However,the previous studies mainly focused on the superconductive properties of SiC-doped MgB2 and rarely explored its sintering process.

本文结合差热分析和物相鉴定，系统研究了SiC掺杂MgB2体系的烧结过程，并在此基础上探究了其反应动力学机理。

The density, electrical contact resistance and hardness of these two alloys were tested. The results show that Ag and rare earth oxide appear in Ag-Y and Ag-Ce alloy after internal oxidation. The distribution of oxide particles is inhomogeneous and seriously conglomerated in Ag-Y2O3 and Ag-CeO2 sintered bulk, but they are dispersed and uniform in Ag matrix after severe plastic deformation. The relative densities of wire materials are larger than 99% and the electrical contact resistances are low (＜2.2 μΩcm).

结果表明：Ag-Y和Ag-Ce合金粉末经内氧化处理后生成Ag和稀土氧化物2种物相；Ag-Y2O3和Ag-CeO2材料烧结坯中氧化物颗粒分布不均匀且团聚严重，但材料经过大变形加工后，氧化物颗粒细小，均匀地弥散分布在银基体上；最终产品丝材的相对密度均达到99%以上，电阻率较低(＜2.2 μΩcm)。

The phase assemblages and the reasons induced the changes in mechanical properties of the sintered samples with addtion of SiB6 are also discussed.

文中还对烧结样品的物相和影响力学性能的原因进行了讨论。

High-Al cement or calcium aluminate cement, soft clay, kyanite, Al2O3 and/or SiO2 powder, and naphthalenesulfonic acid-formaldehyde condensate.

铝硅质原料是焦宝石、莫来石或高铝矾土中的一种或几种以上，其中Al 2 O 3 ≥45％；结合剂为高铝水泥或纯铝酸钙水泥；高铝水泥占喷补料总量不少于5％，其中Al 2 O 3 ≥46％，CaO≤40％；纯铝酸钙水泥中Al 2 O 3 ≥69％，CaO≤25％；烧结剂和可塑剂为软质粘土，膨胀剂为蓝晶石；外加剂为萘磺酸甲醛缩合物。

The effects of composition and sintering temperature on the phase assembly and bulk density of the samples were studied.

研究了组成、烧结温度对试样物相和密度的影响。

The CMOR,HMOR,oxidation resistance,thermal shock resistance and corrosion resistance of the Si3N4-SiC composite fired in oxidating atmosphere were investigated; the phase composition and microstructure of the composite were also studied by XRD and SEM.

对氧化气氛下烧结的Si3N4-SiC复合材料进行了常温强度、抗氧化性能、抗热震性能、抗侵蚀性能的研究，并利用XRD 和SEM对试样进行了物相和显微结构分析。

The lead-less piezoelectric ceramic composition is prepared through sintering at relatively low temperature, say, 1190 deg.c or even lower, and has good piezoelectric characteristic, practical plane electromechanical coupling coefficient kp, high Curie point and no lead and lead compound contained.

本发明的制备工艺能在较低温度下，如1190℃或更低温度下烧结无铅压电陶瓷组合物，使制备的无铅压电陶瓷具有好的压电性、可实用的平面机电耦合系数kp和高的居里温度，制备工艺过程中不含铅或铅的化合物。

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面，更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值，分为几个相等的区间作为横轴，并将各区间内所测定值依所出现的次数累积而成的面积，用柱子排起来的图形，也叫做柱状图。