In late Tang period,influenced by west Asian great cutting Dao,each 'country' is more powerful because of this shape.Because it's hard to find iron and ironstone,a lot of sword was needed to re-smelted.Moreover the former shape didn't reach the new war condition,so it's abandoned and there's little exsited(only inscribed in Tang poems and Tang drawings).

二、在唐末五代十国时期，受中西亚大砍刀的影响，各"国"因为此刀型比原有唐刀更加结实有力，先后装备这种刀型，加上当时各"国"贸易流通受政治影响极大，铁和铁矿石很难买到，故须将大量的刀剑重新回炉炼制此新刀型，加上原有刀型无法适应新的战争条件，导致此刀型被废弃，故现存实物极少（只在唐诗、唐画中有描绘）。

This invention relates to a new type nanometer crystal Fe-Zr-Nb-Si-Al-Cu series soft magnetic alloy super thin band and its process technology in which, the mother alloy is smelted by vacuum IF induction oven, an amorphous band is processed by a single quick cooling device to be processed by magnetic field heating at last to get the needed product with good soft magnet performance and iron core made by the super thin band improves its magnetic performance greatly.

本发明为一种新型纳米晶Fe-Zr-Nb-Si-Al-Cu系软磁合金超薄带及其制备工艺。由真空中频感应炉冶炼母合金，用单辊冷急装置制得非晶带，最后对非晶带进行磁场热处理，从而制得所需产品。本发明的合金超薄带具有优良的软磁性能，生产成本也较低。由本发明的超薄带制得的铁芯，其磁性能有很大改善，在国防和民用工业方面有广泛用途。

Polypropylene was modified by using smelted ash powder/ EPDM rubber blends as toughener.

将粉煤灰与三元乙丙橡胶混炼后与聚丙烯树脂熔融共混进行增韧改性。

Through comparing and analyzing the metallurgical effects, proper addition quantity of the modifier was 80 kg per heat. The experiment results showed that the modifier smelted the slag fast and reduced the oxidizability of the top-slag rapidly. Comparing with the original process, the average content of aluminum in the steel was increased by 0.06%, desulphurization ratio was increased by 89.25% and TFe was reduced by 0.6%, then stabilizing the production of aluminum containing steel.

试验中用改质剂代替原工艺中的精炼剂（Q235C钢种），通过对改质剂不同加入量的冶金效果进行对比分析，确定的改质剂加入量为每炉80 kg，试验表明，改质剂化渣快，能迅速降低顶渣的氧化性，与原工艺相比，钢中平均铝含量提高0.06%，脱硫率提高89.25%，渣中全铁降低0.6%，稳定了含铝钢的生产。

The optimal Seebeck coefficient is 268 for specimens smelted for 14 hours and cooled for 80 hours.

Seebeck 系数最佳值出现在熔炼时间14小时、降温时间80小时的试片，其值为268。

Through characteristic analysis on the vanadic titanomagnetite smelted in BF,it is realized that the injection of pulverized coal is advantageous to smelting vanadic titanomagnetite in blast furnace under the condition of complete combustion.

通过分析钒钛磁铁矿高炉冶炼的特殊性，认为在保证煤粉燃烧率的前提下，喷煤更有利于钒钛磁铁矿高炉冶炼，其煤比可以赶上普通矿高炉冶炼的领先水

Panzhihua v-bearing titanomagnetite has a titanium recovery of only 7% when smelted by traditional process,an enormous waste of titanium resource.

攀枝花钒钛磁铁矿使用传统工艺流程冶炼，钛资源的回收只有7%，浪费巨大。

The weight percentage for the components of the hyaline coating is as follows: SiO2 45 to 54 percent, B2O3 15 to 20 percent, one or more of Na2O, K2O and Li2O, 10 to 24 percent, one or more of TiO2, ZrO2 and ZnO, 6 to 18 percent , and the rest is one or more of CaO, MgO and CeO2. Firstly, the glass powder is mixed with the mill additions to be pulped and then plated on the surface of titanium or the titanium alloy. After being dried, the surface of titanium or the titanium alloy is directly used for a thermal hydrogen treatment or smelted at a temperature of 900 to 1, 000 DEG C for 15 to 30 minutes and then a hyaline coating with a thickness of 20 to 70 micrometers is formed on the surface of titanium or the titanium alloy; secondly, titanium or the titanium alloy plated with the coating is conducted a thermal hydrogen treatment. After the treatment technique is finished, the coating flakes off automatically in the process of cooling; and finally, a surface treatment is supplemented to meet the requirement of the workpiece surface.

该玻璃质涂层成分按重量百分比：45-54SiO2，15-20B2O3，10-24Na2O、K2O、Li2O中的一种或多种，6-18TiO2、ZrO2、ZnO中的一种或多种，余量CaO、MgO、CeO2一种或多种，将玻璃粉与磨加物混合制浆并涂覆在钛或钛合金表面，干燥后直接用于热氢处理，或在900-1000℃下熔烧15-30min，在钛或钛合金表面制得20-70微米玻璃质涂层，随后将制有该涂层的钛或钛合金置于氢气气氛下进行热氢处理，处理工艺结束后，涂层在冷却过程中自剥落，最后辅以表面处理即可满足工件表面要求。

Some metals can be smelted at low temperature.

3有些金属可以在低温下冶炼。

Yes, I will gather you and blow upon you with the fire of My overflowing wrath, and you will be smelted in the midst of it.

22：21 我必聚集你们，把我盛怒的火吹在你们身上，你们就在其中镕化。

The absorption and distribution of chromium were studied in ryeusing nutrient culture technique and pot experiment.

采用不同浓度K2CrO4(0，0.4，0.8和1.2 mmol/L)的Hoagland营养液处理黑麦幼苗，测定铬在黑麦体内的亚细胞分布、铬化学形态及不同部位的积累。

By analyzing theory foundation of mathematical morphology in the digital image processing, researching morphology arithmetic of the binary Image, discussing two basic forms for the least structure element: dilation and erosion.

通过分析数学形态学在图像中的理论基础，研究二值图像的形态分析算法，探讨最小结构元素的两种基本形态：膨胀和腐蚀；分析了数学形态学复杂算法的基本原理，把数学形态学的部分并行处理理念引入到家实际应用中。