所合成的AB_2单体为原料，合成了一系粘度较低、溶解性良好，带端酚羟基、苯甲酰基、乙酰基、氰代苯基和苯酰苯亚胺基的芳香族超支化聚酰亚胺，通过核磁波谱、红外光谱分析和元素分析对其结构进行确证。

With the increase of content of triamine monomer, the mechanical property of polyimide foams is improved, and the glass transition temperature of polyimide foams increases.

随着三胺单体含量的增加，聚酰亚胺泡沫材料的力学性能和玻璃化转变温度得到提高。

The successful synthesis of the aromatic triamine containing pyridine ring laid an important foundation for preparation of a novel hyperbranched polyimide.

这种新型含吡啶环芳香三胺单体的成功合成将为一类新型超支化聚酰亚胺的制备奠定重要的基础。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。