涂层

By synthesizing three amine types inhibitor,we separately put them into top coat and ground coatings measuring with Electrochemical Impedance test and Salt fog test,the conclusion:corrosion inhibiting coal tar-epoxy coatings have more corrosion resistance than coal tar-epoxy coatings.

在环氧煤沥青的底漆和面漆中分别加入自行合成的胺类缓蚀剂R、Y和Z后，采用交流阻抗和盐雾实验等方法测试，结果表明，涂层的耐蚀性能有较大提高，涂层针孔电阻Rfp的值阻提高 2～ 3个数量级，并且涂层的物机性能不受影

However, in the temperature range of 1150-1300℃, the surface morphology of SiC coatings changes to rounded hillocks and the as-deposited coatings are very rough.

沉积温度和SiC涂层表面形貌的关系如下： 950℃时，沉积的SiC颗粒非常细小，为独立的球形堆积； 1000～1100℃时， CVD SiC涂层表面光滑、致密； 1150～1300℃沉积的SiC涂层呈现出球状或瘤状结构且表面粗糙。

The result shows the tribology properties are good, the kinetic friction coefficient are under 0.1. In the same conditions of wearing test, the weight loss of surface treated with EDC is about one tenth of the weight loss without treatment, and is about one sixth of the weight loss treated with electroless composite coating.

结果表明：在本试验的条件下，涂层的滑动摩擦系数较小，均在0.1以下，说明涂层的摩擦学性能较好；在相同的磨损实验条件下，用液中放电沉积方法处理过的表面磨损失重量是未处理表面的1/10左右，是化学复合镀方法处理表面的1/6左右，说明涂层的耐磨性相对较好。

In order to reach the purpose of using pre-laser cladding method preparation of Ni-based amorphous alloy coatings on 45 steel substrate surface by the method was carried out. The principles of the three clusters and the amorphous line of the law of composition rules were used. The Ni59.35Nb34.45Sn6.2 alloying powder which has a great glass-forming ability in conventional preparation methods of amorphous alloys was chosen. In the protection of atmosphere, the amorphous surface coating was prepared. The microstructure, micro-hardness and performance of the different output power of the laser cladding were analyzed.

中文摘要：为了达到研究预置激光熔覆可以在45钢上制备Ni基非晶合金涂层的目的，采用非晶形成能力三判据原则及非晶成分团簇线定律法则，选择了采用常规非晶合金制备方法中具有极大玻璃形成能力的Ni59.35Nb34.45Sn6.2合金粉末，在保护气氛下，制备非晶涂层，并对不同输出功率下得到的涂层进行微观组织和结构表征及性能测试。

The thin and low-resistance conductive coating which less than 3μm and 10Ω/□was obtained through two mild post-treatments, water immersion and low-temperature sintering (150℃).

通过水浸泡与低温烧结(150℃)对导电涂层进行后处理，均能得到涂层厚度小于3μm，表面电阻小于10Ω/□的低电阻薄导电涂层。

This paper reviews characteristics of nonskid coatings for aircraft carrier deck s, focuses on the application situations, existing problems and development directions of resin matrix nonskid coatings and metal, matrix nonskid coatings for aircraft carrier deck s.

综述了国外舰载飞机甲板用防滑涂层的特点，着重介绍了树脂基防滑涂层和金属基防滑涂层在国外舰载飞机甲板上的应用情况、存在的问题以及未来的发展方

The microstructure of the coating and the mechanism of the wear resistance were analyzed. Compared with the coating using oxyacetylene flame process, results showed that the wear resistance of coating prepared by plasma spray welding process is higher than that of the coating using oxyacetylene flame process.

进而对涂层的微观组织和耐磨机理进行了分析和研究，并且与氧乙炔火焰喷焊技术所制备的涂层进行了对比测试分析，结果表明，利用等离子喷焊技术所制备的超厚涂层耐磨性能更为出色。

The present invention adopts polyvinyl perchloride and organosilicon modified acrylic resin as main filming material and adds cyanuramide phosphate and expanding graphite into common polytriammonium phasphate as fireproof assistant to constitute foaming material. The present invention has greatly raised foaming rate and the foamed layer has thickness of 30-50 times the original coating thickness and fireproof limit up to 90 min.

本发明采用高氯化聚乙烯和自行合成的有机硅改性丙烯酸酯树脂为主要成膜物质，并在通常所用的聚磷酸铵类防火助剂的基础上，加入三聚氰胺磷酸盐和可发性膨胀石墨作为发泡材料组成，大大提高了涂层的发泡率，发泡层厚度可达原涂层厚的30～50倍，耐火极限可达90min(涂层厚度2mm)。

The main products are: Hammer, thermal conductivity detector, permeameter, contraction of the expansion device, hand-held strain gauge, waterproof material detector, low-bending device, slag ball content in separators, heat load tester, performance test combustion furnace, a variety of thickness, thermal expansion of graphite electrode NG, coal strength meter, electric tamping device, hydrophobicity tester, mineral wool density meter, concrete drilling sampling machines, sawing machines, removed machine, setstube machine, hydraulic bending machine, impervious tester, determination of heat resistance, heating telescopic measuring device, an extension device, penetration tester, small meter, viscometer, drying time tester, pencil hardness tester, pendulum hardness, the adhesion tester, film zoned grid, and resistant to scrubbing detector, solvent resistance detector, wearable device, flat grinding device, wear-resistant coating shakeout device, staining resistance tester, impact tester , piercing instrument, instrument bending film, film coating, and sanding machines, cone-shaped grinding, high-speed dispersion machine, three roller grinder, Scratch tester, indentation tester, gloss Miriam, white tester, fresh video of Miriam, Miriam reflectivity, iron cobalt colorimeter, paint density cup, crack resistance testing apparatus, leveling device, flow hanging device, visual color box, the minimum temperature detector into a grinding, low temperature brittleness tester, visual color boxes, electronic pull machine, Mooney Viscometer, vulcanizing device, the proportion of direct-reading, the cold compression tester, heritage wearable device, Heritage scratch device, the friction coefficient detector, coating Detect zoned grid plate , coating resistance tester, such as burning a variety of test equipment.

主要产品有：回弹仪、导热系数测定仪、渗透仪、收缩膨胀仪、手持应变仪、防水材料检测仪、低温弯折仪、渣球含量分离器、热荷重试验仪、燃烧性能试验炉、各种测厚仪、石墨电极热膨胀仪、煤强度测定仪、电动击实仪、憎水性测试仪、矿棉容重测定仪、混凝土钻孔取样机、锯切机、磨平机、套丝切管机、液压弯管机、不透水试验仪、耐热性测定具、加热伸缩测定器、延伸仪、针入度仪、细度计、粘度计、干燥时间试验器、铅笔硬度计、摆式硬度计、附着力测试仪、漆膜划格器、耐洗刷测定仪、耐溶剂测定仪、耐磨仪、平磨仪、涂层落砂耐磨仪、耐沾污测试仪、冲击试验仪、穿孔仪、漆膜弯曲仪、涂膜涂布器、砂磨机、锥形磨、高速分散机、三滚研磨机、划痕试验仪、压痕试验仪、光泽仪、白度仪、鲜映性仪、反射率仪、铁钴比色计、涂料密度杯、抗裂性试验仪、流平仪、流挂仪、目视比色箱、最低成磨温度测定仪、低温脆性试验仪、目视比色箱、电子拉力机、门尼粘度仪、硫化仪、直读比重计、压缩耐寒试验仪、文物耐磨仪、文物划痕仪、摩擦系数测定仪、涂层检测划格板、涂层耐燃烧试验仪等多种试验仪器。

The smooth surface of nano-HA prothesis fails to take advantage of the benefit of nano-HA.

光滑表面的纳米羟基磷灰石假体未能发挥纳米级羟基磷灰石的优势；在影响骨整合方面就羟基磷灰石涂层来说，涂层表面改性可能比单纯涂层材料纳米化更重要。

The labia have now been sutured together almost completely.The drains and the Foley catheter come out at the top.

此刻阴唇已经几乎完全的缝在一起了，排除多余淤血体液的管子和Foley导管从顶端冒出来。

To get the business done, I suggest we split the difference in price.

为了做成这笔生意，我建议我们在价格上大家各让一半。