Transparent YGO ceramics were prepared by sintering at 1670℃ for 2h in vacuum using the powders calcined at 1100℃. The YGO ceramics shows a high in-line transmittance of 74.6% in the visible-light region, much higher than that of transparent Y2O3 ceramics prepared by the same process.
采用所制备的YGO:Eu纳米粉体,在1670℃真空烧结2h可获得透光性良好的透明陶瓷,样品在可见光区的最高透过率可达74.6%,高于相同工艺条件下制备的氧化钇透明陶瓷。
-
The mechanism of the fracture of radially oriented toriods of sintered SmCo_5has been investigated. It showed that the fracture of radially oriented toroids af-ter sintering may be caused by wild anisotropy of thermal expansion.
研究SmCo_5辐向取向烧结环体的断裂机制指出:SmCo_5的强烈各向异性的热膨胀性质决定了辐向环在烧结后的断裂。
-
According to the future trend of iron ore and the comparison of process and metallurgical properties, the hybrid pelletized sinter can replace the now compound burdens, it is the future trend of the blast furnace burden constitution.
从含铁原料的发展趋势和工艺过程以及冶金性能的比较,混合球团烧结矿完全可以替代现有的复合炉料,它是高炉炉料结构的发展方向。
-
It is found that the density of sinters is better when the temperature raise. The conductivities of sinter by addition of 5% polyethylene glycol than that of 1% polyethylene glycol.
结果表明:当烧结温度提高时,陶瓷样品的致密度提高,添加5%聚乙二醇制备的陶瓷样品的电性能比添加1%聚乙二醇制备的陶瓷样品高。
-
Farther X-Ray diffraction, SEM, spectro-meter analysis reveals that the element Cr which sinters and induces phase transformation leads to relatively smaller oxide weight-loss of 40Cr, then the oxidation laws of two steels are surmarized.
用XRD、SEM、EDS等方法对两种钢的氧化皮进行分析,得出40Cr钢氧化失重率相对减小的原因是因为Cr合金元素的烧结引起的相变所致。
-
All the products are produced with strict technology control, rigid quality control to meet the high requirement of clients and advanced world standard. The main product-Taishan ceramic roller is Chinese famous ceramic brand.Shandong famous brand product. It is also the unique alternative ceramic roller for silicon carbonate. The company is the unique ceramic roller enterprise whose products can be suitable for high-temperature sintering, oxidizing flame and reducing flame of daily-use ceramics.
本公司所有产品皆以最严格工艺控制、最严密品质检测,保证所有产品都能符合客户严格的使用要求,并达到世界第一的水准,其主导产品--泰山陶瓷辊棒,是唯一可替代碳化硅的陶瓷辊棒,是目前国内唯一一家能达到日用陶瓷高温烧结、氧化焰、还原焰皆适宜的陶瓷辊棒生产企业。
-
For example, some primary and secondary copper smelting plant is still in use behind blast furnace process, sulfur dioxide utilization rate of only 65%; primary and secondary lead smelting enterprises, commonly used sintering pot lead smelting process, flue gas concentration is low, can not use the sulfur into the atmosphere each year up to 25 million tons.
例如,一些中小学炼铜厂仍处于落后高炉使用过程中,二氧化硫的只有65%的利用率,小学和中学铅冶炼企业,普遍使用的烧结锅炼铅工艺,烟气浓度低,可不使用到大气中的硫,每年达到25万吨。
-
These results demonstrated that the sectional structure of the nozzle's orifice would not significantly affect the morphology and the size of the generated microspheres at least for the present system. RESS was also performed by nozzle B at the extraction temperature and pressure of 388K and 30.0MPa and pre-expansion temperature of 453K, and agglomerated microspheres with mean diameter of 0.8μm were obtained.
以α-Al〓O〓微滤膜为基膜的SCSI过程实验结果定性地验证了上述数学模型的可靠性,经过SCSI、水解及烧结过程后,陶瓷膜的孔径改变情况由气体渗透和泡压法表征,结果表明当膜面性质有利于均相成核时,陶瓷膜流动平均孔径减小;相反平均孔径增大,这与过程模拟结果是一致的。
-
During filtration,some parameters such as pressure drop over filter and the flux of liquid nitrogen were tested.
同时应用基于达西定律的烧结金属过滤器的压降计算模型,对实验工况的过滤器的压降进行预测。
-
Wheat straw, thermosetting resin, alcohol ,etc, were selected as raw materials and Zncl2, K2CO3,(NH4)2HPO4 and Na2B4O7·10H2O as additives. All these components were mixed uniformly according to the proportion and hot-pressed to sample with the dimension. The samples were put into the vacuum furnace and sintered in the atmosphere of nitrogen ,and the termination temperature was 300℃, 400℃, 500℃, 600℃, 700℃ and 800℃, respectively, and woodceramics were prepared and the effects of the additive on the ratio of remaining carbon were investigated.
试验选取了麦秸、热固型酚醛树脂、酒精等为原料,氯化锌、碳酸钾、磷酸氢二氨以及硼砂等为阻燃剂,按照一定的比例混合均匀并热压成一定尺寸的坯体,再将坯体在氮气保护下按两种升温模式分别烧结至300℃、400℃、500℃、600℃、700℃和800℃,制备出各温度点下的木质陶瓷,观察分析了阻燃剂对其残碳率的影响。
- 推荐网络例句
-
It has been put forward that there exists single Ball point and double Ball points on the symmetrical connecting-rod curves of equilateral mechanisms.
从鲍尔点的形成原理出发,分析对称连杆曲线上鲍尔点的产生条件,提出等边机构的对称连杆曲线上有单鲍尔点和双鲍尔点。
-
The factory affiliated to the Group primarily manufactures multiple-purpose pincers, baking kits, knives, scissors, kitchenware, gardening tools and beauty care kits as well as other hardware tools, the annual production value of which reaches US$ 30 million dollars.
集团所属工厂主要生产多用钳、烤具、刀具、剪刀、厨具、花园工具、美容套等五金产品,年生产总值3000万美元,产品价廉物美、选料上乘、质量保证,深受国内外客户的青睐
-
The eˉtiology of hemospermia is complicate,but almost of hemospermia are benign.
血精的原因很,以良性病变为主。