Crisscross weld joints and butt weld joints of Ti80 alloy welded by handwork-argon-arc method were disposed by ultrasonic peening method.

采用超声波法对手工氩弧焊接的Ti80板材两种焊接接头进行了冲击处理。

The newly developed products: welded joints, male connector, such as gas and natural gas pipelines and accessories.

新开发的产品有：焊接接头，螺纹接头等煤气，天然气管道配件。

Through metallographic examination and microanalysis, it can be observed that at the weld interface of the joints there is a decarbonized layer on the S25C steel side and a carburized layer on the SUS405 steel side.

金相及显微分析可见，在焊接接头的结合界面上，S25C钢一侧存在脱碳层，SUS405钢一侧存在增碳层，这是造成接头组织分布及硬度分布不均匀的主要原因。

The microstructure of joints showed comparatively fine equiaxed grains and a narrow heat aff...

显微组织分析表明：搅拌摩擦焊接接头具有细小的等轴晶粒和狭窄的热影响区，阻碍了滑移带的形成和裂纹的扩展，从而提高了接头的疲劳性能。

All in all, under the factors above, the depleted zone in pearlite steel would crack fragilely for formation of creep-flaw in low stress during operating at high temperature before designed expiration date.

异种钢的焊接接头在高温运行中，在高温和应力的作用下，珠光体的脱碳层会产生蠕变裂纹，发生低应力脆性断裂，从而导致接头的早期失效。

The res ults of arc-starting and welding tests for titanium alloy are also presented in detail in the paper . Tensile strength of welding joints has reached the demands of we lding standard, esp. no spatters on back weld are obtained in contrast w ith EBW.

文中详述了空心阴极焊枪设计、引弧试验情况及钛合金焊接工艺试验，结果表明焊接接头拉伸强度达到标准的要求，特别是与电子束焊相比，焊缝背面无焊接飞溅。

Measures of improving for low temperature toughness by selecting the welding materials and strictly controlling the welding process for welded joints of low temperature low-alloy steel, nickel alloy steel and chrome-nickel austenitic stainless steel for low temperature pressure vessels were summed up.

为了改善工作于低温环境的压力容器用低合金低温钢、镍合金钢和铬镍奥氏体不锈钢的焊接接头低温韧性，而采取改进焊接材料、严格控制焊接工艺的措施。

The steel is provided with the characteristics of ultra fine grain and ultra purity, so the result has the excellent mechanical properties with combination of strength and toughness. DC flash butt welding is a kind of solid joining method with high efficiency. The micro characteristics of HAZ affect the weld joints greatly.

直流电阻闪光对焊是一种高效的固态连接方法，其焊接热影响区的显微特性对焊接接头的性能有着重要的影响，由于这种方法与熔化焊具有本质的区别，所以对超细晶粒钢的闪光对焊焊接适用性研究会有助于推进新一代钢铁材料的研究和应用开发。

The results show that, the coefficients of welded joints are both greater than 0.9, but the yield strength of weld joint filled with Al-Mg-Zr-Sc welding wire is greater 100 MPa than that of filled with Al-Mg-Zr welding wire. It indicates that the Al-Mg-Zr-Sc welding wire is the best alteration of filling materials to weld of Al-Mg-Sc alloy.

但采用Al-Mg-Zr-Sc合金焊丝为填充材料时，焊缝晶粒组织明显细化，熔合区形成的细小等轴晶层提高了基材与焊缝填充材料的结合力，焊接接头的屈服强度比采用Al-Mg-Zr合金焊丝为填充材料时提高了100 MPa，显著提高了Al-Mg-Sc合金焊接构件的许用强度，因此焊接Al-Mg-Sc板材更宜采用Al-Mg-Sc-Zr焊丝。

The welded joint of deeply rolled steel ,which was work-hardened, has softening zones of reerystallizaton. The tensile strength of the joint is not affected if the softening zones are narrow.

深度轧制钢激光焊接接头出现再结晶软化区，当软化区宽度较窄时，不影响整体接头强度。

It has been put forward that there exists single Ball point and double Ball points on the symmetrical connecting-rod curves of equilateral mechanisms.

从鲍尔点的形成原理出发，分析对称连杆曲线上鲍尔点的产生条件，提出等边机构的对称连杆曲线上有单鲍尔点和双鲍尔点。