Moreover, NaF as the mineralizer can promote the crystal nucleation and make the crystallization of zeolite ZSM-11 easier.

在固相体系合成中，矿化剂NaF起到了促进成核结晶的作用，使得合成纯相的ZSM-11沸石更容易。

The traditional mineralizer fluorine and sulfur are replaced by basalt and slag.

矿化剂选用了玄武岩和矿渣替代了传统的氟硫矿化剂。

The results showed that calcium aluminates powder could be obtained under lower temperature calcination after adding mineralizer to the raw materials.

研究表明：加入矿化剂后，可在更低温度条件下煅烧制备出铝酸钙粉，有利于节能减排。

The feasibility of chromium residue as cement mineralizer was proved theoretically and practically.

研究对比了掺加铬渣前后水泥制品、"三废"排放和装置消耗的各项性能指标，得出了铬渣作水泥矿化剂的最佳掺加量。

The inorganic mineralizer (K2SO4) plays a key role in controlling the nucleation and growth of the nanowires and the function of K2SO4 were also discussed.

研究发现，无机盐对一维纳米线形貌的控制至关重要，还详细讨论了K2SO4在α-FeOOH纳米线的成核和生长过程中所起的作用。

In this paper,Sn doped ZnO crystals were synthesized by hydrothermal method with 3M KOH as mineralizer.

采用水热法，在ZnO中添加SnCl2.2H2O作前驱物，3M KOH作矿化剂，温度430℃，填充度35%，反应24h，合成了掺杂Sn的ZnO 晶体。

The results showed that the feeding of mineralizer lowered the calcination temperature of α-Al2O3, promoted its crystal transformation and reduced its sodium oxide content.

矿化剂在煅烧α-Al2O3过程中的作用主要表现在降低煅烧温度、促进α-Al2O3晶型转化和降低α-Al2O3中氧化钠含量。

In this work, a large amount of uniform and high-dispersed α-FeOOH nanowires with diameters of 40 nm and lengths up to 2~3 μm were synthesized via a low-temperature hydrothermal route using K2SO4 as mineralizer.

本文以K2SO4为矿化剂，在100 ℃低温水热条件下，制备出大量形貌均一、高分散的直径约40 nm、长度为2~3 μm的α-FeOOH纳米线。

9H2O compounds as raw materials, urea as mineralizer.

采用水热法以乙酸锌和硫化钠为原料，尿素为矿化剂制备ZnS纳米粒子。

SnO2 nanocrystals were prepared by a hydrothermal method using SnCl45H2O as the raw material and Na2SO4 as mineralizer at lower reaction temperature and shorter time.

系统地研究了以SnCl45H2O为原料，以Na2SO4为矿化剂，采用水热法在较低温度下和较短的反应时间内制备结晶良好并均匀分散的SnO2纳米晶。