A series of polyimide/SiO2-TiO2 hybrid films with different contents and weight ratio of inorganic particle were fabricated using tetraethoxyl silicane and tetrabutyl titanate as precursor by situ method .

以正硅酸乙酯和钛酸四丁酯为前驱体,采用两相原位同步法制备一系列不同含量及重量比的聚酰亚胺/SiO2-TiO2杂化薄膜,利用红外光谱、扫描电镜和XRD观察了薄膜的化学结构和微观结构,并测试了薄膜的热稳定性。

A clean production technology of sodium sulfoxylate formaldehyde by one-step process with sodium pyrosulfite ,zinc powder and formaldehyde as raw materials was studied in detail.

详细研究了以焦亚硫酸钠、锌粉和甲醛为原料,一步法合成甲醛合次硫酸氢钠的清洁生产工艺,其最佳操作条件为:焦亚硫酸钠与锌粉物质的量比约1∶2.5,焦亚硫酸钠与甲醛物质的量比约1∶2.1,亚硫酸氢钠溶液的pH 3.3~3.6,活化温度≤45℃,最高温度97~102℃,高温反应时间

Phenolic resin/montmorillonite hybrid resin were prepared by Zn_2 catalyst and cured by p-toluene sulphonic acid through one step process in this paper.

在醋酸锌催化剂作用下,采用边缩聚边插层的一步法制备了酚醛树脂/蒙脱土杂化树脂,并采用对甲苯磺酸为室温固化剂制得酚醛树脂/蒙脱土复合材料。

PI-1 and PI-2 polyimide films were prepared from 3,3′,4,4′-benzophenone tetracarboxylic dianhydride and ODA确良by two-step polymerization under the thermal and mixed imidization procedures.

采用两步法首先合成聚酰胺酸,然后经热酰亚胺化和混合酰亚胺化工艺制备了BTDA/ODA型的PI-1 和PI-2两种聚酰亚胺薄膜。

Synthesis and Characterization of MWNT-containing Polyurethane-urea Based on the typical two-step polyurethane-urea synthesis, self-crosslinkable polyurethane-urea compounded of PTMO Poly (tetramethylene oxide, MDI (4,4'-diphenylmethane diisocyanate) and extended by AEAPS (aminoethyl aminopropyl trimethoxysilane) were prepared.

含有纳米碳管的聚氨酷的合成、表征及性质研究首先通过典型的两步法合成了软段为pTMOPoly(tetramethyrene oxide,叠年东师范大李博士后么站银告硬段为MD!(4,4'一diPhenylmethane diisocyanate),扩链剂为AEAPS (aminoethylaminoProPyltrimethoxysilane)的聚氨醋。

Glycerol polyether 3010, tolylene diisocyanate , 1,4-butanediol and catalysts are used as raw materials to preparecasting polyurethane elastomer in one step.

以聚醚多元醇3010,甲苯二异氰酸酯,1,4-丁二醇和催化剂为原料,采用一步法来制备浇注型聚氨酯弹性体。

Application of PTCD with pigtail-shape transfixion pin in one step for interventional therapy of liver and kidney cyst LUO Chuan-bin,OU Guang-qian.

5 cm肝肾囊肿用猪尾型穿刺针一步法PTCD治疗肝肾囊肿治疗方法简便实用、安全,治愈率和有效率明显提高。

The dehydrating agent and the dehydrating condition on removal of trace water in the synthetic solution of triethyl orthoformate were investigated.

研究了原甲酸三乙酯一步法合成反应中脱除微量水分的脱水剂和脱水条件,通过正交实验确定了脱水的最优化工艺条件。

Flame—retardant resin was prepared by the condensation and polymerization of phosphoric acid, trihydroxy methyl propane and epoxy chloropropane,the resin was then reacted with hexane diacid and diglycol under certain condition ,resulting in polyol containing 1.5% P and 17— 18% polyester polyol, which was foamed with polyisocyanate, water and catalyst by one— step method, producing fire...

通过磷酸、三羟甲基丙烷和环氧氯丙烷的缩合和聚合反应制得阻燃树脂,然后将它与己二酸、一缩二乙二醇在一定条件下反应制得含P1.5%和含Cl17~18%的聚酯多元醇,再将它与多异氰酸酯、水、催化剂等组分采用一步法发泡工艺制得阻燃聚氨酯软泡塑料。

Flame— retardant resin was prepared by the condensation and polymerization of phosphoric acid, trihydroxy methyl propane and epoxy chloropropane,the resin was then reacted with hexane diacid and diglycol under certain condition ,resulting in polyol containing 1.5% P and 17— 18% polyester polyol, which was foamed with polyisocyanate, water and catalyst by one— step method, producing fire—resistant PU soft foam.

通过磷酸、三羟甲基丙烷和环氧氯丙烷的缩合和聚合反应制得阻燃树脂,然后将它与己二酸、一缩二乙二醇在一定条件下反应制得含P1.5%和含Cl17~18%的聚酯多元醇,再将它与多异氰酸酯、水、催化剂等组分采用一步法发泡工艺制得阻燃聚氨酯软泡塑料。

第29/40页 首页 < ... 25 26 27 28 29 30 31 32 33 ... > 尾页
推荐网络例句

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面,更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值,分为几个相等的区间作为横轴,并将各区间内所测定值依所出现的次数累积而成的面积,用柱子排起来的图形,也叫做柱状图。

You rap, you know we are not so good at rapping, huh?

你唱吧,你也知道我们并不那么擅长说唱,对吧?