Since the production of carbon nanotubes synthesized by arc-discharge method contains impurities such as carbon nano-particles, amorphism carbon and graphite fragment, several purification methods were used to purify carbon nanotubes. It is found that with oxidation method in air, we can easily get purified carbon nanotubes.

由于用电弧放电法合成出来的纳米碳管产物中除了有纳米碳管外，还含有一些纳米石墨颗粒、无定形碳和石墨碎片等，因此本文对用电弧放电法合成出的纳米碳管进行了多种方法、探索性的提纯研究，实验结果发现，利用大气氧化法对纳米碳管进行提纯效果好，设备简单，是一种方便实用的方法。

Abstract］ Objective To Treating the nano-SiO2 particle by silicon coupling reagent, functionalize the SiO2 by making double bond on its surface. Polymerizing on the surface of nano-SiO2 surface by the method called emulsion polymerization, the nano-SiO2 is covered by polymer to get the PMMA-KH-570-nano-SiO2 complex material. Test the surface structure of the surface of nano-SiO2 by FTIR, and test sort of its mechanical performances.Comparing the treated nano-SiO2 which is directly dispended in the PMMA emulsion with the SiO2 without any treatment, we are trying to find an effective method which can not only increase the dispersion of SiO2, but also improve the mechanical performance of the artificial teeth.

目的 通过硅烷偶联剂KH-570处理SiO2纳米粒子，向其表面引入双键使其功能化，采用乳液聚合的方法在SiO2纳米粒子表面进行接枝聚合，实现高分子对SiO2纳米粒子的表面包覆处理，制得PMMA－KH-570－SiO2纳米复合材料，采用FTIR对SiO2纳米粒子表面结构进行了表征研究，并且测定了它的多种机械性能，与表面处理过的SiO2纳米粒子直接分散至PMMA乳液中制得的复合材料、未添加任何增强物质的空白组进行比较，探索一种能够提高SiO2在基体中的分散性，为义齿复合材料的研究和开发提供理论依据和参考。

The biomechanical tests showed that two kinds of artificial bones had not significant difference on compressive strength and Young\'s modulus(P＞0.05),while the flexural strength of nano-nacre artificial bone was less than the control group(P＜0.05).3.The results of CCK-8 showed that the difference were not significant in each group,the proliferation of osteoblast reached the peak at the 5th day;7 days after being co-cultured,the total protein content of study group was higher than control group and blank group(P＜0.05),while the difference between control group and blank group was not significantP＞0.05The difference of alkaline phosphatase activities among three groups was not significant(P＞0.05The SEM view showed that osteoblast attached and grew well in two kinds of artificial bone.4.X-ray photography showed that two kinds of powder started to degrade in 2 weeks;this phenomenon became more appear in 4 weeks,nano-nacre powder degraded faster than micron-nacre powder,while the hole shadow was easy to be found;in 8 weeks,all the femoral holes recovered and returned to normal bone mineral density in all groups.Analysis of tetracycline fluorescent double marks in the hard tissue grinding slices indicated that new bone grew fastest around the bone defect area in study group,while most slowly in blank groupP＜0.05 SEM(scanning electron microscope observation showed that nano-nacre powder degraded more quickly.The same result can be found through the demineralized sections morphometric analysis,and both of the composite artificial bones made from those two kinds of nacre powder had the good connection with the adjacent tissue in rats body without apparent inflammatory response.5.X-ray photography showed that rabbit\'s bone defects healed faster in study group since NNAB implanted than in control group since MNAB implanted.At 24 weeks after operation,bone density in radial defects had nearly accessed to the normal area,while lower in control group,and turned up nonunion in blank group;The checking of BMD showed that results in study group were higher than those in control group at 8,16 and 24 week(P＜0.05), and the difference between the BMD values in study group at 24 week and those in blank group was not significant(P＞0.05).The gross specimens showed satisfactory histocompatibility both in study group and in control group,with bone tissue growing from two sides into the center of implanted materials; Normal slices in HE stain and hard tissue grinding slices in Stevenel\'s blue/Van Geison\'s picro-fuchsin stain showed that the bone growth tendency was better in study group than that in control group,and the medullary cavity had been penetrated to the implanted materials in study group at 24 week;Analysis of tetracycline fluorescent double marks in the hard tissue grinding slices indicated that new bone in both groups grew fastest 8 weeks after surgery,while slow down at 16 week.

纳米珍珠层/消旋聚乳酸复合人工骨与微米珍珠层/消旋聚乳酸复合人工骨分别与成骨细胞共培养后，其各时间点CCK-8法检测值与空白对照无显著差异(P＞0.05)，成骨细胞均在第5天达到增殖高峰期；培养7天后，实验组细胞蛋白含量高于对照组及空白组(P＜0.05)，后两者之间则无显著差异P＞0.05碱性磷酸酶活性在三组间均无显著差异(P＞0.05电镜下可见成骨细胞在两种人工骨上都有良好生长贴附能力。4.X-ray显示两种粉体在大鼠股骨骨洞植入第2周时都开始出现了降解，第4周时更为明显，纳米珍珠层粉较之微米珍珠层粉降解更快，而空白对照组骨洞阴影仍可见，至8周时，则所有组骨洞均己闭合修复，X-ray下已不可见原钻孔痕迹，恢复正常骨质密度；硬组织磨片四环素荧光双标记结果显示纳米珍珠层粉植入组较其余两组在骨缺损区周围新骨生长速度更快，空白组速度最慢P＜0.05电镜观察及常规脱钙切片亦可见到纳米粉体降解较快；由以上两种原材料制得的纳米珍珠层/消旋聚乳酸复合人工骨与微米珍珠层/消旋聚乳酸复合人工骨在大鼠体内均与周围组织结合良好，无明显炎症反应。5.X-ray显示纳米珍珠层/消旋聚乳酸复合人工骨植入兔桡骨缺损区后其骨愈合速度较对照组微米珍珠层/消旋聚乳酸复合人工骨植入的快，至植入术后24周，实验组骨缺损区接近正常骨密度，对照组骨缺损区密度较低，空白组则呈现骨不连状态；骨密度测量结果显示术后8周、16周、24周实验组的骨密度值高于对照组(P＜0.05，24周实验组的骨密度值与术前所测得的正常值无显著性差异P＞0.05动物取材大体所见均显示组织相容性良好，骨组织逐渐由植入材料两端向中央生长；常规切片HE染色及硬组织磨片Stevenel\'s blue/Van Geison\'s picro-fuchsin联合染色均可见实验组骨缺损区长势优于对照组，至术后24周，实验组骨髓腔与材料已呈相交通状；硬组织磨片荧光显微镜下观察，两组材料在术后8周处于骨生长最快速时期，16周时速度开始减慢，术后4、8、16周时实验组的新骨生长速度均较对照组的快

The method comprises following steps: reacting hydroxylation carbon nano-tube successively with reagent containing halogen and hydrosulphide to prepare sulfhydryl carbon nano-tube; reflowing the sulfhydryl carbon nano-tube and platinum salts in polyatomic alcohol, processing in hydrogen atmpsphere to obtain sulfhydryl anchoring platinum / carbon nano-tube catalyst; reflowing the sulfhydryl carbon nano-tube successively with the hydrochloroauric acid and the platinum salts in polyatomic alcohol, processing in hydrogen atmpsphere to obtain sulfhydryl anchoring platinum-gold / carbon nano-tube catalyst.

本发明将市售羟基化碳纳米管先后与含卤试剂和氢硫化物反应得到巯基化碳纳米管。再将巯基化碳纳米管与铂盐在多元醇中回流，氢气氛中处理得到巯基锚固铂/碳纳米管催化剂。将巯基化碳纳米管依次与氯金酸和铂盐在多元醇中回流，氢气氛中处理得到巯基锚固铂-金/碳纳米管催化剂。

Result 1 Magnetic nanoparticles, magnetic nanoparticles modified with antisense oligodeoxynucleotide of human telomerase reverse transcriptase induced HL-60 tumor cells to apoptosis, we could see typical morphologic change of apoptosis cells: karyopyknosis, chromation"s condensing and aggregation in nuclear, forming crescent-shaped or annulus structures to lean on edge of cell nucleus"s membrane and posing apoptosis body by Atomic Force Microscope, Fluorescence microscope, transmission electron Microscope 2 There was a significant difference compared with control group(p.01), inhibition ratio had significant positive correlation with medication dosage and time ;during 0.8-8μM dosage amplitude, inhibition ratio accrescenced by dosages increasing. However, the inhibition ratio would decrease when dosage over 8-80μM.

结果 1 磁性纳米粒子、修饰有端粒酶反义寡核苷酸的磁性纳米粒子诱导HL-60细胞发生凋亡，原子力显微镜、光学显微镜、荧光显微镜和透射电镜下均观察到HL-60细胞呈现典型的凋亡细胞的形态变化：细胞核固缩，核内染色质浓缩、凝聚、形成新月形或环状结构紧靠在细胞核膜边缘，并形成凋亡小体。2 磁性纳米粒子、修饰有端粒酶反义寡聚脱氧核苷酸的磁性纳米粒子对HL-60肿瘤细胞的生长和增殖有明显的抑制作用，与对照组相比有显著性差异(p＜0.01)，在剂量为0.8-8μmol／L范围内，抑制率随剂量的增加而增加，当剂量超过8μmol／L时，抑制率反而下降；3 磁性纳米粒子、修饰有端粒酶反义寡聚脱氧核苷酸的磁性纳米粒子可增强p53基因的表达活性，引起DNA降解损伤，反向调节细胞周期活动，促使细胞从G0期进入G1期，抑制肿瘤细胞的生长。4 修饰有端粒酶反义寡聚脱氧核苷酸的量子点能通过内吞作用进入HL-60肿瘤细胞的细胞核，可以在细胞内进行定位和促进HL-60肿瘤细胞的凋亡。

Scanning electron microscopy,transmission electron microscopy,circular dichroism and small-angle X-ray diffraction were used to analyze the aggregation mode of CSG in the organogel phase.A hierarchical self-assembly model was proposed to explain the transition from molecular to primary and secondary structure.It is shown from our results that CSG can aggregate into a micellar fibril nanostructure with high length-to-width ratio which is bundled and entangled to form a three-dimensional(3D) network that immobilize the fluid component probably by surface tension.Moreover,sol-gel polymerization of tetraethoxysilane was carried out using CSG in the gel phase.

通过扫描电镜(ScanningElectron Microscopy，SEM)、透射电镜(Transmission Electron Microscopy，TEM)、圆二色谱(Circular Dichroism，CD)和小角X—射线衍射仪(Small-angle X-rayDiffraction，SAXRD)考察CSG分子自组装行为结果表明，CSG形成的聚集体具有多级结构：首先CSG通过手性堆叠自组装形成直径在9—10nm的细纳米纤维，这些细的纳米纤维再以不规则的六方堆积的方式进行排列，构成直径在40—100nm的粗纳米纤维(即细纳米纤维的&捆束&)，最后粗纳米纤维互相粘连形成三维网络状结构，使有机溶剂&固定&，从而形成凝胶；以CSG有机凝胶为模板，四乙氧基硅烷为前体，通过溶胶—凝胶聚合的方法制备了直径大约为100nm的二氧化硅纳米管。3。

In the dissertation the low-dimensioned orthovanadate nanomaterials such as Lanthanum orthovanadate (LaVO_4) nanorods, Cerium orthovanadate (CeVO_4) nanorods, Yttrium orthovanadate (YVO_4) nanorods and one-dimensional ammonium vanadate nanomaterials were chosen as the objects of study. Modern testing methods were used to study the preparation, structure and properties of low-dimensioned orthovanadate nanomaterials.

以LaVO_4纳米棒、CeVO_4纳米棒、YVO_4纳米棒等低维稀土钒酸盐纳米材料和一维钒酸铵纳米材料等为研究对象，采用现代测试手段对低维钒酸盐纳米材料的合成、结构和性能进行了深入研究，探讨了组成、结构及性能的相关性，分析了结构形成和性能优化的机理和规律。

The static experiment is done. In this paper, first I introduce some characteristics of the nano-fluids such as motion. The parallel laser is used to illuminate vertically the nano-particle producing dynamic speckle. The Laser speckle velocity is underlain by the fact that movement of a diffuse object illuminated by coherent light results in a random time variation of a speckle pattern observed in both the image plane and the diffraction field.

在描述了纳米流体的基本特点，以及根据布朗运动理论纳米流体的运动特性的基础上，考虑到将采用激光垂直照射纳米流体，由纳米颗粒散射的光线将互相干涉形成散斑的测试方法，从理论上推导了纳米颗粒的运动速度和散斑运动速度的关系，得到了在菲涅尔衍射区域，散斑的移动速度等于纳米粒子的移动速度的结论。

Copper nanoparticles were modified by surface modifier, methyl - methylacrylate, and minified by use of fluid-flow comminuted method, the disper sity and dispersion stability of the modified copper nanoparticles as additive i n CD 15W/40 engine oil were evaluated by high velocity centrifuger; its morpholo gy and particle size were tested by TEM and XRD analysis; and its tribological p roperty in CD 15W/40 engine oil was investigated by ball on pan tribo-tester.

采用化学改性法与液流粉碎机械法对纳米铜微粒进行了表面改性和分散研究，采用高速离心机考察了表面改性后纳米铜微粒作为添加剂在CD15W/40柴油机油中的分散性及分散稳定性，采用TEM、XRD测试了表面改性纳米铜微粒的形貌及粒径大小，采用球盘磨损试验机考察了表面改性纳米铜微粒作为CD15W/40全配方调配油添加剂的摩擦学性能，用SEM、EDS观察了磨损表面的形貌、线扫描、面分布及元素含量，分析了纳米铜微粒在摩擦过程中的减摩润滑机理。结果表明：甲基丙烯酸甲酯化学改性结合液流粉碎方法处理后纳米铜微粒的粒径进一步均匀、细化，平均粒径为24nm，并在CD15W/40油中分散性好，悬浮稳定时间长。

The method takes an ethanol suspension of monocrystal tungsten trioxide (WO3) nano-plates as a precursor, and utilizes the habit that the nano-plate with high diameter-thickness ratio tends to be parallel to a substrate and the principle that solvent volatilization causes the oriented self-assembly of the nano-plate to prepare the tungsten oxide (WO3) nano film which is formed by overlapping the tungsten trioxide (WO3) nano-plates and oriented along the [002] crystallographic direction.

本发明涉及一种取向氧化钨纳米薄膜的制备方法，该方法以单晶三氧化钨(WO 3 )纳米片的乙醇悬浮液为前驱物，利用高径厚比的纳米片趋向平趟于基底的习性，以及溶剂挥发诱发纳米片取向自组装的原理，制得由三氧化钨(WO 3 )纳米片叠加而成的沿[002]晶向取向的三氧化钨(WO 3 )纳米薄膜。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。