Alloy electroforming of nickel and manganese with average grain sizes below 100nm were carried out.

开展了镍锰合金纳米晶电铸研究，获得了晶粒尺寸在60-100nm范围的镍锰合金电铸层。

SEM is used to observe the morphology of the samples after the corrosion test, and the effects of ZrO2 concentration on the corrosion resistance of the nano composite electroforming deposits are analyzed, and its corrosion resistance mechanism is discussed.

用SEM观察了各种样品腐蚀后的表面形貌，分析了纳米ZrO2微粒复合量对复合电铸层耐蚀性的影响，同时对纳米复合电铸层的腐蚀机理进行了初步探讨。

So it usually needs to roughen the surface toimprove the bonding strength. But the coarseness was not used in this paper. The technique ofarc spraying zinc in advance and then arc spraying copper was put forward to solve the problemof bonding strength.

而本研究根据锌喷涂层具有较好的附着性，提出了在电铸层上先喷涂锌后喷涂铜的工艺路线，较好地解决了铜喷涂层与电铸层结合强度偏低的问题。

We also introduced spectrophotometer into the analysis of sulfamate type electrolete to measure the content of nickel sulfamate for the first time. This method is much easier than the conventional chemistry titration, it can be accomplished within one minute. Furthermore, it enhances significantly the precision of the measurement.

在电铸液分析中，我们首次将分光光度法应用于氨基磺酸盐型镍电铸液中氨基磺酸镍的测定，该方法较传统的化学滴定法操作更简单，它可以在1分钟内完成氨基磺酸镍浓度的测定，且大幅提高了分析结果的精确度，样品的消耗量仅为原来的千分之一。

In this paper, Ni-nano-lanthanum oxide (La2O3) composite deposit was obtained by electroforming from a nickel sulfamate solution containing La2O3 nanoparticles.

本文在氨基磺酸镍电铸液中加入一定量的稀土氧化镧(La_2O_3)纳米颗粒，制备了Ni-纳米La_2O_3复合电铸层。

In this thesis, the concentration of graphite powder in the liquid nickel sulfamate and current density are chosen as parameters for composite electrodeposition of nickel and graphite powder. In addition, after electrodepositing, the graphite powder is oxidized into carbon dioxide through heating process for obtaining porous structure. Filter devices of various specifications can be made by controlling the hole dimension of the porous structure.

本研究为了制作出多孔洞结构，将在氨基磺酸镍电铸液中以不同的石墨粉浓度及电流密度为参数进行复合电铸，并且经由加热处理使石墨氧化成为二氧化碳以制造出多孔结构，根据这些多孔结构的孔径大小可以获得各种规格的过滤结构元件。

The higher the concentration of manganese sulphamate in the electroforming electrolyte, and the lower the tem- perature of the electrolyte, the more manganese content is in the layers.

在复杂形状零件进行Ni—Mn合金电铸时，选择较低的电解液锰盐浓度、较高的电解液温度和合适的脉冲电流脉宽等工艺条件，有利于改善电铸层锰含量分布的均匀性。

The results showed that wear ratio of copper tool-electrodes electroformed with pulse current were obvious lowe...

结果表明，脉冲电铸铜电极可降低损耗，且在一定工艺条件下脉冲电铸电极具有优异的耐电蚀性能。

The influences of concentration of SiCp, temperature, pH value of the plating solution and current density on ratio of the electroformed layer were studied.

研究在Q235钢表面上复合电铸铁基SiCp摩擦材料的制备工艺，探讨了镀液中SiCp的浓度、电流密度、pH值和镀液温度对电铸层中SiCp含量和电铸层性能的影响规律。

A conformal anode of special construction is adopted to improve the uniformity of deposition distribution of alloy electroformed layers.

设计了一种可用于复杂回转形零件电铸的装置，为了改善合金电铸时沉积金属分布的均匀性，该装置采用了特殊结构的象形阳极并利用ANSYS有限元软件对象形阳极进行了精确的轮廓形状设计。

The split between the two groups can hardly be papered over.

这两个团体间的分歧难以掩饰。

This approach not only encourages a greater number of responses, but minimizes the likelihood of stale groupthink.

这种做法不仅鼓励了更多的反应，而且减少跟风的可能性。