粗糙表面

By using the KDMRF-1000F MRF polishing machine and KDMRW-1 water based MR fluid,one K4 flat work piece (80 mm in diameter) and one K9 sphere work piece (145 mm in diameter) were polished,experiments show that work piece one has a peak-to-valley value of 55.3 nm and a root-mean-square value of 5.5 nm;and work piece two has a PV value of 40.5 nm and a RMS of 5 nm,which indicates that the surface roughnesses of two work pieces have been improved obviously.

实验显示，样件一面形收敛到PV值55.3 nm，RMS值5.5 nm；样件二面形收敛到PV值40.5 nm，RMS值5 nm；样件的表面粗糙度均有显著改善。结果表明，磁流变修形技术具有高精度、高效率、高表面质量的特点。

The laser used for Raman excitation in the experiment would assist the etching process of Si in DHF and roughen the silicon surface.

研究了DHF腐蚀硅片时表面氢终端的变化过程，并指出表面微粗糙度随腐蚀逐渐增加。

The surface roughness is one of important parameters of surface quality evaluation.

表面粗糙度是评价表面质量的一个重要指标。

Surface roughness is one of the most important requirements in NC machining.

在数控加工中，表面粗糙度是衡量已加工表面质量的重要指标之一。

objective to study the effect of surface roughness on gingival epithelial cells attaching to titanium.

目的 研究表面粗糙度对龈上皮细胞在纯钛表面黏附情况的影响。

When the saturated vapor of pure R11 or R113 was condensed on the PF tubes under free convection conditions, the HTCs (based on the outside area of the base tube, the same be1ow) were 14 to 20 times those of the smooth tube because the condensate surface tension made the condensate film on fin surfaces thin and the rough saw-toothed fin surfaces disturbed the boundary layer in the condeneate film.

纯R11、R113的饱和蒸气在大空间花瓣形翅片管上冷凝时，由于凝液的表面张力将翅片表面上的液膜拉薄以及粗糙的锯齿形的翅片表面扰乱了凝液膜内的流动边界层，传热膜系数（以坯管外表面积为基准，下同）是光滑管的14—20倍。

DFM three-dimensional phase picture of Ag layer showed that Ag layer stacked closely on surface of matrix, and its surface was scraggy.

DFM的三维立体相图分析表明：在环氧树脂表面激光诱导出的Ag沉积层呈紧密堆积，其表面粗糙不平。

Scratch test revealed that the adhesion strength between the GLC film and UHMWPE substrate was as high as 90N. The volume wear rate of GLC coated UHMWPE was 1.6×10^(-17)m^3/, which is 19 times reduced.

结果表明：磁控溅射法制备的GLC薄膜与基体结合力大于90 N，且对表面粗糙度没有影响；表面镀覆GLC薄膜的体积磨损率为1.6×10^(-17)立方公尺/，是UHMWPE的1/19。

The surface of the shadow mask 1 facing the surface of the glass substrate 130 is roughened.

并对与掩膜(1)的玻璃基板(300)表面相对一侧的表面实施粗糙化处理。

This shear force increased with the roughness of the surface.

镀层表面越粗糙，垂直于氧化膜的切应力分量越大，表面裂纹和锡须生长也越多。

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面，更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值，分为几个相等的区间作为横轴，并将各区间内所测定值依所出现的次数累积而成的面积，用柱子排起来的图形，也叫做柱状图。