查询词典 moisture content

It cannot be utilised unless air dried to reduce moisture content to 30 % or less.

它不能利用，除非风干，以减少水分含量30％或以下。

Experiments and calculation has proved the effect of moisture content on longitudinal properties of tracheids cell wall is much less than the effect on macroscopic mechanical properties of wood.

12实验和理论计算均表明，含水率对管胞细胞壁纵向力学性能的影响程度明显小于其对木材宏观力学性能的影响。

The effect of moisture content on tensile strength of tracheids is less than the effect on MOE.

含水率对管胞的抗拉强度影响更不显著，饱水态下抗拉强度只比气干态低1.5-10％（平均值为2.7％）。

Further study indicates stiffening effect is related to MFA of tracheids、cross-section dimensions of samples and moisture content.

2木材微切片纵向拉伸时具有刚性强化特性，这是由于微纤丝沿着载荷重新取向，角度减小造成的。

The definite small leaf oak bough moisture content distribution rulemay for determine its bough biomass to provide the theory basis,greatly reduces the biomass investigation work load.

确定小叶青冈树干含水率分布规律可以为测定其树干生物量提供理论依据，大大减小生物量调查工作量。

Moisture content at all the soil depths was significantly higher (p≤0.05) in orange orchard than in forest on both the slopes.

两种坡地桔园3个深度的土壤水分含量均显著高于灌木林地相同深度的土壤水分。

In summary, the treatment of reducing the moisture content as soon as adding FGJ or MIX to the napier grass properly can make quality napier grass silages.

因此，适当降低象草的含水率同时添加FGJ或MIX能调制优质象草青贮

The results were as follows the airdried density ( moisture content of wood is 12%), the basic density and the ovendry density were 0.583 g·cm-3, 0.462 g·cm-3 and 0.507 g·cm-3 respectively, the airdried density was at the medium level in domestic wood species;the shrinkage coefficient of radial, tangential and volumetric were 0.099%, 0.183% and 0.296% respectively, the maximum swelling were 4.106%, 7.958% and 12.627% respectively;the ratio of tangential shrinkages to radial shrinkages was 1.5-1.9;the toughness was 52.12 kJ·m-2;the hardness of cross, radial and tangential section were 41.53 MPa, 31.41 MPa and 35.51 MPa respectively;the compressive strength parallel to grain was 44.50 MPa ;the modulus of elasticity in static bending and the bending strength were 12.63GPa and 127.31 MPa respectively;the shearing strength parallel to grain of radial and tangential were 8.76 MPa and 10.54 MPa respectively;the cleavage strength to grain of radial and tangential were 124.3 N·mm-1 and 138.6 N·mm-1 respectively.

结果表明大叶栎木材的气干密度（含水率为12％）、基本密度和全干密度分别为0.583 g·cm-3、0.462 g·cm-3和0.507 g·cm-3，气干密度属于国产木材的中等级水平；径向、弦向和体积干缩系数分别为0.099%、0.183%、0.296%，湿胀率依次为4.106%、7.958%和12.627%，差异干缩为1.5-1.9，其尺寸稳定性较好；冲击韧性为52.12 kJ·m-2，端面、径面和弦面硬度分别为41.53 MPa、31.41 MPa和35.51 MPa，顺纹抗压强度为44.50 MPa，抗弯弹性模量和抗弯强度分别为12.63 GPa和127.31 MPa，径面和弦面顺纹抗剪强度分别为8.76 MPa和10.54 MPa，抗劈强度依次为124.3 N·mm-1和138.6 N·mm-1。

Oven dried wood particles with moisture content less than 3% and HDPE were blended for 10 min to produce a homogenous mixture in a 10 l high-intensity laboratory mixer from Papenmeier.

烤箱用～弄干木材粒子湿气内容少於 3%，而且 HDPE 为 10 最小被混合从 Papenmeier 在一个 10 l 高强度实验室混合器中生产一个 homogenous 混合。

After the 24 h immersion in water, all specimens were oven-dried at 1050C for 24 h and weighed to calculate the moisture content based on the oven-dry weight.

在水里面的 24 h 浸渍之後，所有的样品在 1050C 为 24 h 是烤箱弄干的并且秤重计算被基於烤箱-干重量的湿气内容。

The split between the two groups can hardly be papered over.

这两个团体间的分歧难以掩饰。

This approach not only encourages a greater number of responses, but minimizes the likelihood of stale groupthink.

这种做法不仅鼓励了更多的反应，而且减少跟风的可能性。