Glass powder plug porcelain glaze, sealant, connector sealant, fine grained alundum powder, glass-ceramics and ceramics for electrostatic precipitator (ceramic rotating shaft, vibrating bar, wall bushing, porcelain insulation seat). Apart form being supplied to Sanle General Electric Corporation as the accessories of the military supplies, these products sell well in more than 20 provinces, cities and autonomous regions in China, and are exported to many countries and regions in Europe and North America, being well received by the users.

本公司主要生产：电真空玻璃制品，电真空陶瓷制品（A-75、A-95、A-94.3、A-99等）、玻璃粉（火花塞瓷釉、密封剂、接插件密封剂）、刚玉微粉、微晶玻璃及电收尘设备用陶瓷（瓷转轴、振打棒、穿墙套管、绝缘瓷座）等六大系列几十个品种的产品，产品除供三乐电气总公司军品配套外，还覆盖全国二十几个省、市、自治区，并远销欧美等多个国家和地区，深受用户欢迎。

The deformation mechanism is mainly the single-slip and cross-ship, the fracture mechanism is mainly the congregation of transgranular micro-hole, and large uniform deformation occurred before tough fracture, and therefore, the ability of plastic deformation and the mechanical properties of the material were remarkably improved. These fully indicate that the new melt-treatment developed in this work is an effective and advanced technique, and further testify that the improvement of metallurgical quality of the material is the key to enhance its mechanical properties, especially its plastic deformation performance. The results of tensile and compression tests at elevated temperature also indicate that the suitable hot-working temperature range is 400～450℃. 4. A steady-state plastic flow exists during the plastic deformation of the aluminum sheet used for pressure can at elevated temperature. A hyperbolic sine relationship can be satisfied between the steady-state flow stress and strain rate by introducing an Arrhenius term which involves some thermal activation parameters, i.

压力罐用铝材中的主要冶金缺陷为Al〓O〓夹杂物、气孔及富Fe杂质相；高效熔体处理显著改善了材料的冶金缺陷的存在形态，使含杂量明显减少、夹杂物尺寸变细小且分布均匀，富Fe杂质相变为细小、分布均匀的团球状或短棒状的复杂化合物，同时也明显细化了结晶组织；此外，由于高效熔体处理有效地减少了材料中裂纹萌生源数量，因而改变了材料的塑性变形微观过程及断裂方式，主要以单滑移和交滑移进行塑性变形，断裂方式为穿晶微孔聚集型，韧性断裂前产生了大量的均匀变形，不易出现变形失稳，从而显著提高了罐用铝材的塑变能力和力学性能。

By using the band mixing tunnelling resonant theory in quantum well and the Monte Carlo simulation,the static and dynamic performances of GaAs/AlAs heterostructure intervalley transferred electron devices are investigated.

半导体超晶格国家重点实验室，北京 100083；南京电子器件研究所，南京 210016 使用量子阱能带混合隧穿共振理论及Monte Carlo 模拟方法计算了GaAs/AlAs 异质谷间转移电子器件的静态和动态工作特性。

Rutilated Quartz: Crystal in the metal containing titanium dioxide is the most clan Need Rutilated crystal, is made crystal king, is the company line number of the natural power of decision-makers the best wearing stones.

发晶：在含有金属晶体二氧化钛是最需要发晶族晶体，晶体是由国王，是天然的决策权，公司行号决策者最好穿石头。

Through the observation via scanning electron microscope,we can discover that chips mainly have three types of micro-shapes like acicular,massive and squamose,its formation corresponds to PBX macro-fracture which caused by the nucleation and growth of crack and mainly embodied as transgranular fracture of explosive particles.

利用SEM观测发现PBX切屑主要有针状、块状和鳞片状三种细观形态，切屑的形成体现为裂纹的成核扩展导致的宏观断裂，并主要表现为炸药颗粒的穿晶断裂。

The nanocrack is a crack in nano size withingrain and it may cause transcrystalline fracture.

纳米级裂纹是晶粒中纳米大小的裂纹，它可能是导致穿晶断裂的裂纹。

The results showed that the rupture is transcrystalline cleavage cracking by hydrogen embrittlement basically,i.e.cathodic stress corrosion cracking.

指出管件破裂基本上属氢脆引起的穿晶型解理开裂，即阴极型应力腐蚀破坏。

The results show that the steel in different solution has better performance of anti-hydrogen induced cracking,there is no cracking inside the steel; micro-cracking on the specimen surface mainly nucleates at pitting corrosion pits and expands along the polygonal ferrite; the expansion mode is mostly transgranular type, and the expansion terminates in acicular ferrite.

研究结果表明：该管线钢在两种溶液中均具有较好的抗氢致开裂性能，试样内部没有发现裂纹；试样表面的微裂纹主要在点蚀坑处形核并沿多边形铁素体扩展，扩展模式多为穿晶型，并终止于针状铁素体。

I do alloy plant professional system Die: stranding mode (threading die, in lane Die, Die lead), straighten die, extrusion die, Extrusion Die (Aguilar-line), the drawing module, extubation Die, Die cold pier, profiled die; Diamond Die: Natural Diamond Die, Die polycrystalline, imports polycrystalline module, and to match production with the various models of Roberts powder.

我厂专业制做合金模具：绞线模（穿线模、过线模、引线模）、调直模、挤压模、挤塑模、拉丝模、拔管模、冷墩模、异形模具等；钻石模具：天然金刚石模、聚晶模、进口聚晶模；并生产与之相匹配的各种型号拔丝粉。

The grains of sintered body were enlarged and the phenomena of particle pulling-out decreased with increasing alumina content. ZrO〓/Al〓O〓 sintered composite body could reduce the alumina grain size dramatically.

当ZrO〓含量较多时，烧结体颗粒较小，晶粒拔出现象明显，随着Al〓O〓含量的增加，晶粒长大，颗粒主要是穿晶断裂。

Fancy gold-plated dangling earrings with facetted White Opal crystals.

花式镀金悬垂耳环与facetted白欧泊水晶。

This essay chooses the study aim from biology teachers in middle school in Shi Jiazhuang which tells us that most of the middle school biology teachers in Shi Jiazhuang have the"burnout", lower successfulness, individualize.

本文选取石家庄市初中生物教师作为研究对象，运用问卷调查的方法对石家庄市初中生物教师职业倦怠的现状进行调查，调查结果发现，石家庄市初中生物教师这一群体普遍存在职业倦怠，情感枯竭程度偏高，成就感偏低，去个性化程度最为严重。