Results indicate that when the strain rate is 1200 s-1, the twin number of samples in different orientation increases with plastic strain increasing; when the strain rate increases to 2800 s-1, the σ-ε curves have no obvious charges as the angle is 0o and 45o, compared with that at 1200 s-1; however the σ-ε curves vary from concave to convex when the angle is 90o, because thermal softening has occurred with increasing plastic strain, which results in the number of twin decreasing, and smaller strain hardening

结果表明：当加载应变率为1200 s-1时，不同取样方向的样品中孪晶数量均随塑性变形应变量的增大而增多；当加载应变率增大到为2800 s-1时，取样方向为0°和45°、流变曲线形状较应变率为1200 s-1时没有明显变化，而取样方向为90°时曲线形状由应变率为1200 s-1时的凹形变为凸形，曲线形状变化的原因是由于应变量增大，热软化效应使得孪

By means of the complex variable function method and introducing the conformal transformation,the anti-plane shear problem about two semi-infinite collinear cracks in one-dimensional hexagonal quasicrystals was investigated and the exact solution to mode Ⅲ SIFs was found out.

利用复变方法，通过引入适当的保角映射，研究了一维六方准晶狭长体中双半无限共线裂纹的反平面剪切问题，给出了Ⅲ型裂纹问题的应力强度因子的精确解。

The effects of thepreparation conditions on the structures and performances of the sol samples were studied,followed by investigating the formation mechanism of the anatase TiO_2 particles. Thecharacterization of the as-obtained sol-gel samples shows that the TiO_2 and P-doped TiO_2sols have anatase crystal structures, and the latter has higher crystallizability than theformer.

通过对TiO_2溶胶进行微观结构表征，发现：TiO_2溶胶和掺磷TiO_2溶胶均呈锐钛矿晶型，颗粒呈梭形，分散性较好，后者的结晶度更高；两者在可见光区均有较大的光吸收，最大吸收波长为550nm，磷的加入使得TiO_2的禁带宽度变大。

Based on the average lattice and average atom models, effects of interstitial impurities on the valence electron structures and phase transformation of Ti-Al alloys are analyzed, and the degree of descension of bond energy, melting point and liquidus temperatures as affected by interstitial impurities are calculated by the bond energy formula of the EET.

应用固体与分子经验电子理论的平均晶胞和平均原子模型分析计算了间隙杂质对Ti-Al合金价电子结构和相变的影响。同时根据该理论的键能公式计算了间隙杂质影响下的键能、熔点和液相线的变化。

By use of time-varying Fourier coefficient series of power system variables, new dynamic phasor models of thyristor-controlled reactor are developed. In this model the higher order harmonic components that have less impacts on dynamic characteristic of TCR are neglected, and through the average operation of time-domain model of TCR, a dynamic phasor state-space model of TCR is derived.

利用电力系统变量的时变傅里叶系数得到晶闸管控制电抗器(thyristor controlled reactor，TCR)的动态相量模型，该模型忽略了对TCR动态特性影响较小的谐波分量，并通过对TCR时域模型的平均运算获得动态相量状态空间模型。

Finally roud and flat elliptic cross-section samples with uniform shape, smooth surface and unidirectional crystals have been successfully obtained.

最终在等截面送料、变截面送料的条件下分别抽拉出了成形良好，表面光洁，具有单向柱状晶组织的圆形截面、扁椭圆形截面的样件。

The result shows that B combines with N prior to Al at high temperature and brings about coarse particles of BN (about 900 nm), which effectively reduces the amount of fine and dispersive AlN particles, and BN precipitate clinging to MnS precipitation coarsens MnS particles, the pinning of austenite grain boundary is alleviated and the grain growth of ferrite is suppressed.

结果表明高温时B优先于Al与N结合生成粗大的BN粒子(约900 nm)，有效降低了热轧过程细小而弥散的AlN析出量，同时BN依附MnS析出而粗化MnS粒子，减弱了细小弥散析出粒子对奥氏体晶界钉扎以及相变后铁素体晶粒长大的抑制作用。

The lower energy is because that the chemical bond between O〓 and M〓 has not formed completely, which cause by the higher covalency of Eu〓-O〓 bond in amorphous state. And the larger half width is caused by the disorder of sites.

这是由于在非晶态状态下金属氧键尚未完全形成，从而导致Eu〓-O〓的共价性较高，因此电荷迁移带处于较低的能量位置；而格位的无序性导致其光谱变宽。

Products involving rough, drawing, extubation reduced strokes, straight rod, special-shaped, natural diamond, polycrystalline mode, as well as bicycles, sewing machines dedicated mold standard parts, odd-shaped molds for various species, is strong in technology have advanced equipment to improve its service life detection is 30 times more than high-speed steel, non-disposable, can be used many times to repair, rehabilitate unchanged after life.

产品涉及毛坯、拉丝、拔管缩杆、直杆、异形、天然钻石、聚晶模以及自行车、缝纫机标准件的专用模具、奇形模等多样品种，力量雄厚工艺设备先进，检测完善它的使用寿命是高速钢的30多倍，非一次性，可多次修复使用，修复后寿命不变。

Products involving rough, drawing, extubation reduced strokes, straight rod, shaped, natural diamond, polycrystalline modulus as well as bicycles, sewing machines dedicated mold standard parts, odd-shaped molds for diverse species, is strong in technology have advanced equipment to improve its service life Detected are 30 times more than high-speed steel, non-disposable, can be used many times to repair, after repair the same life expectancy.

产品涉及毛坯、拉丝、拔管缩杆、直杆、异形、天然钻石、聚晶模以及自行车、缝纫机标准件的专用模具、奇形模等多样品种，力量雄厚工艺设备先进，检测完善它的使用寿命是高速钢的30多倍，非一次性，可多次修复使用，修复后寿命不变。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。