The rhombohedral pattern R of alite stabilized by certain impure ions is more hydrated.

阿利特或硅酸三钙，(C3S)固溶体是水泥熟料中最重要的矿物，某些杂质离子可以稳定其多晶型中的三方R型，具有较高的水化活性。

The influence of ZnO on the formation of minerals and the temperature range for the coexistence of C4A3S and alite in clinker containing calcium sulphoaluminate 4CaO.

借助差热分析、X射线衍射及化学分析等，研究了ZnO对含硫铝酸钙的硅酸盐水泥熟料中阿利特和硫铝酸钙矿物形成及共存温度范围的影响。

The results showed that compared with traditional fluorite and phosphorous slag, phosphorous slag composite mineralizer was effective on reducing amount of f-CaO in cement clinker and improving burnablity of raw meals, but the effect was still obvious when sintering temperature and sintering time were increasing. The analysis of XRD, SEM and petrographic structure showed that phosphorous slag composite mineralizer decreased viscosity of liquid, promotes the formation of Alite in clinker and improves crystal form and size of minerals.

结果表明，与传统的萤石和磷渣矿化剂相比，磷渣与萤石复合的矿化剂可有效降低水泥熟料中游离氧化钙的含量，改善生料的易烧性；在燃烧温度与时间增加的情况下，改善作用仍然明显；通过XRD、SEM与岩相结构分析表明，磷渣与萤石的复合矿化剂降低了液相的粘度，促进了A矿的生长，对矿物的结晶形态有改善作用，有利于晶体尺寸的生长发育。

Effect of K2O and Na2O on the formation of alite－ sulfoaluminate cement clinker and the resultant cement was studied using limestone, pfa, clay and gypsum as raw materials.

以石灰石、粉煤灰、粘土、石膏等为原料，研究了 K2O、 Na2O对阿利特－硫铝酸盐水泥熟料矿物形成及性能的影响。

Using special alumine grog as aggregate and powder,adding active SiO2 fine powder and α-Al2O3 fine powder,using pure calcium aluminate cement as bonding agent,and adding effective additives,the prepared mixture was shaped by casting vibration,then a kind of lower cement and high alumina casting preformed block was made.

以特级矾土熟料为骨料和粉料，配以活性SiO2微粉和α－Al2O3微粉，以纯铝酸钙水泥作结合剂，并加入有效的外加剂制成混合料，经浇注振动成型，得到一种低水泥高铝质浇注料预制块。

Belite– calcium barium sulphoaluminate cement is a new type of cementitious material.

贝利特–硫铝酸钡钙水泥是一种新型的水泥材料，通过在贝利特熟料矿物体系中引入硫铝酸钡钙矿物，达到提高贝利特水泥早期强度的目的。

By combining calcium barium sul- phoaliminate with a belite mineral system.

贝利特–硫铝酸钡钙水泥是一种新型的水泥材料，通过在贝利特熟料矿物体系中引入硫铝酸钡钙矿物，达到提高贝利特水泥早期强度的目的。

By means of sem, it is found that in the portland cement clinker with high quality, the alite take the shape of trigonalrhombohedron,and belite shows the shape of irregular ovum, also with the parallel and cross twin-crystals.

借助于扫描电子显微镜发现优质硅酸盐水泥熟料中A矿呈复三方偏三角体形貌特征；而 B矿则呈不规则的浑圆状，并且从外层可看到平行双晶和交叉双晶共存。

Therefore, through the thermodynamic analysis and calculation of calcining active calcareousness rotary kiln in Pan Zhihua Steel Factory, the relationships among rotary kiln efficiency, output and gas-fired quantity could be concluded.

因此，本文通过对攀钢煅烧活性石灰回转窑进行了热力分析计算，得到了回转窑效率、产量、燃气量等之间的关系，通过对各影响参数的了解，可以掌握回转窑的热工制度，同时也可以掌握熟料的煅烧状况。

It is convenient for sinter to be leached, and the secondary reaction appears little. The slurry after sinter leaching is transferred into autoclave for desilicification at about 170℃, and the siliceous modulus of solution reaches more than 200. Then some lime is added for deep-desilication at normal pressure, the siliceous modulus of solution increases more than 600 even if the Al2O3 content is more than 200g/L.The SiO2 coefficient in hydrate garnet from deep-desilication is more than 0.28. Under conditions of the addition of seed and application of novel technology of carbonization, the contents of Na2O and SiO2 in product are less than 0.37% and 0.025%, respectively.

实验结果显示：烧成的熟料溶出条件宽松，二次反应程度弱；溶出浆液在170℃左右直接进行加压脱硅，脱硅后溶液的硅量指数大于200，再加入适量的石灰进行深度脱硅，即使溶液中氧化铝浓度超过200g/L时，精液的硅量指数也大于600，且得到的水化石榴石中二氧化硅饱和系数大于0.28；通过加入晶种和采用新的碳酸化分解工艺制度，产品中的SiO2 含量降至0.025%， Na2O含量小于0.37%；加入表面活性剂，不仅能将碳分母液蒸发至Na2OT浓度大于300g/L，而且还可有效减缓表面上结疤的形成速度。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。