To optimize the compounding of the photo-sensitive resin, a novel prepolymer was synthesized and token by FT-IR. The prepolymer was an alicyclic epoxy acrylate, which was synthesized from the alicyclic epoxy resin.

为了优化光敏树脂配方，作者又合成了一种光敏树脂组分中的主体树脂并经傅立叶红外光谱表征，该树脂是以脂环族环氧树脂为原料合成的脂环族环氧丙烯酸酯。

The results also show the sensitivity is enhanced for the pigments with a larger anilide ring. It is important to note that the photosensitivity is greatly increased when the coupler component changed ftom a 2-hydroxy-3-naphthanilide to a 2-hydroxy-11H-benzocarbazole-3-naphthanilide coupler. Clearly, conjugation effects favours to enhance the photosensitivity.

偶合基部分共轭环的扩大使蒽醌偶氮染料的光敏性增加，特别是偶合基萘环上扩大了一个咔唑环后，其吸收光谱大幅红移，光敏性提高了几十倍，这一结果对红外偶氮光导染料的设计合成具有重要参考价值。

The volt-ampere characteristic property with photodiode and photosensitive audion is the basis designing an experiment's.

以光敏二极管和光敏三极管的伏安特性作为设计实验的基础。

The platform designing that the photoelectricity sensor tests the instrument experiment this time adopt CSY-998G , the system making use of the photoconductance effect to be one kind of body effect of semiconductor materials , building an experiment, test photosensitive audion waiting for photosensitive transistor volt-ampere characteristic property.

此次设计采用CSY-998G光电传感器试验仪实验平台，利用光电导效应是半导体材料的一种体效应，建立实验系统，测试光敏三极管等光敏晶体管的伏安特性。

At last, the photoconductivity of some samples was detected, and the results of characteristics evaluation revealed that superfine Y-TiOPc is excellent photoelectric material.

最后，对制备的部分产品进行光敏性能检测，结果显示超细Y型酞菁氧钛具有良好的光敏性能，是一种优良的有机光导材料。

It includes the following steps: polymerizing 2, 4-dihydroxyl metaphenylene diamine hydrochloride, diamine monomer and dipic acid anhydride to gain the polyimide that contains hydroxy on the molecule chain, making the hydroxyl take esterification reacting with acyl chloride and acrylic acid to gain polyimide photosensitive material that has negative photonasty.

该聚酰亚胺光敏材料以2，4-二羟基间苯二胺盐酸盐，二胺单体和二酸酐为原料进行聚合，得到分子链上含羟基的聚酰亚胺，然后使羟基与丙烯酸及其衍生物的酰氯发生酯化反应，得到具有负性感光性能的聚酰亚胺光敏材料。

The changing rule of the hardness of SZ-01 photosensitive resin surface after curing with temperature, illumination distance, and illumination time was studied with orthogonal experiment and recurrent neural network methods. A group of reasonable technique parameters were found with genetic algorithm optimization, which can make the hardness of photosensitive resin after curing the highest.

综合利用正交试验和递归神经网络的方法，研究了光敏树脂SZ-01在光固化成形后表面硬度随着环境温度、光照距离及光照时间的变化规律，并利用遗传优化设计的方法，找到了一组合理的工艺参数组合，使得光敏树脂固化后的表面硬度达到最大。

Experiment on photosensitivity characteristics of the samples preformed both at room and high temperature (410℃), respectively.

对薄膜在室温和较高温度(410℃)下进行光敏特性测试，结果表明，薄膜的制备工艺参量对其光敏特性有较大影响；较高温度下其敏感特性和室温下测试的结果大体一致；在合适条件下制备的薄膜对不同波长的光有较好的敏感特性。

A 10-mA input trigger current from a microcontroller turns on the power phototriac which in turn provides power to the motor.

来自微控制器的10mA输入触发电流会开启功率光敏，然后光敏再为电动机供电。

A dye recycled photosensitization system has been designed. As a result of studies in the mechanism of electron transfer reaction of xanthene iodonium salt, it is proposed that the dye-recycled process consists of three-step reactions during the photosensitization: The oxidative fading product of dye is formed through electron transfer under irradiation; In the presence of H-donor, product changes into acidic leuco dye product; Product undergoes deprotonization under action of base to regenerate initial dye.

本文设计了染料循环再生的光敏反应体系，通过对占吨碘翁盐电子反应机制的深入研究，提出了占吨染料在光敏反应过程中的染料再生循环，它依次由三个反应过程组成：在光作用下，通过电子转移反应，产生染料氧化褪色体；在H给体存在下，通过H转移反应，使产物转化为染料酸式隐色体；在碱作用下，发生去质子反应，染料再生回复到染料的起始结构。