The results show that microstructure of rolled steel is bainite + sorbite + some nubby ferrite, and the hardness is 32 HRC.

结果表明，该钢在轧制状态能获得贝氏体+索氏体+少量块状铁素体组织，硬度达32HRC。

With the increased of tempering temperature, the content of tempering troostite decreased, meanwhile tempering sorbite and particles precipitation increased.

且随回火温度的升高，回火屈氏体含量降低，回火索氏体含量增加，第二相粒子析出增加。

In order to improve anti-fatigue property of wire rope, poval solution sorbitized treatment by water quenching replacing by lead quenching has been studied in laboratory, and a heat treatment process to obtain fine and homogeneous sorbite and possess high micro-hardness has been found.

为了进一步提高钢丝绳的抗疲劳性能，本文还进行了用聚乙稀醇水溶液水浴淬火索氏体化处理替代铅浴处理的实验室研究，找到了一种能使钢丝得到细而均匀的索氏体组织和具有较高显微硬度值的热处理工艺。

It is found that the fine tempering sorbite is obtained in condition of 930℃ direct quenching temperature and 640℃ tempering temperature after controlled rolling.

结果表明：经奥氏体再结晶区和未再结晶区两阶段结合控制轧制后在线930℃直接淬火、640℃回火，钢板可获得均匀、细小的回火索氏体组织，其综合力学性能均超过标准要求。

The main methods improving the strength of galvanized wire for bridge cable are to improve the strength of sorbite wire rod, increase drawing hardening effect and decrease strength lose in the course of galvanizing.

提高桥梁缆索镀锌钢丝强度的主要方法是提高索氏体盘条的强度、提高加工硬化效果和减少热镀锌过程的强度损失。

Strain fatigue life in pearlite is longer than that in tempered sorbite with same tensile strength, which can be attributed to the small plastic strains in pearlite.

轨钢的应变疲劳是塑性应变控制过程，抗拉强度相等时，珠光体的应变疲劳寿命高于回火索氏体的疲劳寿命，其原因在于珠光体具有较小的塑性应变幅。

The ginger-like Sorbite forming mechanism andthe high wear-resistance of ginger-like carbide cutter blade werestudied in this paper.

本文从空间形貌上说明姜块状碳化物的形成机制，并从微观机理分析姜块状碳化物提高刀片耐磨性的原因。

The characteristic of the new process is heating under Acl temperature for suitable time to change lamellar Sorbite to ginger-like Sobite.

工具钢在稍低于Acl温度下不太长时间保温，可使珠光体片不完全球化，形成姜块状索氏体，淬火后得到马氏体＋姜块状碳化物组织。

It is found that the fine tempering sorbite is obtained in condition of 930℃ direct quenching temperature and 640℃ tempering temperature after controlled rolling. The mechanical properties of SPV490 steel plate are above the standard requirement.

结果表明：经奥氏体再结晶区和未再结晶区两阶段结合控制轧制后在线930℃直接淬火、640℃回火，钢板可获得均匀、细小的回火索氏体组织，其综合力学性能均超过标准要求。

The microstructure of the material after quenching and tempering was found to be tempered bainite,rather than tempered sorbite expected by the technology,another reason of the failure is the improper heat treatment.

热处理工艺不当是造成端轴断裂的另一重要原因。

This one mode pays close attention to network credence foundation of the businessman very much.

这一模式非常关注商人的网络信用基础。

Cell morphology of bacterial ghost of Pasteurella multocida was observed by scanning electron microscopy and inactivation ratio was estimated by CFU analysi.

扫描电镜观察多杀性巴氏杆菌细菌幽灵和菌落形成单位评价遗传灭活率。