The present invention prepares aldehyde or ketone by catalytic oxidation of alcohol under microwave irradiation, which takes sodium tungstate and tungstic heteropolyacid salts as catalyst, takes bidentate ligand containing nitrogen and oxygen as additive and takes hydrogen peroxide as preparing oxidant.

本发明以钨酸钠和钨的杂多酸盐为催化剂，以含氧氮的双齿配体作为助剂，以双氧水为氧化剂，在微波辐照下催化氧化醇制备得醛或酮。

The mainly conclusions in our research are as flowing: tungsten trioxide powders with 100 nm primary particle are obtained by spray drying,calcination and wet milling process, and an average size of quadric particle composed of agglomerated particles is 0.64 μm; tungtsen powders with 39 nm grain size and 60 -100 nm primary particle are produced directly from previous tungsten trioxide using one step reduction in hydrogen at 700℃, and an average size of quadric particle of tungsten powder is 2.91 μm; tungsten trioxide and copper tungstate compound powders with 100 nm - 200 nm primary particle are produced using ammonia metatungsten and copper nitrate as raw materials by spray drying,calcination and wet milling process;the compound powders are transformed completely into tungsten and copper compound powders by reduction in hydrogen at 700℃,in which tungsten grain size is 59 nm and copper grain size is 51 nm; primary particle size of compound powders is 80 - 120 nm,and an average size of agglomerated quadric particle is 1.86 μm; tungsten nitride powders with 35 nm grain size are prepared from tungsten trioxide powders by nitrogen treatment thoroughly in pure ammonia at 650℃, and an average size of agglomerated quadric particle is 0.64 μm in normal temperature.

研究结果表明：采用喷雾干燥—焙烧—球磨工艺可以制备出粒度约为100nm的WO_3粉体，它们在团聚后形成的二次颗粒平均粒度为0.64μm；采用一步直接氢还原方法可在700℃下从上述WO_3粉体制备出晶粒尺寸为39nm的、一次颗粒粒度为60-100nm的W粉体，其二次颗粒的平均粒度为2.91μm；以偏钨酸铵、硝酸铜为原料，采用喷雾干燥—焙烧—球磨工艺可制备出一次粒度为100-200nm的WO_3和CuWO_4混合粉体；采用氢还原工艺可在700℃下将这种粉体完全转变为W、Cu复合粉体，其中W的平均晶粒粒尺寸为59nm，Cu的平均晶粒尺寸为51nm；复合粉体的一次颗粒尺寸为80-120nm，在常温下团聚后形成的二次平均粒度为1.86μm；采用纯氨氮化工艺可以在650℃下由WO_3粉体制得WN，其晶粒尺度为35nm，在常温下团聚后的二次平均粒度为6.4μm。

The main products are sodium tungstate, tungstic acid, ammonium perchlorate, tungsten trioxide, industrial ammonium molybdate, sodium molybdate, Chung-ammonium molybdate, ammonium tungsten migraine, two ammonium molybdate, barium molybdate, tungsten electrode wire cutter, cerium Tungsten welding electrode, etc., such as tungsten and molybdenum products.

主要产品有钨酸钠、钨酸、仲钨酸铵、三氧化钨、工业钼酸铵、钼酸钠、仲钼酸铵、偏钨酸铵、二钼酸铵、钼酸钡、钨绞丝电极、铈钨等氩弧焊电极等钨钼系列产品。

Synergistic effect was observed when these inhibitors compounded with sodium molybdate, sodium tungstate and azimino-benzene, respectively.

这3种缓蚀剂分别与钼酸钠、钨酸钠、苯并三唑复配后的缓蚀效果均好于单独使用缓蚀剂时的效果。

The epoxidation of α-pinene and β-pinene by 50% hydrogen peroxide and a small amount of sodium tungstate, in the presence of quaternary ammonium salt A-1 as a phase transfer catalyst, is carried out.

摘 要：采用季铵盐A-1作相转移催化剂，质量分数为50%的H2O2作氧化剂，三氯甲烷作溶剂，在加入少量钨酸钠的条件下，实现了α-蒎烯和β-蒎烯的环氧化反应。

The progress in the research on Polyaspartic acid as green water treatment corrosion inhibitor is reviewed in detail. The inhibition effects of PASP for carbon-steel, copper and copper alloys corrosion in different solutions are summarized. It is shown that the complex of PASP and sodium tungstate has a good synergistic effect.

综述了近年来聚天冬氨酸作为水处理缓蚀剂的研究进展；探索了其对碳钢、铜及铜合金在不同体系中的缓蚀效果；指出了复配聚天冬氨酸具有较好的缓蚀协同效应。

Epoxysuccinic acid was synthesized from maleic anhydride using sodium tungstate as catalyst and hydrogen peroxide as oxidizer and was characterized by IR and 13 C NMR.

以马来酐为原料，钨酸钠为催化剂，双氧水为氧化剂，合成了环氧琥珀酸，并对其进行了红外、13C核磁表征。

Sodium tungstate ; cyclohexene ; catalytic oxidation ; adipic acid ; acidic ligand ; reaction kinetics

钨酸钠；环己烯；催化氧化；己二酸；酸性配体；反应动力学

It was found from orthogonal experiment that the recombination of sodium benzoate, ammonium benzoate, cinnamic acid and sodium tungstate had good synergistic reaction. Based on the orthogonal experiment, a kind of new prescription of vapor phase corrosion inhibitor for DI material is found, which is not only high effective but also friendly to environment.

通过正交试验发现：苯甲酸钠、苯甲酸铵、肉桂酸与钨酸钠的复配使用，表现出很好的协同作用，从而得到了一种新的环保、高效的用於DI材的气相缓蚀剂配方。

Key words: sodium yttrium tungstate crystal doped with neodymium; Raman spectra; absorption spectrum; Czochralski method

为此，采用提拉法生长了 Nd ， NYW 晶体，分析了晶体的红外光谱、 Raman 光谱和吸收光谱。

According to the clear water experiment, aeration performance of the new equipment is good with high total oxygen transfer coefficient and oxygen utilization ratio.

曝气设备的动力效率在叶轮转速为120rpm～150rpm时取得最大值，此时氧利用率和充氧能力也具有较高值。

The environmental stability of that world - including its crushing pressures and icy darkness - means that some of its most famous inhabitants have survived for eons as evolutionary throwbacks, their bodies undergoing little change.

稳定的海底环境─包括能把人压扁的压力和冰冷的黑暗─意谓海底某些最知名的栖居生物已以演化返祖的样态活了万世，形体几无变化。