乙烯基

Results show that the tensile strength and the tear strength could reach 8.71MPa and 52.14kN/m respectively in the presence of 150phr ethylene silicone rubber,1phr hydrogenous silicone oil,2phr polyvinylsilicone oil,4 phr hydroxyl silicone oil and 40phr amorphous silica.

结果表明，在150份乙烯基质量分数为0.13%的硅橡胶中加入1份硅氢基质量分数为1.65%的含氢硅油、2份乙烯基质量分数为8%的多乙烯基硅油和4份羟基硅油，用40份白炭黑增强，可得到拉伸强度为8.71 MPa，撕裂强度为52.14 kN/m的乙烯基硅橡胶。

To develop an eco-friendly epoxy impregnating resin system for groundwall insulation of large generators, the curing reaction mechanism has been fully studied, the formulation and the curing techniques have been optimized, and the influence of different constitution on the curing reaction, microstructure, and final performances have been studied and characterized.In this paper, influences of different reactive organo-siloxanes on the curing reaction and performances of epoxy V.P.I.

本文研究比较了含有环氧基、氨基或乙烯基的反应性硅氧烷，包括：γ-缩水甘油醚氧丙基甲基二乙氧基硅烷、β-(3，4环氧环已基)乙基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅、β-(3，4环氧环已基)乙基三甲氧基硅烷、γ-甲基丙烯酰氧基丙基三甲氧基硅烷、乙烯基三乙氧基硅烷和苯胺甲基三乙氧基硅烷对环氧V.P.I。

The present invention relates to a thermoplastic interpolymer product comprising an alpha -olefin interpolymerized with at least one vinyl or vinylidene aromatic monomer and/or at least one hindered aliphatic or cycloaliphatic vinyl or vinylidene aromatic monomer and, in at least one aspect, is characterized as having substantially synergistic thermal properties.

本发明涉及一种包含与至少一种乙烯基或亚乙烯基的芳族单体和/或至少一种受阻的脂族或环脂族的乙烯基或亚乙烯基芳族单体共聚的α－烯烃热塑性共聚体产物，及至少一方面，其特征为具有实质协同热性质。

So, by the Diels-Alder reaction of tetraphenylcyclopentadienone, acenaphthenecyclone and benzophenanthrenecyclone with the vinyl groups in C gum, three kinds of polymethylvinylsilicone oil with condensed aromatics are synthesized respectively: polymethylvinylsilicone oil with tetraphenylphenyl groups (called C_1 gum for short), polymethylvinylsilicone oil with acenaphthenyl groups (C_2 gum) and polymethylvinylsilicone oil with benzophenanthrene groups (C3 gum).

根据此原则，利用四苯基环戊二烯酮、苊式环戊二烯酮和菲式环戊二烯酮与C胶上的乙烯基进行Diels—Alder反应，分别合成了三种含稠环基团的乙烯基硅油：四苯基苯基乙烯基硅油(C_1胶)，苊式多苯基苯基乙烯基硅油(C_2胶)和菲式多苯基苯基乙烯基硅油(C_3胶)，并根据~1HNMR谱图上不同氢原子的积分面积计算了三种胶中稠环基团和乙烯基的含量。

Compounds were determined from more than 3 stages, including germacrene D, caryophyllene, phenol, 2, 6-bis (1, 1-dimethylethyl)-4-methyl-,β-elemene,γ-elemene, 1-octanol, 2-butyl-, dibutyl phthalate, cyclohexane, 1-ethenyl-1-methyl-2-(1-methylethenyl)-4(1-methylethylidene)-and butyl caprylate.

其中，3个时期以上能检测到相同的化学成分有9种，分别是大牻牛儿烯D、丁香烯、2，6-二叔丁基－4-甲基苯酚、β-榄香烯、γ-榄香烯、2-丁基－1-辛醇、邻苯二甲酸二丁酯、1-乙烯基－1-甲基－2-（1-甲基乙烯基）－4-（1-甲基亚乙烯基）环己烷和辛酸丁酯。

The absorbency changes of both thiol and vinyl functional group were monitored independently by FTIR spectrometer during vinyl silazane photopolymerizing with ethanedithiol, Based on the results,the kenitics of reaction was studied and the convertion of both thiol and vinyl functional groups were investigated.

采用傅立叶变换红外光谱法跟踪巯基和乙烯基吸光度的变化，跟踪测定了光聚合反应过程中巯基和乙烯基的转化率，研究了乙二硫醇/乙烯基硅氮烷体系的光聚合反应动力学。

Three novel rigid compounds 3, 6-bis[2-(4-pyridylethenyl]-9-ethylcarbazole (L~1), 3,6-bis[2-(2-pyridyl)ethenyl]-9-ethylcarbazole (L~2), 3,6-bis[2-(4-pyridyl)ethenyl]-9 -ethylpyridylcarbazole (L~3) were successfully synthesized by Heck reaction, which were fully characterized by elemental analyses, NMR, MS, IR spectra and single X-ray diffraction analysis.

利用Heck偶联反应，成功地合成了三种新型刚性的吡啶基咔唑类化合物：3，6-二[2-(4-吡啶基)乙烯基]-9-乙基咔唑(L~1)，3，6-二[2-(2-吡啶基)乙烯基]-9-乙基咔唑(L~2)和3，6-二[2-(4-吡啶基)吡啶基]-9-乙基吡啶基咔唑(L~3)，通过元素分析、核磁共振谱、质谱、红外光谱和单晶X-射线衍射等分析手段确证了它们的结构。

Two novel A-it-A' type benzothiazole-based derivatives with benzothiazolyl, phenyl-acetyl or pyridine cation groups as π electron acceptor, diethenylphenyl as π conjugated bridge: 4-(2-benzothiazolyl) ethenylchalcone (1) and 4-{4-[2-(benzothiazole-2-yl) ethenyl] styryl}-N-methylpyridinium iodide (2) were synthesized.

以苯并噻唑、苯乙酰基和吡啶阳离子为电子受体，二乙烯基苯为共扼桥，合成了两个新的A-π-A'型苯并噻唑衍生物：4-（2-苯并噻唑）－乙烯基查尔酮(1)和4-｛4-［2-乙烯基］苯乙烯基｝－N-甲基吡啶碘盐(2)。

Two novel A-π-A′ type benzothiazole-based derivatives with benzothiazolyl,phenyl-acetyl or pyridine cation groups as π electron acceptor,diethenylphenyl as π conjugated bridge: 4-(2-benzothiazolyl)ethenylchalcone(1) and 4-{4-[2-(benzothiazole-2-yl)ethenyl]styryl}-N-methylpyridinium iodide(2) were synthesized.

以苯并噻唑、苯乙酰基和吡啶阳离子为电子受体，二乙烯基苯为共轭桥，合成了两个新的A-π-A′型苯并噻唑衍生物：4-(2-苯并噻唑)-乙烯基查尔酮(1)和4-{4-[2-乙烯基]苯乙烯基}-N-甲基吡啶碘盐(2)。

Use D4 or DMC,vinyl di-blocking agent,ringy vinyl,hexamethyl-disiloxane as raw materials,tetramethyl hydroxyl ammonium as catalyst,we synthesized a vinyl silicone oil.

以D4，乙烯基双封头，乙烯基环体，六甲基二硅氧烷等为原料，四甲基氢氧化铵为催化剂合成了摩尔质量和乙烯基含量不同的乙烯基硅油；以高含氢硅油，含氢双封头，D4合成实验所需的含氢硅油；以白碳黑为填料通过密炼等工序制备了医用高透明液体注射硅橡胶。