焙烧

The process of infusion, drying and calcinations makes lanthanon oxide as rare earth absorbent .

通过浸渍———干燥———焙烧法制备预载镧氧化物稀土吸附剂，探讨了该吸附剂对水中磷的吸附性能。

Kunming University of Science and Technology have invented a new efficient exploitation of sulphide iron ore resources, and obtained a state invention patent.

这种新方法是采用合理的工艺流程和新药剂制备高纯硫铁矿精矿，将精矿焙烧制取硫酸和优质铁精矿，铁精矿可以直接炼铁，从而达到充分利用硫铁矿中硫和铁资源的目的。

The leaching ratio of copper from the copper slag, roasted at 680℃ for 4 hours, attains approximately 92% under the conditions of 2 mol/L sulfuric acid leaching for 2 hours at 70℃.

在680℃焙烧4h后，采用2mol/L硫酸于70℃浸出2h后可以达到良好的浸出效果，使铜的浸出率达到92%以上。

Dry at about 100 degree and put it into muffle furnace to heat for 2 to 6 h and get nano-TiO2 powder.

在100℃左右下烘烤干，使溶剂挥发，所得二氧化钛放入马福炉内焙烧2～6h即得纳米TiO 2 粉体。

The high-sulfur bauxite was pretreated in muffle furnace, rotary tube furnace and fluidized bed.

摘 要：采用马弗炉、旋转管式炉和流化床对我国高硫铝土矿进行焙烧预处理。

The chemical formula of the phosphor is SrMoO4:Eu. The method comprises the following concrete steps that: according to the molar ratio of 2:100:100 to 4:100:100, Eu2O3, MoO3 and SrCO3 solids are put into a mortar to be ground and fully mixed; an obtained product is placed in a crucible in a muffle furnace to be roasted for 3 to 4 hours at the temperature between 500 and 700 DEG C, and then a needed product can be obtained.

该荧光粉的化学式为：SrMoO 4 ：Eu 3 ，具体步骤为：将Eu 2 O 3 ，MoO 3 和SrCO 3 固体按照摩尔比为2∶100∶100～4∶100∶100的比例置于研钵中研磨，使其充分混合；将所得产物置于坩埚内放在马弗炉中于500℃～700℃的温度下焙烧3-4h，即得所需产品。

The method is to move the stoving from inside the pellet producing apparatus to one alone stoving furnace outside the pellet producing apparatus. Inside the stoving furnace, there are waveguide tube connected to microwave generator and conveying belt in the bottom, and the pellet is fed to inside cavity of the stoving furnace on the conveying belt, stoved by microwave quickly and discharged on the conveying belt to vertical pellet furnace for roasting.

该方法是将由人造球团矿加工设备内完成的烘干段工艺移出到设备外完成，在设备外单独设置有一烘干炉体，该烘干炉体内腔有波导管与微波发生器连接，在烘干炉体的底部有输送带，球团通过输送带送入烘干炉体内腔，利用微波发生器产生的微波对球团快速加热烘干，经烘干后的球团，通过输送带送至球团竖炉完成焙烧工艺。

The d 001 basal spacings of Ti-Na-MMT decreased with the increase of the calcination temperature.

随着焙烧温度的升高，晶面间距逐渐减少。

Many roasters stop the roasting process after the "first pop".

许多烘烤焙烧过程停止后，他说：&首先弹出&。

This paper address the preliminary knowledge about sateflow and the modeling method about safety interlocking loop base on sateflow and farther expatiate it with a example of prewarming burner of alumina hydrate furnace.

本文介绍了Stateflow的基础知识以及基于Stateflow的安全联锁回路仿真建模方法，并以氢氧化铝焙烧炉预热燃烧器作为具体实例进一步阐述。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。