Injection molding feed of Fe-Ni-Cu-C alloy coarse powder with particle size of 60um was prepared, effect of rate of shear, temperature and proportion of powder and binder to rheological behavior of feed was studied, viscosity number of three kinds of feed in different temperature was measured by capillary viscosimeter strain sensitivity factor three kinds of feed with different component were compared.

制备了平均粒度为60m的Fe-Ni-Cu-C合金粗粉汁射成形喂料，研究了剪切速率、温度、粉末和粘结剂比例对喂料流变行为的影响，应用毛细管粘度计测量了三种喂料在不同温度下的粘度值，比较了三种不同成分喂料的应变敏感性因子的大小。

The monotonic and cyclic shear tests of the interface between geotextile and gravel as well as geotextile drawing tests were conducted with the apparatus. The interface was found to exhibit strain-softening and obvious aeolotropic normal displacement which was affected by the normal stress.

剪切试验结果表明，粗粒土与土工布接触面出现了一定程度的应变软化，相对法向位移的变化受法向应力影响很大，并表现出异向性。

Being different from the unique vein pattern under quasistatic compress, adiabaticshear fracture occurs at high stress rate in dynamic compressive test. In addition to the veinpatterns in the fractural surface, some melting area is also observed.

与准静态压缩条件下的均匀脉络纹断口形貌不同，在高应变率下发生绝热剪切破坏，在含有部分脉络纹断口中，还出现了绝热引起的熔化区。

Through metallographic analyses, the failure is found to be dimple intercrystalline fracture under high strain-rate loading.

基于试样金相和断口分析，30CrMnSiNi2A钢在高应变率冲击加载条件下产生了韧窝型沿晶断裂，导致材料宏观上表现为剪切破坏。

In order to overcome the defect of traditional methods and to find a new simply and effective time-domain method to eliminate the influence of boundary reflection. The main contents of studies and achievements are as follows: The liquefiable saturated sand dynamic character researches are conducted by means of the resonant column test and the dynamic tri-axial test; The undrain dynamic relationship between stress and strain, the damping ratio, saturated sand liquefaction mechanism, laboratory liquefaction standard, the effective factors of liquefaction are considered in laboratory. Liquefaction strength parameters used in element numerical simulation are obtained.

为克服传统方法存在的问题，寻求一种简单有效、能消除截断边界反射影响的时域有限元方法，本文主要开展了如下研究工作：对工程场地土体进行了标准贯入、静力触探、剪切波速等现场原位试验、室内动三轴试验以及共振柱试验，针对研究区域内可液化的饱和土进行了动力特性试验研究，分析了饱和土体的不排水动应力～应变关系和阻尼特性；对研究区域内的饱和砂土的液化机理，室内试验液化判别标准及影响饱和砂土液化的诸多因素进行了研究，得出了工程场地土体的抗液化强度指标等有限元模拟所需参数。

Moreover, the effects of strain－rate history on its constitutive relation under torsion load were firstly researched by means of interrupted load tests at different temperatures and prestrain rates.

在给定应变率下，其剪切强度随温度的升高而降低。

In the extensional rheometric tests, the occurrence of phenomena of "strain hardening1relied on the structure of linear long chains, and mPE didn"t show the behavior of "strain hardening", which implied that the melt strength of mPE was poor.

通过研究发现，在n1PE中混入少量LDPE，不仅能够显著降低n1PE的熔体粘度，提高其熔体粘度对剪切速率的依赖性，而且还可以有效地提高mPE的熔体强度，使mPE熔体在拉伸流动中出现显著的&应变硬化&现象。

All model parameters could be easily gained from the results of one-dimensional compression tests and triaxial undrained shear tests.

分别计算了代表性等向和K0固结黏土的三轴不排水等应变率加载、不排水剪切蠕变及蠕变破坏过程，与试验结果进行对比，验证本文模型的有效可行性。

The research contents include following aspects:(1) In this paper,a series of consolidated and undrained triaxial compression tests were carried out on soil samples of various dry density to study strain types ;the stable prosperities and strength characteristics of the silty soil of the Yellow River Estuary.

论文的主要研究工作包括：(1)通过对不同干密度的黄河口粉质土重塑土样的固结不排水剪切试验，分析探讨黄河口粉质土的应变类型；强度指标的变化规律以及稳态强度的特征。

Secondly, with a triaxial test instrument for unsaturated loess which can work with computerized tomograph carried original Q3 and Q2 loess testing on instantaneously, quantificationally and undamaged scanning. Combining CT images, data and stress-strain curve, this paper divided shearing process into 4 period with respectively analyzing studying.

其次，应用非饱和黄土的三轴CT扫描仪，进行了原状Q_3、Q_2黄土的三轴试验过程的动态、定量、无损的CT扫描，结合CT图像、数据与应力应变关系，对非饱和黄土的剪切过程分4个阶段进行了深入分析研究。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。