The corrosion behavior of austenite stainless steel weld joint in the different acidic medium was studied.

研究了奥氏体不锈钢焊接接头在不同酸性介质中的腐蚀行为。

Effect of longitudinal magnetic field on microstructure and properties of MIG weld joint of mild steel

采用横向变拘束试验，研究铝锂合金和2024合金的焊接热裂纹敏感性；并对焊缝组织进行分析，探讨它对两种合金焊接开裂倾向的影响。

Ii The effect of mechanical property nonhomogeneity in weld joint-heterogenous bodies on J integral.

焊接接头非均匀体的力学性能非均匀性对J积分的影响

Iii The effect of mechanical property nonhomogeneity in weld joint-heterogenous bodies on COD.

焊接接头非均匀体的力学性能非均匀性对COD的影响。获得了一些重要结论。

The resistance spot weld nugget is formed when the interface of the weld joint is heated due to the resistance of the joint surfaces to electrical current flow.

电阻点焊狗头时会形成界面的焊接接头加热，由于阻力的联合表面的电流流动。

When the above phosphating process was used on the weld joint of wire, the result showed that the phosphate coating can eliminate surface transverse cracks.

生产性磷化试验表明，采用低温快速磷化工艺对盘条焊接区进行磷化处理，能有效地防止表面横向裂纹的产生。

When the Al-Mg-Zr-Sc welding wire was used as filling material, the grains of welding seam were refined obviously, and the weld joint was greatly strengthened by forming of fine equiaxial grains layer in fusion zone.

结果表明：采用两种焊丝焊接的Al-Mg-Sc合金薄板的焊接接头强度系数均大于0.9。

When the Al-Mg-Zr-Sc welding wire was used as filling material,the grains of welding seam were refined obviously,and the weld joint was greatly strengthened by forming of fine equiaxial grains layer in fusion zone .

但采用Al-Mg-Zr-Sc合金焊丝为填充材料时，焊缝晶粒组织明显细化，熔合区形成的细小等轴晶层提高了基材与焊缝填充材料的结合力，焊接接头的屈服强度比采用Al-Mg-Zr合金焊丝为填充材料时提高了100 MPa，显著提高了Al-Mg-Sc合金焊接构件的许用强度，因此焊接Al-Mg-Sc板材更宜采用Al-Mg-Sc-Zr焊丝。

The results show that, the coefficients of welded joints are both greater than 0.9, but the yield strength of weld joint filled with Al-Mg-Zr-Sc welding wire is greater 100 MPa than that of filled with Al-Mg-Zr welding wire. It indicates that the Al-Mg-Zr-Sc welding wire is the best alteration of filling materials to weld of Al-Mg-Sc alloy.

但采用Al-Mg-Zr-Sc合金焊丝为填充材料时，焊缝晶粒组织明显细化，熔合区形成的细小等轴晶层提高了基材与焊缝填充材料的结合力，焊接接头的屈服强度比采用Al-Mg-Zr合金焊丝为填充材料时提高了100 MPa，显著提高了Al-Mg-Sc合金焊接构件的许用强度，因此焊接Al-Mg-Sc板材更宜采用Al-Mg-Sc-Zr焊丝。

This article has studied HG70 steel and HS-70 welding wires weldings,the welded joint,welding quality,and the welding operational performance,in restricts under the welding condition,Uses HS-70 welding wires,Experiments the steel plate the weld joint stretch,degree of hardness and the resilience test result indicated that,HG70 steel and HS-70 welding wires weld joints have the low crack sensitivity,The welding quality is good,Its weld joint has the fine mechanics performance,thus explained they had the fine welding match.

0前言非调质钢具有优良的使用性能和较低的生产成本，受到普遍重视。HG70钢是武钢开发的工程结构用钢，具有强度高、低温韧性好的特点。传统高强度钢一般碳当量较高，焊接性能较差。通过加入微量合金元素、采取新的控轧和调质工艺，使得HG70钢在提高强度的同时，亦保持了较高的韧性和较低的碳当量，因而从理论上讲HG70应具有较好的焊接性能，但HG70钢与HS-70焊丝的匹配情况，还有待于分析验证。

It has been put forward that there exists single Ball point and double Ball points on the symmetrical connecting-rod curves of equilateral mechanisms.

从鲍尔点的形成原理出发，分析对称连杆曲线上鲍尔点的产生条件，提出等边机构的对称连杆曲线上有单鲍尔点和双鲍尔点。

The factory affiliated to the Group primarily manufactures multiple-purpose pincers, baking kits, knives, scissors, kitchenware, gardening tools and beauty care kits as well as other hardware tools, the annual production value of which reaches US$ 30 million dollars.

集团所属工厂主要生产多用钳、烤具、刀具、剪刀、厨具、花园工具、美容套等五金产品，年生产总值3000万美元，产品价廉物美、选料上乘、质量保证，深受国内外客户的青睐