After drying at low temperature, sintering, acid-washing, water-washing,filtration and drying at high temperature. Tantalate or Niobate compound was got finally. As compared with traditional proce...

用新工艺生产的钽或铌酸盐化合物用于制备钽或铌酸盐晶体时,从根本上克服了传统方法固体粉末混料不均匀等缺点所造成的质量不稳定的问题。

The results show that increasing the solids loading of slurry up to 45% allows minimizing deformation of green sheets during drying and sintering process effectively. When the content of monomers in shurry is 2%-4%, and the content of plasticizer in shurry is 3%-6%, green sheets with good strength and flexibility are obtained. The microstructures and the electric characteristics of PTCR chip thermistors were investigated. A five-layer chip PTCR thermistor with room resistance of 0.8Ω, temperature coefficient of resistance of 13.40%/℃, and ratio of maximum to minimum of resistance larger than 10^5 is successfully fabricated.

研究表明:浆料固相体积分数对坯体的乾燥及烧结行为有较大影响,当浆料固相体积分数在45%以上时,可有效避免制品乾燥和烧结过程中收缩过大而产生的变形开裂缺陷;当有机单体的质量分数为2%~4%,丙三醇的体积分数为3%~6%时,可获得有一定强度和柔韧性的生坯;研究了注凝成型PTCR陶瓷的微观结构及陶瓷元件的PTCR性能,成功地制备了层数为5、室温电阻为0.8Ω、电阻温度系数为13.40%/℃、升阻比大於10^5的多层片式PTCR元件。

The results show that increasing the solids loading of slurry up to 45% allows minimizing deformation of green sheets during drying and sintering process effectively. When the content of monomers in shurry is 2%-4%, and the content of plasticizer in shurry is 3%-6%, green sheets with good strength and flexibility are obtained. The microstructures and the electric characteristics of PTCR chip thermistors were investigated. A five-layer chip PTCR thermistor with room resistance of 0.8 Ω, temperature coefficient of resistance of 13.40%/℃, and ratio of maximum to minimum of resistance larger than 105 is successfully fabricated.

研究表明:浆料固相体积分数对坯体的干燥及烧结行为有较大影响,当浆料固相体积分数在45%以上时,可有效避免制品干燥和烧结过程中收缩过大而产生的变形开裂缺陷;当有机单体的质量分数为2%~4%,丙三醇的体积分数为3%~6%时,可获得有一定强度和柔韧性的生坯;研究了注凝成型PTCR陶瓷的微观结构及陶瓷元件的PTCR性能,成功地制备了层数为5、室温电阻为0.8 Ω、电阻温度系数为13.40%/℃、升阻比大于105的多层片式PTCR元件。

The effects the particle size in ternary system on sintering are also studied.

同时还对三元系统中原材料粒度对烧结的影响进行了研究。

Meanwhile, the catalyst were thermally stable and has a high resistance to sintering.

同时,催化剂具有较高的热稳定性,抗烧结。

It is found that proper sintering process can effectively improve the microstructure and thermal sensitive properties of the NTC thermistor materials.

分析表明,该烧结程序能有效改善热敏电阻材料的微观结构和热敏性能。

On the base of high temperature compression, the two-time hot pressing sintering was conducted at 1050℃,1090℃ and 1150℃.

结果表明,经过二次热压后,材料的相对密度和弯曲强度有了较大幅度的提高,在1090℃时,材料的相对密度达到了96%,弯曲强度达到605.5MPa。

An automatic sampling system was applied in SHAOGANG №6 sintering plant,it is made up of bucket type cutter sampler,chemical analysis sample preparation,sinter size analysis and tumbler test etc.

韶钢烧结厂新建的6号烧结机(360 m2)采用了一套自动采制样系统,该系统由采样、化学样制备、粒度分析和转鼓检测等的几个部分构成。

The blue-and-white porcelain is belongs the Underglaze Decoration ,which the colorant is based on a kind of cobalt mineral raw material, and then high temperature sintering.

青花瓷属于陶瓷釉下彩装饰,它是以含钴的矿物原料为着色剂,在高温下烧成。据考古资料表明,早在唐宋时代中国就有青花瓷的烧造,但直至元代才在景德镇出现成熟的青花瓷器。

To obtain uniform structure and excellent properties, their sintering temperatures arent too high, 1200℃ is the best.

所以欲获得显微结构均匀、性能优异的ZnO压敏陶瓷片,其烧结温度不能过高,以1200℃为宜。

第28/57页 首页 < ... 24 25 26 27 28 29 30 31 32 ... > 尾页
推荐网络例句

I didn't watch TV last night, because it .

昨晚我没有看电视,因为电视机坏了。

Since this year, in a lot of villages of Beijing, TV of elevator liquid crystal was removed.

今年以来,在北京的很多小区里,电梯液晶电视被撤了下来。

I'm running my simile to an extreme.

我比喻得过头了。