The results show that the effect of addition or no-addition of degasser on grain refinement of Al-5.0%Si alloy ingot is...

结果表明，除气剂的添加与否对Al-5%Si合金铸锭组织的细化没有影响，铸锭由粗大的柱状晶组织构成；采用合适的超声波处理时间，Al-5%Si合金铸锭的等轴晶获得率大幅度提高，可使整个铸锭组织变为细化的等轴晶组织；超声波振动时间过长将导致铸锭内气孔的增加；根据克劳修斯-克拉柏龙方程，某一强度的超声波引起的压力冲击波作用，导致液相转变为固相，引起了超声波的细晶作用。

Si ingots were studied under different ultrasonic frequencies,e g without degasser and ultrasonic,with degasser only,with degasser and ultrasonic under constraint cooling in the bottom of the ingot.

研究了不同超声波频率下熔体处理方法对Al-1.65%Si铸锭除气的影响，如：没有添加除气剂和超声波处理、只添加除气剂不进行超声波处理、铸锭底部强冷情况下既添加除气剂又进行超声波处理的情况。

The effects of the melt treatment methods on the degassing efficiency of ultrasonically refined Al-1.65%Si ingots were studied under different ultrasonic frequencies,e g without degasser and ultrasonic,with degasser only,with degasser and ultrasonic under constraint cooling in the bottom of the ingot.

研究了不同超声波频率下熔体处理方法对Al-1.65%Si铸锭除气的影响，如：没有添加除气剂和超声波处理、只添加除气剂不进行超声波处理、铸锭底部强冷情况下既添加除气剂又进行超声波处理的情况。

The movement of the water-cooled mould relative to the ingot is essentia...

同时认为，对于抽锭式重熔过程来讲，结晶器与钢锭之间的相对移动，实际上是接触钢锭表面的渣壳内侧渣璧相对于被拉裂的与结晶器接触的渣壳外侧渣壁的剪切运动。

By means of thermo—elastic-plastic finitive element method, the thermo—mechanical loading chart of the ingot mould in working cycle is obtained; with this chart as a control factor, multicycle experiment is carried out on a thermo—mechanical simulater, resembling the circumstance of the real working condition.

即用热弹塑性有限元法获得钢锭模一个使用周期内的热—力载荷谱，在热力模拟实验机上用该热—力载荷谱控制进行多周期模拟实验分析。

In order to further understand the organization and performance of the product extruded from beryllium bronze,the nonuniformity of ingot casting organization extruded from beryllium bronze,the quenching macrocrystalline ring organization and layer structure of extrusion bars,the nonuniformity in mechanics,and extrusion effects were analyzed.

为了进一步了解铍青铜正向挤压制品的组织和性能，分析了铍青铜挤压铸锭组织的不均匀性、挤压棒材淬火后的粗晶环组织、以及挤压棒材的层状组织；同时对挤压棒材力学性能的不均匀性和挤压效应进行了分析。

A brief introduction to the preparation of metallographic specimen of NdFeB ingot or strip casting are given in this article.

文章介绍了钕铁硼铸块或速凝薄带的金相样品的制备方法。

The minority carrier lifetime scan mapping along the multicrystalline ingot was obtained by means of Microwave Photo Conductive Decay.

应用微波光电导衰减仪测得了铸造多晶硅硅锭沿生长方向少子寿命的分布图。

Listen,point and check your answers.

听，指出并且检查你的答案。

Warming needle is one of effective treatment methods for knee arthralgia aggravated by cold,and it is simple,safety,so it should be developed in clinical acupuncture and moxibustion extensively.

但以本院科针灸门诊在2005年1月—2006年6月期间共收治膝痛患者100余例，经过临床的诊断后，其中施以温针治疗的48例，疗效显著，报道如下。1临床资料本组病例48