水玻璃涂料

The acorreding mathod is presented to solute the defficulty of the directly transfering coating technique under self-hardening conditions,and the process obtains the propose of short time,low cost,smooth surfaces and accurate sizes.

采用CO2水玻璃硬化背砂的铸造工艺及在自硬条件下涂料直接转移技术的工艺难点。

Using sodium silicate solution as the binder of zinc-rich coating ,zinc powder as the filler,distilled water as the solvent,and adding thicker,solidifier,sodium silicate inorganic zinc-rich coating s were prepared.

以硅酸钠溶液为成膜基料，锌粉为颜填料，去离子水为溶剂，加入增稠剂，固化剂等助剂，制备钠水玻璃富锌涂料；应用红外光谱分析、流变学测量和耐液性观察，研究钠水玻璃富锌涂料的固化机理。

Composite and technology of preparing, brushing, stoving of the coatings was determinedby the experiment, composite and technology of preparing, moulding, curing of sodium silicate bonded sand cured by organic ester was also determined too,then the foundry technology test of sleeve made from high chromium cast iron was done.

通过实验确定了实型铸造水基棕刚玉涂料的组成、配制、涂刷和烘干工艺；确定了有机酯硬化水玻璃砂的配比及混制、造型和硬化工艺，并进行了高铬铸铁套筒浇注试验。

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面，更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值，分为几个相等的区间作为横轴，并将各区间内所测定值依所出现的次数累积而成的面积，用柱子排起来的图形，也叫做柱状图。