熟料

The paper introduces in brief the service condition and invalidation type of chain in cement clinker apron converyor, and gives an overall analysis of wearing-out failure principle of the chain.

简要介绍了裙板输送机用水泥熟料链条的服役工况和失效形式；全面分析了该链条的磨损失效机理。

A high alite content Portland cement clinker was burnt at low temperature in laboratory and its performance was tested.

实验室低温烧制了一种高阿利特硅酸盐水泥熟料并测试了其性能。

Impurity ions doped in alite affect the structure and properties of alite .

水泥熟料矿物阿利特中固溶有多种杂质离子，这些杂质离子的存在影响到阿利特的微结构和性质。

It makes the solid state reaction speedy and the amount of solid solutions more formed in alite, thus improves the performance of cement clinker.

这一作用使固相反应速度加快，A矿固溶体数量增多，进而改善水泥熟料的性能。

In common clinker,quenching at all start temperature,the X-ray diffraction pattern showed all the character of the monoclinic alite.

不掺杂熟料中阿利特在所有开始温度淬冷，都呈现M型衍射特征。

Quenching at other lower start temperature,the X-ray diffraction pattern of alite was like the character of the MⅠpattern alite.

在其它较低温度开始淬冷，掺杂熟料中阿利特更多呈现MⅠ型晶体的衍射特征。

Hydration process and products, crystallization morphology and paste structure as wellas physical and mechanical properties of alite type oil well cement at pressure of 400kg/cm~2and temperatures from 75℃ to 300℃ have been investigated.

研究了在温度75～300℃和压力400kg/cm~2水热条件下硬化的阿利特型纯熟料油井水泥的水化产物、水化过程、结晶形态、水泥石结构及其物理力学性能。

Sulphoaluminate alite cements were successfully prepared from fly ash, bauxite and CaF2 as a fluxing agent by designing MG and MS values, i. e., the controlling of CaO and CaSO4 content, and the sintering at 1150℃, 1200℃, 1250℃, 1300℃ and 1350℃ respectively.

以粉煤灰为主要原料，CaF2为矿化剂，设计MG和MS值，控制CaO和CaSO4含量，分别在1150、1200、1250、1300和1350℃温度下烧制高胶凝性硫铝酸钙－阿利特复合矿相水泥熟料。

The alite content of the clinker exceeded 70%, and the well-burnt temperature below 1400 ℃, the 3d and 28d compressive strength reach to 42.8MPa and 65.8MPa.

该熟料中的阿利特含量高于70%，烧成温度≤1400℃。其3d抗压强度可达42.8MPa，28d抗压强度可达65.8MPa。

The alite content of the clinker exceeded 70%, and the well-burnt temperature below 1400℃, tile 3d and 28 dcompressive strength reach to 42.8MPa and 65.8MPa.

该熟料中的阿利特含量高于70％，烧成温度≤1400℃。其3d抗压强度可达42.8MPa，28d抗压强度可达65.8MPa。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。