Through the methods of sol-gel, hydrothermal reaction and forced hydrolysis, iron oxide particles with cubic, spherical, spindle and acicular shape were prepared with adding different regulators of crystal growth, such as NaH2PO4, HEDP. And through the methods of complexing-precipitate and precipitate, copper oxide and power blue were prepared respectively.

通过水热法、溶胶-凝胶法分别制备出了纳米球形和立方形Fe_2O_3；采用强迫水解法，通过添加晶型控制剂NaH_2PO_4、HEDP分别制备出了纳米纺缍形和针形Fe_2O_3，通过络合沉淀法制备出纳米球形CuO，通过沉淀法制备出纳米Co_2O_3。

Hydroquinone-formaldehyde organic aerogels with high HC ratio (10~40, molar ratio of hydroquinone to catalyst) have been prepared using sol-gel process. And carbon aerogels have been prepared by pyrolyzing the aerogels.

溶胶－凝胶法制备了高HC比（10~40，对苯二酚与催化剂(Na2CO3)的物质的量之比）的对苯二酚－甲醛有机气凝胶，并经高温碳化处理得到其碳气凝胶。

There are two transition points in the resistant-temperature curve of the La_(0.7)Ca_(0.3)MnO3 film fabricated by sol-gel method, and it is the result of the interaction between double exchange and small polarons that play a important role in CMR films.

在溶胶-凝胶法制备的La_(0.7)Ca_(0.3)MnO_3薄膜的电阻-温度曲线中，出现了两个转变点，这是双交换作用和晶格畸变产生的小极化子相互竞争的结果；

Using LaNiO3 as a buffer layer, highly (100)-oriented PZT thin film heterostructures are successfully prepared using a sol-gel process on both Si and platinized silicon substrates.

采用LaNiO3缓冲层技术，在硅和铂化硅两种衬底上实现了高度(100)择优取向的PZT铁电薄膜。

Glass coatings that include iron and cerium oxidations were prepared by citric acid sol-gel and dip-coating method.

采用柠檬酸溶胶－凝胶法制备了含有铁离子和铈离子的溶胶，并用浸渍－提拉法和热处理工艺在玻璃表面镀制了Fe/Ce氧化物薄膜。

The palladium-octaisopentyloxy-phthalocyanine-doped ormosil glass (octa -PdPc glass) is prepared by the sol-gel method. The nonlinear coefficient of Octa-PdPc glass is measured by single-beam Z-scan method. The result with automatic Z-scan system is more accurate than the manual measurement.

的EPM2000。我们用溶胶-凝胶法制备了掺杂八异戊氧基钯酞菁玻璃，并利用自动Z扫描测试系统对该样品的三阶非线性光学特性进行了研究，结果表明该材料具有大的三阶非线性系数。

ZnO quantum-dots capped with SiO2 were synthesized by Sol-gel method in dilute water-free solution.

本文利用溶胶-凝胶法在非水稀溶液中制备出SiO2包覆的ZnO量子点。

The FTIR and TEM results show that Ce3-sol free from NO3-, CO32- was prepared by ion exchange method without washing, then the CeO2 crystal of high purity was synthesized by oxidation with H2O2 and vacumm drying. The sample obtained had an average diameter of 3 nm and good dispersity.

FTIR、TEM分析表明，离子交换法无需对合成的Ce3溶胶进行洗涤即可去除NO3-、CO32-等阴离子杂质，并用H2O2将该溶胶氧化，经真空干燥可制得粒径分布均匀，平均晶粒尺寸约3 nm，高纯度的CeO2粉体。

The sol–gel was then thermally cured under vacuum in a Heraeus vacuum oven for 3 hours at 70 °C.

这个 当时的热溶胶-凝胶法在真空中一流真空烘箱3小时在70°C。

Tungsten powder and H2O2 are used as main starting materials to prepare nano structure d tungsten trioxide films with Pd catalyst by sol-gel technique and spin coating method.

以钨粉和双氧水为原料，采用溶胶-凝胶技术结合提拉镀膜法，制备了纳米结构掺钯气致变色WO3薄膜；分析了薄膜的折射率、厚度、结晶度、红外特性和表面形貌随温度变化特性；研究了薄膜的气致变色性能。

On the other hand, the more important thing is because the urban housing is a kind of heterogeneity products.

另一方面，更重要的是由于城市住房是一种异质性产品。

Climate histogram is the fall that collects place measure calm value, cent serves as cross axle for a few equal interval, the area that the frequency that the value appears according to place is accumulated and becomes will be determined inside each interval, discharge the graph that rise with post, also be called histogram.

气候直方图是将所收集的降水量测定值，分为几个相等的区间作为横轴，并将各区间内所测定值依所出现的次数累积而成的面积，用柱子排起来的图形，也叫做柱状图。