Sb can combine with Cu and P to form a low melting point compound which lowers the melting point of binary Cu-8P eutectic alloy by nearly 200℃. Bi and Cu can create compounds with low melting point(270℃) distributing at the boundaries and that is the reason why the melting point of (Cu-8P)-Bi is lower than that of binary Cu-8P eutectic alloy. The eutectic cluster can be refined with the addition of Fe, and that is the reason why the addition of Fe can decrease the melting point of Cu-8P alloy. Two means of decreasing the melting point of Cu-8P are found.

一定量的Sb与Cu， P形成低熔点相，从而大幅降低了Cu-8P合金的熔点，使其熔点降低近200℃；加入少量Bi后， Bi与Cu在共晶团晶界上形成熔点为270℃左右的低熔点化合物，且Bi的加入明显细化Cu-8P合金共晶团，从而使Cu-8P合金的熔点降低；加入Fe能明显细化Cu-8P合金的共晶团，使层片间距由8μm减为2μm以下，并使共晶团由层片状向短棒状转变，虽然Fe与Cu形成熔点为806℃的高温相，但Fe的细化作用使得Cu-8P合金的熔点降低，但降低幅度不大。

The results show that melting point and fusion enthalpy of the fresh nano-aluminium powders are 649.7 ℃ and 3.7 kJ/mol in Ar, respectively, which are 10.3 ℃ and 7.09 kJ/mol lower than those of coarse-grained Al.

研究结果表明：在Ar气流中，新纳米铝粉的熔点为649.7 ℃，熔化焓为3.7 kJ/mol，分别比粗晶铝的熔点(660 ℃)和熔化焓(10.79 kJ/mol)低10.3 ℃和7.09 kJ/mol；在N2气流中，从20 ℃升温到800 ℃时，新纳米铝粉增重约为33%，熔点为648.8 ℃。

The furnace body is made ф2200×1500 the outer covering main body by the 12mm steel plate, lower part the furnace body 45° the installment has the sensor, the sensor orientation silicon steel plate is made the weight 2 ton induction iron cores by Wuhan Steel Corporation Silicon steel plate Factory production top gear's W-151 the cold rolling 0.35m/m, primary is made the water cooling coil by 10×10×2 the copper pipe, and installs the stainless steel water cooling restricting, the power frequency has the core smelting furnace's metal melt fluid namely for the sensor sencondary coil, the entire electric stove is a transformer actually, the necessary 6 grades from the pair regulating transformer, shift gears by the electricity cabinet control, the voltage may from low to high, divide 6 promotions to arrive at 380V, each grade of voltages are different, the output is also different, the furnace temperature along with the files position is also different, but the height is different, adapts smelts colored or the black and so on melting point different metals, and may make the new furnace lining to smelt diamantine drying furnace fireproof.

炉体由12mm钢板制成Ф2200×1500外壳主体，炉体下部45°安装有感应器，感应器由武钢硅钢片厂生产的最高档的W-151冷轧0.35m/m取向硅钢片制成重2吨感应铁心，初级由10×10×2铜管制成水冷线圈，并安装不锈钢水冷保护套，工频有芯熔炼炉的金属熔液即为感应器的次级线圈，整个电炉实际就是一个变压器，配套一台6档的自耦调压变压器，由电柜控制换档，电压可由低到高，分6级升到380V，每档电压不同，输出功率也不同，炉温也随档位不同而高低不同，以适应熔炼有色或黑色等熔点不同的金属，并可作新炉衬耐火冶金砂烘炉之用。

The furnace body is made ф2200×1500 theouter covering main body by the 12mm steel plate, lower part the furnace body 45° the installment has the sensor, the sensor orientation silicon steel plate is made the weight 2 ton induction iron cores by Wuhan Steel Corporation Silicon steel plate Factory production top gear's W-151 the cold rolling0.35m/m, primary is made the water cooling coil by 10×10×2 the copper pipe, and installs the stainless steel water cooling restricting, the power frequency has the core smelting furnace's metal melt fluid namely for the sensor sencondary coil, the entire electric stove is a transformer actually, thenecessary 6 grades from the pair regulating transformer, shift gears by the electricity cabinet control, the voltage may from low to high, divide 6 promotions to arrive at 380V, each grade of voltages are different, the output is also different, the furnace temperature along with the files position isalso different, but the height is different, adapts smelts colored or the black and so on melting point different metals, and may make the new furnace lining to smelt diamantine drying furnace fireproof.

炉体由12mm钢板制成Ф2200×1500外壳主体，炉体下部45°安装有感应器，感应器由武钢硅钢片厂生产的最高档的W-151冷轧0.35m/m取向硅钢片制成重2吨感应铁心，初级由10×10×2铜管制成水冷线圈，并安装不锈钢水冷保护套，工频有芯熔炼炉的金属熔液即为感应器的次级线圈，整个电炉实际就是一个变压器，配套一台6档的自耦调压变压器，由电柜控制换档，电压可由低到高，分6级升到380V，每档电压不同，输出功率也不同，炉温也随档位不同而高低不同，以适应熔炼有色或黑色等熔点不同的金属，并可作新炉衬耐火冶金砂烘炉之用。

When different materials mixed,the mixture will have a mixed melting point of mixture ,and the mixed melting point of mixture is different from the intersoluble solutions.we separate the intersoluble solutions by different melting piont of intersoluble solutions when separate temperature is flexible temperatureThese intersoluble solutions different in melting point, the method would make the high melting point material became solid while the low melting point material still be liquid by adopting cryogenic treatment with stirring so as to meet the requirement of purifying these two solutions.

这种分离方法的特点是利用两种互溶性物质具有不同的熔点，通过低温处理，并同时加以搅拌，震荡，使高熔点物质和低熔点物质形成固液混合体，再对固液混合体进行离心分离得到高熔点的固体和低熔点的液体，从而达到浓缩、提纯两种物质目的。

Through analyzing on the upper part of oil box and the design of the drawing die structure,the characteristics of the low melting point alloy were described,and discussed the characteristics of low melting point alloy die and the application in plate materical drawing process, the attention problems of die design were pointed out.

以分析油箱上体工艺特性和设计其低熔点合金拉伸模具结构为例，论述了低熔点合金材料的特点，介绍了低熔点合金模具的特点及其在板料冲压工艺中的应用，指出了模具设计应注意的问题。

The furnace body's ф2200×1500 outer covering main body is made of 12mm steel plate,installed sensor in the lower part 45°of furnace body, the sensor is weight 2 ton induction iron cores made from top gear's W-151 the cold rolling 0.35m/m made by Wuhan Steel Silicon steel plate Factory, primary manufactured the water cooling coil from 10×10×2 copper pipe, and installed stainless steelwater cooling cover, the power Frequency Induction melting Furnace 's metal melting fluid namely the sensor sencondary loop, the entire electric furnace is a transformer actually, match a 6 grades self regulating transformer, shift gears by the electric tank control, the voltage may from low to high,divide 6 grade to rise to 380V, each grade of voltage is different, the output power is also different, the furnace temperature is also different along with different grade,so can suit smelting colored or black and so on different melting point metals, and may use as new furnace lining fireproof to smeltdiamantine drying furnace.

炉体由12mm钢板制成Ф2200×1500外壳主体，炉体下部45°安装有感应器，感应器由武钢硅钢片厂生产的最高档的W-151冷轧0.35m/m取向硅钢片制成重2吨感应铁心，初级由10×10×2铜管制成水冷线圈，并安装不锈钢水冷保护套，工频有芯熔炼炉的金属熔液即为感应器的次级线圈，整个电炉实际就是一个变压器，配套一台6档的自耦调压变压器，由电柜控制换档，电压可由低到高，分6级升到380V，每档电压不同，输出功率也不同，炉温也随档位不同而高低不同，以适应熔炼有色或黑色等熔点不同的金属，并可作新炉衬耐火冶金砂烘炉之用。

In this kind of composite low-melting-point alloy can be transformed from solid into liquid in the range of processing temperature of polymers, which provides a possibility to change form and size of fillers during processing and design electrically conductive path in composite, The progress of studying on electrically conductive plastics and adhesives containing low-melting point alloy as conductive filler is reviewed.

其中的低熔点合金可以在聚合物加工的温度范围内转变为液态，为在加工过程中实现填料的形态转变和导电复合材料中导电通道的设计提供了可能。概述了以低熔点合金为导电填料的导电塑料和导电胶粘剂的研究进展，其中有关低熔点合金在加工过程中的尺寸和形态变化的研究工作值得关注。

The sheath-core ratio, compounding ingredient of the sheath ,chip drying process and drawing process were discussed for the composite spinning of low-melting point and normal polyester chips.

研究了低熔点聚酯切片的流变性能，以及低熔点聚酯与普通PET皮芯复合纺丝时的皮芯层复合比、皮层组分配比、切片干燥工艺和纤维拉伸工艺。

Nanocrystalline hexagonal VSi〓, with an average diameter of 35nm, was prepared via a reduction-silication route by the reaction of metallic sodium with vanadium tetrachloride and silicon at 650℃ in a molten salt system of magnesium chloride and sodium chloride. The sample had good oxidation resistance at 1000℃.

金属硅化物通常具有很高的熔点、较低的电阻率、很好的高温热稳定性，有些还具有奇异的光、电、磁、超导、催化等性能，因此是一类最富潜力的高温结构材料和电子材料。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。