Therefore, the apatite-forming ability and the vitro bioactivity of merwinite prepared by sol-gel process have been certificated.

因此，溶胶－凝胶法合成的铁蔷薇辉石具有良好的诱导羟基磷灰石形成能力和体外生物活性。

The results showed that pure merwinite powers with dimensions of 1 to 3μm could be obtained at 1400℃. The HAp was obviously detected on merwinite after 7days of soaking, and the HAp crystalline on column-like merwinite after being soaked for l4days was in warm-like structure.

结果表明：在约1400℃的煅烧温度下可以得到纯相镁蔷薇辉石粉体，其粒径约为1~3μm；圆柱状镁蔷薇辉石在模拟体液浸泡7d后就能明显检测到表面有舟基磷灰石生成，浸泡14d后呈结晶较好的蠕虫状结构。

Pure merwinite powers were synthesized by sot-gel process, and the column-like merwinite with dimensions of l0mm×5mm was prepared under the 10MPa uniaxial pressure. The in vitro bioactivity of merwinite powers was studied by soaking them into simulated body fluid.

用溶胶－凝胶法制备出纯相镁蔷薇辉石(Ca3MgSi2O8)粉体，并在10MPa的轴向压力下，将其压制成尺寸为10mm×5mm的圆柱状块体，通过模拟体液浸泡对其体外生物活性进行研究。

An investigation to the microstructure of worn sample of dry vibratable materials for tundish working lining after using 40 hours shows that the materials changes the properties of slag by the chemical filter, increases the viscosity of slag, forms a dense layer at slag/refactories interface, then blocks the more slag penetrate in it. The complex phase formed at the interface, such as magnesiowusite and complex spinel et al, would absorb in more low-melting point minerals, then degrade its melting point and dissolve into slag, which forms low-melting point silicate phase, penetrates into dry vibratable materials along with Monticellite and Merwinite bonding phase by diffusion.

根据使用40小时后的中间包工作层残衬结构分析，其侵蚀机理为：干式料对渗入熔渣产生化学过滤作用，增大熔渣粘度，在干式料/熔渣界面形成致密结构，阻碍熔渣的进一步渗透；随着反应的进行复合矿物中熔剂含量的增多，熔点降低，溶于熔渣形成低熔点的硅酸盐相，并沿着干式料中的钙镁橄榄石和镁蔷薇辉石等结合相向干式料基质中扩散渗透。