Microstructure evolution in eutectoid steel during warm deformation in the temperature range from 600 to 700℃ was investigated by simulating hot compression test, SEM and thermomagnetic measurement. The effects of deformation and subsequent annealing on the spheroidizing of pearlite, refining of microstructure and dissolution of cementite were studied.

利用热模拟压缩变形、SEM和热磁法实验,研究了共析钢在600~700℃变形过程的组织演变规律,探讨了变形及随后保温过程对珠光体球化、组织超细化和渗碳体溶解、再析出的影响。

It is convenient for sinter to be leached, and the secondary reaction appears little. The slurry after sinter leaching is transferred into autoclave for desilicification at about 170℃, and the siliceous modulus of solution reaches more than 200. Then some lime is added for deep-desilication at normal pressure, the siliceous modulus of solution increases more than 600 even if the Al2O3 content is more than 200g/L.The SiO2 coefficient in hydrate garnet from deep-desilication is more than 0.28. Under conditions of the addition of seed and application of novel technology of carbonization, the contents of Na2O and SiO2 in product are less than 0.37% and 0.025%, respectively.

实验结果显示:烧成的熟料溶出条件宽松,二次反应程度弱;溶出浆液在170℃左右直接进行加压脱硅,脱硅后溶液的硅量指数大于200,再加入适量的石灰进行深度脱硅,即使溶液中氧化铝浓度超过200g/L时,精液的硅量指数也大于600,且得到的水化石榴石中二氧化硅饱和系数大于0.28;通过加入晶种和采用新的碳酸化分解工艺制度,产品中的SiO2 含量降至0.025%, Na2O含量小于0.37%;加入表面活性剂,不仅能将碳分母液蒸发至Na2OT浓度大于300g/L,而且还可有效减缓表面上结疤的形成速度。

Methods Activate groups A and C meningococcal polysaccharide with cyanogens bromide and prepare into MenAPS-ADH and MenCPS-ADH derivatives by reacting with 1, 6-adipic acid dihydrazine. Mix MenAPS-ADH and MenCPS-ADH derivatives with purified tetanus toxoid at a certain mass ratio, then add l-ethyl-3(3-dimethylaminopropyl)-carbodiimide to prepare bulks of MenAPS-TT and MenCPS-TT conjugates respectively. Mix the two bulks at a certain ratio, add stabilizer and lyophilize to prepare group A+C meningococcal polysaccharide conjugate vaccine.

A群和C群脑膜炎球菌多糖在溴化氰的活化下,以1,6己二酰肼作为连接子,与精制破伤风类毒素在碳二亚胺作用下结合,再按一定的比例将两者混合,制成A+C群脑膜炎球菌多糖结合疫苗原液,加保护剂冻干后,制成A+C群脑膜炎球菌多糖结合疫苗。

High-intensity combined safety glass is a revolution of glass plate history. Traditional glass is fragile, heavy and easy to hurt person when broken. However, high-strength compound safety glass consisted with two tempered glasses with a layer as a sandwich , its thickness is only 1.1 +1.1 mm, or 1.5 +1.5 mm, 1.8 +1.8 mm, 2.0 +2.0 mm—Intensity, as well as impact strength, of tempered glass have been greatly increased. Even if glass is broken, its splinter will be adhesive together and will not hurt person mainly coz the glass is very thin. This glass bears the duty of door hinge as door plate of wardrobe or cupboard in the installation.

高强度复合安全玻璃的面世是碳光板玻璃板材的一次革命,传统的玻璃让人们感觉:易碎、笨重、破裂后伤人;然而高强度复合安全玻璃是由两片强化过的玻璃,再经过夹胶复合的玻璃,玻璃的厚度仅有1.1mm+1.1mm或1.5mm+1.5mm、1.8mm+1.8mm、2.0mm+2.0mm…钢化过的玻璃强度大大增强了,抗冲击力度也非常高,即使玻璃破碎后也粘接在一起不会伤人,很重要的一点因为玻璃的厚度很薄,作为任何衣柜或橱柜的门板在安装方面解决了门铰链的承重问题。

第3/3页 首页 < 1 2 3
推荐网络例句

The split between the two groups can hardly be papered over.

这两个团体间的分歧难以掩饰。

This approach not only encourages a greater number of responses, but minimizes the likelihood of stale groupthink.

这种做法不仅鼓励了更多的反应,而且减少跟风的可能性。

The new PS20 solar power tower collected sunlight through mirrors known as "heliostats" to produce steam that is converted into electricity by a turbine in Sanlucar la Mayor, Spain, Wednesday.

聚光:照片上是建在西班牙桑路卡拉马尤城的一座新型PS20塔式太阳能电站。被称为&日光反射装置&的镜子将太阳光反射到主塔,然后用聚集的热量产生蒸汽进而通过涡轮机转化为电力