This is directly related to the accumulation and elimination of electronic charge in the interface between ZnSe and electrode, which is accordance with the ρ〓-V curve.

晶体的C-V、I-V曲线反映了n-ZnSe半导体的电学特征。C-V、I-V曲线正向电压漂移与电极接触处电荷累积与耗尽有关，并在载流子浓度与电压的变化曲线上得到反映证实。

Furthermore, the structures and properties of Y-shaped CNTs are found to be related to the length of the CNT branch.

当分支管长度大于1 nm时，Y型碳纳米管的结构、能隙和电学性质均出现周期性振荡变化的趋势。

The results indicated that their dielectric tangents were relatively smaller than those reported in other articles.

经电学性能测试，三种陶瓷的介电损耗与相应的其他文献报道的数据相比，均较小。

The ethylene-vinyl acetate copolymer formulations containing nanoscale aluminum hydroxide as a flame retardant,organic montmorillonite and zinc borate as synergists were prepared by melt-blending.

采用熔融共混挤出法制备纳米氢氧化铝为主体的阻燃乙烯-醋酸乙烯共聚物材料，研究了阻燃增效剂纳米有机蒙脱土与硼酸锌对复合材料阻燃、力学与电学性能的影响。

In fact, we had obtained polythiophene films with high quality in BF3 ethyl ether, a kind of solvated Lewis acid. The electric conductivity of the polythiophene film is a bout 100 Scm-1. and the tensile strength is as high as 140 MPa, which is forty percent higher than that of aluminum.

事实上，我们已经从一种Lewis酸催化下的低电位聚合体系—噻吩/三氟化硼乙醚溶液中得到了高质量的聚噻吩薄膜，在降低了的聚合电位下得到的聚合物具有优异的力学及电学性能：拉伸强度达140MPa(比金属铝高40%)，电导率则可达100Scm-1。

In fact, we had obtained polythiophene films with high quality in BF〓-ethyl ether, a kind of solvated Lewis acid. The electric conductivity of the polythiophene film is about 100Scm〓, and the tensile strength is as high as 140Mpa, which is forty percent higher than that of aluminum.

事实上，我们已经从一种Lewis酸催化下的低电位聚合体系-噻吩/三氟化硼乙醚溶液中得到了高质量的聚噻吩薄膜，在降低了的聚合电位下得到的聚合物具有优异的力学及电学性能：拉伸强度达140MPa（比金属铝高40％），电导率则可达100Scm〓。

The effect of sintering temperature on the density, structure and the electric properties of NKN ceramics were investigated.

研究了烧结温度与NKN陶瓷的密度、结构以及电学性能的关系。

In this paper, the effects of oxygen pressure and dopant ratio on the resistivity and optical transmittance of ZnO:Al films by pulsed laser deposition have been investigated.

结果表明：掺杂比、氧分压强影响着膜的电学、光学性能和膜的结晶状况。

The effects of oxygen pressure and dopant ratio on the resistivity and optical transmittance of ZnO:Al films by pulsed laser deposition have been investigated.

结果表明：掺杂比、氧分压强影响着膜的电学、光学性能和膜的结晶状况。

In the present work, pale-yellow KLN crystals with high-quality are grown successfully by a modified Bridgman technique for the first time, the crystallizing behavior, defects and properties of KLN crystals are studied also.

本课题首次将坩埚下降法生长技术用于KLN晶体的生长研究，成功地生长出浅黄色、高质量KLN晶体，同时研究了KLN熔体的析晶行为以及晶体缺陷，测试了KLN晶体的电学和光学性能。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。