索氏体

Temperature rang: 500～650℃, tempered organization is tempered sorbite.

回火温度范围为500～650℃，回火组织是回火索氏体。

The characteristic of the new process is heating under Acltemperature for suitable time to change lamellar Sorbite to ginger-likeSobite.

介绍了一种工具钢在稍低于Acl温度下不太长时间加热，使片状索氏体不完全球化，形成姜块状碳化物的工艺。

The main methods improving the strength of galvanized wire for bridge cable are to improve the strength of sorbite wire rod, increase drawing hardening effect and decrease strength lose in the course of galvanizing.

提高桥梁缆索镀锌钢丝强度的主要方法是提高索氏体盘条的强度、提高加工硬化效果和减少热镀锌过程的强度损失。

Through adding micro-amounted Cr,V to steel and using proper controlled cooling technology in producing high carbon wire rod,the more complete sorbite and higher properties are obtained and the need of producing high quality stranded wire can be met.

在生产高碳硬线时，通过添加微量合金元素Cr、V 并配以合适的控冷工艺，可获得较完全的索氏体组织和较高的机械性能，满足更高级别的钢绞线生产要求。

Derived from high-temperature tempering tempering sorbite organizations.

高温回火所得组织为回火索氏体。

The results show that 82B wire rod brittle fracture is mainly caused by excessive inclusion,reticulate carbide,lower sorbite in the microstructure,and surface defect of wire rod.

结果表明，82B钢盘条脆断的主要原因是夹杂物级别超标、组织中出现网状碳化物、索氏体含量偏低以及盘条表面缺陷等。

The results showed that the best controlled cooling technology was the third test scheme, that is, some blowers with 100% opened angle, and the microstructure of the wire rod with best comprehensive mechanical properties was sorbite and a little of pearlite.

结果表明，最佳工艺是部分风机开口度为100%，盘条金相组织为索氏体+少量珠光体，综合力学性能最好。

The results showed that the junction area of the hi-Cr white iron-carbon steel cast-in casting consisted of the ferrite zone and the Fe,C,Cr-containing sorbite zone .

结果表明：高铬白口铸铁-铸钢镶铸铸件结合层为铁素体带和含有Fe、C、Cr的索氏体带组织构成。

By optimizing such process as refining dreg series and deoxidizing,mode of adding slagging raw materials,blowing Ar system,preventing nitrogen adding in refining process,adopting such process measures as controlling degree of superheat of smelten steel strictly,selecting suitable pulling speed and colling water quantity,using electromagnetism stir in continuous casting,the center carbon segregation index is at about 1.04 basic...

通过对精炼工序中精炼渣系和脱氧工艺选择、造渣原料的加入方式、吹氩制度、防止增氮等工艺的优化，在连铸中采用严格控制钢水过热度、选用合适的拉速和冷却水量、使用电磁搅拌等工艺措施，中心碳偏析指数集中在1.04左右，夹杂物尺寸变小、数量大为减少，疏松和缩孔均降低到0.5级以下，线材面缩率达到34%以上，大部分为41%~44%，索氏体体积分数达到91%，可顺利拉拔至0.3 mm。

To meet the inspecting requirements of sorbitic content of high carbon steel wire rods ,mancomputer interactive measurement was made by image analysis system on the basis of random statistical principleThe results shown that this method was accurate and reliabl

为适应对高碳钢盘条中索氏体含量的检测要求，本文提出通过图象仪运用随机统计原理进行人机交互测量，结果准确可靠。

With Death guitarist Schuldiner adopting vocal duties, the band made a major impact on the scene.

随着死亡的吉他手Schuldiner接受主唱的职务，乐队在现实中树立了重要的影响。

But he could still end up breakfasting on Swiss-government issue muesli because all six are accused of nicking around 45 million pounds they should have paid to FIFA.

不过他最后仍有可能沦为瑞士政府&议事餐桌&上的一道早餐，因为这所有六个人都被指控把本应支付给国际足联的大约4500万英镑骗了个精光。