碱硬锰矿

The single phase solid solution of hollandite solid-soluted cesium was synthesized in Cs2CO3, BaCO3, Al2O3 and TiO2 as raw materials by high temperature solid phase reaction.

以cs2CO3、BaCO3、Al2O3和TiO2为原料，通过高温固相反应，合成了单相的固溶Cs的碱硬锰矿固溶体。

Strontium-doped solid solution of hollandite was successfully prepared using strontium carbonate (SrCO3), barium carbonate (BaCO3), alumina (Al2O3), and titanium oxide (TiO2) as raw materials by designing formulas and high temperature solid phase reaction.

以碳酸锶(SrCO3)、碳酸钡(BaCO3)、氧化铝(Al2O3)和二氧化钛(TiO2)为原料，通过配方设计，用高温固相反应合成掺锶碱硬锰矿固溶体。

The results show that under the conditions of 1 200 ℃,20MPa and strong deoxidized atmosphere hollandite-rich synroc can be well used for immobizition of cesium with loading of

研究结果表明，在1 200℃，20MPa和较强还原气氛条件下，热压制备的富碱硬锰矿人造岩石固化体可较好地固化137Cs废物，包容量为

Hollandite-rich synroc with different simulated ~(137)Cs separated from HLW is fabricated and tested.

利用富碱硬锰矿(Hollandite，BaAl2Ti6O16)作为主体矿相，制备了Cs包容量为3%~8%的富碱硬锰矿人造岩石固化体，测定了所制固化体的物理性能。

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面，更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值，分为几个相等的区间作为横轴，并将各区间内所测定值依所出现的次数累积而成的面积，用柱子排起来的图形，也叫做柱状图。