ZnO polycrystalline films, with a preferred orientation in c-axis, were grown by RF magnetron sputtering at reran temperature on quartz substrate.

用射频磁控溅射方法在未进行人为加热的石英玻璃衬底上，生长了良好c轴择优取向的ZnO多晶薄膜。

In our experiments, the hafnium films were deposited on molybdenum substrates by radio frequency magnetron sputtering technology, and the barium oxide layers were prepared by the chemical method to simulate the grid structure of traveling wave tubes. Then, the surface phase and compositional change in the grid was studied under high temperature by annealing from 900K to BOOK, which can be used in explaining the suppression mechanism of hafnium film.

实验中，利用射频磁控溅射技术在Mo基底上制备了Hf膜，并利用化学方法制备了BaO涂层以模拟行波管栅极结构，随后在N_2保护下，通过在900K到1300K范围内退火，研究栅极处于高温工作环境下表面相结构和成分的变化，以此解释了Hf薄膜抑制栅极电子发射的工作机理。

Cerium dioxide thin films were deposited on glass substrates using R. F. magnetron sputtering.

本文采用射频磁控溅射法在玻璃基片上沉积CeO2薄膜。

Chromium oxide thin films were deposited on 45 steel substrate by reactive magnetron sputtering.

利用射频反应磁控溅射法在45钢基体上制备了氧化铬薄膜。

In this paper, SiO2 coating was prepared on sapphire s

本文采用射频磁控反应溅射法在蓝宝石衬底上制备了SiO2涂层。

Columnar structure, which is observed in the films deposited by conventional magnetron sputtering, disappears in the film synthesized at ICP power of 200 W and substrate temperature of 300℃.

利用感应耦合等离子体增强射频磁控溅射技术在Si(111)片和M2钢表面制备了ZrN薄膜，研究了基片的温度和ICP功率对ZrN薄膜的结构以及性能影响。

In sputtered Ni/Al and Ni/Cr multilayers,X-ray diffractionindicatesan expansion of the Ni lattices along the growth direction, which results instress in the multilayers.

在溅射制备的一系列Ni/Al和Ni/Cr多层膜中，X-射线衍射表明Ni层晶格在沿其膜面发向上与体材料相比存在轻微的膨胀，这导致了在沿其膜面发向上存在张应力。

In this thesis, we concentrate on the development in theoretical prediction and experimental synthesis of CN compounds in the recent 10 years. By means of ion beam sputtering, treating melamine at high temperature and pressure, pyrolyzing melamine and treating pyrolysis products of melamine by impulsive discharge and high-speed impact, we explore the routes to synthesize carbon nitrides. The chemical compositions, crystal structures and bonding states of the CN films and powders obtained from the experiment are studied by the use of EDX, XRD, TEM, XPS and FTIR.

本文概述了十年来碳氮化合物在理论预测和实验研究方面的进展；采用离子束溅射、三聚氰胺高温高压和三聚氰胺热解以及产物的脉冲放电和高速冲击加脉冲放电处理等三种方法，探索了碳氮化合物的合成途径；借助X射线能谱、X射线衍射、透射电镜、X射线光电子谱和红外光谱等手段，对所获得的碳氮薄膜和碳氮粉末进行了成分、晶体结构、价键结构等性质的分析。

The Al2O3 thin films are grown on silicon substrates by radio frequency mag时tron sputtering and are annealed in the nitrogen gru弓at different temperatures.

本文采用射频磁控溅射技术在单晶硅衬底上制备了Al2O3 薄膜，并在氮气中进行了不同温度的退火，对比了退火前后薄膜的结构和光致发光特性。

A series of ZnO thin films were deposited on silicon (100) substrate by facing target radio frequency magnetron sputtering system, and were annealed and supersonically treated.

利用对向靶射频磁控溅射系统在Si(100)衬底上制备了ZnO薄膜，并对其进行了退火和超声处理。

Finally, according to market conditions and market products this article paper analyzes the trends in the development of camera technology, and designs a color night vision camera.

最后根据市场情况和市面上产品的情况分析了摄像机技术的发展趋势，并设计了一款彩色夜视摄像机。

Only person height weeds and the fierce looks stone idles were there.

只有半人深的荒草和龇牙咧嘴的神像。