Ti-Si composite materials are mixed at atomic scale, and Ti-O-Si bond appears in all of the samples with different TiO2 content; the mixed oxides are mainly existed in the form of amorphous pattern, anatase appears when the TiO2 content is more than 80%, but compared with the intension of pure TiO2, it has not integrate structure. The acetic content has great influence in the specific area and crystal structure of the mixed oxides. 20TiSi has good heat stability, still possesses 11m2/g after calcined at 1100℃; calcinations on the large scale of temperature does not cause the break of Ti-O-Si bond, TiO2 is well dispersed in 20TiSi calcined at 1100℃, and it still existed in the form of amorphous.

结果表明：制得的Ti-Si复合氧化物具有很高的比表面积，在TiO_2含量为10％时达到681.5m~2／g，Ti原子进入Si-O四面体结构中，形成Si-O-Ti键，复合氧化物的稳定性好，当TiO_2含量低于60 wt％时，以无定型形式存在；当含量为80％时，出现锐钛矿型TiO_2，但与纯TiO_2相比晶型不完整：醋酸对Ti-Si复合氧化物的比表面积、晶型都有很大的影响；TiO_2含量为20％的20TiSi经1100℃高温焙烧后，仍有较高的比表面积(11m~2／g)，稳定性好，在较宽的温度范围内焙烧，没有引起Ti-O-Si键的断裂，分散度高，没有出现晶型TiO_2。

The study of the geological characteristics, ore-forming condition and genetic type from the Pingdingshan gold deposit, shows that the cryptomerous diorite and dioritic porphyrite in different stages formed a vein rock zone with gold containing ore bodies in the area, and five vein ore bodies were blocked out by spreading out with the NNE direction in the field.

黑龙江嘉荫平顶山岩金矿床的地质特征、形成条件和成因类型的研究表明：矿区内不同阶段的细晶闪长岩、闪长玢岩形成一个含金矿体的脉岩带；矿床范围内圈定5条呈脉状沿北北东向展布的矿体；矿石类型为石英脉型和蚀变岩型；金以裂隙金、晶隙金和明金为主，以银金矿的形式存在，且主要与石英、黄铁矿、毒砂和水云母共生；成矿作用分为热液期及表生期，其中热液期又分为4个成矿阶段，即纯石英阶段，黄铁矿毒砂石英阶段，黄铁矿毒砂水云母石英阶段和石英碳酸盐阶段。

According to the physical aging behavior of rapidly quenched atactic polystyrene , it was found that dual amorphous phases with quite different properties were formed due to the internal stress: free amorphous phase and constrained amorphous phase.

通过研究快速淬冷无规聚苯乙烯的物理老化行为发现，在此试样中由于内应力的存在而形成了两种性质大为不同的非晶区：自由非晶区和受限非晶区。

The results show that as for the as-cast castings, eutectic Si particles are characterized as fibrous or long acicular shape as well as in homogenous distribution, and the impact absorbed energy varies from 1.17 to 2.35J. After T6 heat treatment, the eutectic Si particles become small granular or short bacilliform, and the aspect ratio and area fraction of Si particles decrease evidently. The energy of the T6-treated castings is 1.45-3.80 J, which is higher than that of the as-cast castings. Furthermore, the fracture mechanisms of different regions in the castings were analyzed and discussed.

结果表明：铸态下共晶Si粒子大多为纤维状或长针状，呈不均匀的网状分布，冲击吸收功在1.17~2.35J的范围内变化后；经T6热处理后，团簇状Al-Si共品相明显减少，共晶Si粒子呈现出粒状或短棒状，且细小均匀，Si粒子的长宽比和面积分数都有显著降低，冲击吸收功在1.45~3.80J的范围内变化，比铸态有明显提高。

Tight alloying layer with undulation and without visual pocket and inclusion has been obtained by experiment.The alloying layer is metallurgically combined with the matrix.

试验结果获得了致密、无肉眼可见气孔、夹杂、熔覆表面有一定起伏的合金层，合金层与基体间完全冶金结合；熔覆合金层由单相Fe3 Al构成，覆层组织为粗大的柱状晶团，柱状晶团内包含大量极细小的板条状Fe3 Al晶粒，一些相邻的板条晶之间具有基本相同的晶体学取向。

The results of XRD indicated that the addition of lanthanum in skutterudite could enhance the formation of skutterudite during the synthesis process. The content of skutterudite increases with the increase of the filling fraction in 〓. The lattice parameter of filled skutterudite increases with the increase of lanthanum filling fraction. It is caused by the deformation of Sb〓 ring arising from the "rattling"of the filling atoms in the voids in skutterudite.

对不同填充率方钴矿La〓Fe〓CoSb〓材料的XRD研究发现，镧元素的引入可以促进方钴矿相的合成，相同条件下合成的方钴矿的纯度随镧填充率的增大而提高，材料的晶胞参数随镧填充率的提高而增大，这是填充原子在方钴矿晶体的的孔隙内震颤和晶胞内Sb〓四边形发生扭曲变形所致。

The results of Raman, SEM and EPMA tests show that the microstructure defects of the chalcogenide glasses play an important part in their second-order nonlinear optical properties. The glasses show large SNOP because of Sb2S3 microcrystal or the mental antimony in the glasses even before they were polarized. After the electrical/thermal polarized, GeSbS glasses show larger SNOP with the increase and growth of the microcrystal. The glasses show larger SNOP because of the existence of Sb2S3 microcrystal or the mental antimony in the glasses.

通过研究玻璃的拉曼光谱、扫描电镜和电子探针显微分析后发现，硫系玻璃内部的微结构缺陷对其二阶非线性光学性能有显著影响，玻璃体系内存在的Sb2S3微晶或金属锑颗粒能使硫系玻璃在未经极化处理前就具有较大的二阶非线性光学性能；经电场温度场极化处理后，随着微晶的增多和进一步长大，导致GeSbS玻璃具有更高的非线性光学性能；由于Sb2S3微晶或金属锑的存在，导致玻璃具有较高的二阶非线性光学性能。

The results showed the addition of PPS did not decrease the thermal performance but decreases the heat deformation temperature of PPES/PPS blends. The crystallinity of PPS was hindered with the increasing of PPES contents, the crystal lattice flaws of PPS occurred and the perfect spherocrystal could not appear when the mass fraction of PPES was 80%. The annealing process was favorable to the increase of the heat deformation temperature and the formation of perfect spherocrystal of PPS.

热失重研究表明，在所组成范围内PPS的加入并未降低共混物的热性能，但使共混物的热变形温度有所降低；PPES的加入使PPS的结晶受到阻碍，当PPES质量分数达80%时，PPS产生了晶格缺陷，从而不能形成完善的球晶，退火过程有利於提高共混物的热变形温度，使PPS形成更完善的球晶。

BACKGROUND: Conventional concept suggests that infused crystalloid fluid is first distributed in the plasma volume and then, since the capillary permeability for fluid is very high, almost instantly equilibrates with the extracellular fluid space.

背景：一般我们认为输入晶体液在血容量中是一室分布的但因为的毛细血管通透对晶体液是很高的，所以晶体液在血管内与细胞外间隙立刻就会达到平衡。

SiC polytypes of 6H and 15R and a transition zone between the two were observed under HREM and TEM and discussed from the point view of the crystal structures; the clear evidence of Al〓C〓 nucleated in the SiC particle was provided, indicating the aluminum penetrating the SiC grains is already carbon-saturated and, consequently, Al〓C〓 crystals grow in the particles wherever a temporary local supersaturating is produced; The experimental observation indicated that the types of the interface between SiC and Al are variable and the distribution feature of reaction product, Al〓C〓, were also given in the present work: to be nucleated on SiC, to be aggregated at SiC/Al interface zone or to be aggregated at the crystal boundaries.

通过高分辨透射电镜，本文观察到SiC增强体中6H和15R同质多晶现象及6H-15R SiC转变区，以及另外一种无序的SiC同质多晶，并从其晶体结构的角度解释了6H和15R在晶体内共存的现象。通过高分辨透射电镜，本文给出了Al〓C〓在SiC颗粒内部形核的明证，表明Al〓C〓形核是Al渗透到SiC颗粒内部在C过饱和处在SiC的（0006）面上而形核，而且一种可能的位相关系为A1〓C〓[11〓0]∥SiC[11〓0]。研究结果同时给出了SiC/Al复合材料的界面反应产物A1〓C〓的分布特征：在SiC上形核并生长，聚集于SiC/Al界面去附近，或者聚集于晶界上。