熟料

Clinker compositions were designed and burned at 1350℃, 1400℃, 1450℃ and 1500℃.

设计了18个熟料组成并分别在1350℃，1400℃，1450℃和1500℃下进行煅烧，对所得熟料作游离氧化钙及X射线衍射测试。

The effect of different superplasticizer on clinker grinding efficiency and its compatibility with clinker were studied.

研究了不同类型的高效减水剂对水泥熟料的助磨作用，并进一步探讨了不同水泥熟料与高效减水剂之间的相容性问题。

The results show that the cement clinker are easily calcined and well developed into regular and integrated crystal.

结果表明，水泥熟料有较好的易烧性，熟料主要矿物发育良好。

Using B Grade bauxite as bone material and A Grade bauxite as powder,different binder composition castable for permanent lining fo fundish were studied,with cyanite and sillimanite as expansion additives and Zimujie clay as sinter additive and plastic additive.

以B级高铝矾土熟料为骨料，A级矾土熟料为基质料，同时加入蓝晶石、硅线石为膨胀剂，紫木节粘土为烧结剂、塑化剂，研究了分别采用硅灰、高铝水泥、水玻璃、复合结合剂等为结合剂的不同配方组成的浇注料。

The all raw meal ingredient and all grog ingredient of cordierite and ferrites were prepared,and the composite ceramics was prepared.

用铁氧体生料和堇青石生料的复合及铁氧体熟料和堇青石熟料的复合，制备了堇青石红外辐射复相陶瓷。

Speed up the development of facilities for new type processing cement with daily output of 2,000 ton cement grog and encourage establishment of large cement grog bases with capacity of above 4,000 ton per day.

加快建设一批日产水泥熟料2000吨以上的新型干法水泥生产装置，鼓励建设日产4000吨以上的大型熟料基地。

After 6 h hydration, a great number of needlelike crystals of hydration products were formed and surrounded the clinker grains.

水化早期，水化产物均匀覆盖于熟料颗粒表面，至6 h时，熟料颗粒周围形成大量的细针状水化产物晶体。

The real content of mineral in each cement clinker was measured with the method of chemical extraction , the mineral configuration of each clinker was analyzed by microscope petrographic analysis, and then the effect of composition and configuration of clinker on cement strength was studied.

采用化学萃取法检测了各熟料中的矿物实际含量，采用反光显微镜岩相分析法分析了各熟料的矿物形态，分析了熟料矿物组成及矿物形态对水泥强度的影响。

The company's automation and control products in the CX system of centralized control shaft are Jiantong Nanjing Cement JT energy saving and environmental protection-type large-diameter shaft (§3.8x8.5 meters,§4.0x8.5 meter shaft) fixed-point matching products applies to Nanjing Jiantong Guantang Ltd., Guangxi Pingguo Wanganui Cement Co., Ltd. all JT energy saving and environmental protection-type on large-diameter shaft; the company independently developed CX-JM15C coal environmental protection agents, dedicated to catalytic coal cement shaft kiln calcined, and its coal effect and Kiln Burning can improve working conditions, improve clinker production quality, reduce cost of production of clinker 3-5 yuan / ton clinker; company also provides enhanced FGF efficient composite cement grinding aids, Products has two kinds of solid and liquid, has good strength and grinding role.

公司的自动化控制系列产品中的CX立窑集中控制系统是南京建通水泥公司JT节能环保型大直径立窑（Ф3.8x8.5米，Ф4.0x8.5米立窑）的定点配套产品，应用于南京建通官塘有限公司、广西平果万佳水泥有限公司等所有JT节能环保型大直径立窑上；公司自主开发的CX-JM15C环保节煤剂，专用于水泥立窑催化节煤煅烧，其节煤效果明显，并能改善立窑煅烧工况，提高熟料产质量，降低熟料生产成本3-5元/吨熟料；公司还提供FGF高效复合水泥增强助磨剂，产品有固体和液体两种，具有良好的增强和助磨作用。

Contact model was established to quantitatively calculate the preparation of cement with different clinkers of varying strength by means of mathematical modeling of blending materials. Reactivity of clinkers from varying kiln system can be assessed by this model to produce cement.

采用混杂材料的数学模拟理论，建立了可以定量计算不同强度的熟料混合磨制水泥的接触点模型，应用该模型方法可以比较不同窑型熟料混合粉磨制备水泥时掺加熟料的活性效应。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。