Theoretical analyses show the feasibility of this induction heating, and preliminary experimental results show that it takes only a few seconds to produce the gold -silicon eutectic phase,despite the fact that the thickness of the gold layer is less than a skin - layer depth and no additional susceptor is required.

理论上分析了该方法的可行性，初步试验结果表明，虽然金膜厚度低于感应趋肤深度，但在没有应用感应加热基座的情况下，几秒钟内就形成了金硅共晶相。

The solute redistribution caused by fluid flow is a main factor for the formation of unregular and other eutectic morphologies.

流体流动造成的溶质重新分配是产生非规则层片共晶及其它形态共晶的主要原因。

It is found that with the increase of flow velocity,the Al-Al2Cu eutectic morphologies changes from regular laminae to unregular laminae,unregular rods up to regular rods and the laminar spacingsλ have a little increase.

发现增加流速使Al－Al_2Cu共晶由规则层片状向非规则层片状、非规则棒状、直至规则棒状共晶形态转化，同时层片间距λ略有增加。

Consolidation test is a important link of obtaining mechanical properties index of soil and coefficient of compressibility gained through the test is a key data to evaluating the compressibility of soil. Consisting of solid phase and liquid phase of the salty soil is different from the non-salty one. Eutectic salt in soil may exist as liquid phase, solid phase or both of them and these phases can interconvert because it is affected by temperature, Na_2SO_4 content, water content. Especially when temperature drops, Na_2SO_4 will crystallize and expand, namely salt expansion of soil. These particularities make soil sample put in environmental cabinet when consolidation test is going on. So soil sample can be compressed by temperature controlling system under a set temperature.From experiment, the formulae counting coefficient of compressibility of salty soil have been given.

土的固结试验，是取得土的力学性质指标的一个重要环节，因为土的固结试验所取得的压缩系数，对评价土的压缩性是一个关键数据，但由于盐渍土的固相、液相组成和非盐渍土不同，土中易溶盐受温度、含盐量、含水量的影响可以以液相、固相、液相和固相混合形式存在，且它们之间的存在形式可以相互转换，尤其是当温度下降时，硫酸钠便结晶产生体积膨胀，即盐胀，这些特殊性就使得在进行硫酸盐渍土的固结实验时，须将土样放置在环境箱中，通过温度控制系统使土样在设定的温度下受压产生变形。

First, the grain will be increase at double speed, second, a large scale "structure" builds by collision and coalescence of favorably oriented particles (namely primary phase coalescence), third, primary phase entraps the eutectic structure.

分别研究了浇注温度、拉坯速度、冷却速度等工艺参数对合金组织的影响，结果显示：在本实验条件下，浇注温度以650荀70'℃为宜；拉坯速度以8.4一9.6 cm/min为宜；二次水冷流量控制在1.0一2.0比为宜。综合考虑磁场强度B和冷却速度对非树枝晶组织初生相平均尺寸D和形状因子S影响的数学表达式为：D=A一ns二；。

That if the process can produce much liquid phase during the sintering, and which can become into completely-crystal needle-shap or aborization or bar-shap calcium ferrite instead of glass in the cooling process; if the magnetite is interweaved by the caking into the melting corrosion structure, the granular structure or the eutectic structure instead of exiling in the massive isolation; if the mount of the poreis is little, and uniformitly distributing; if the grain is little; if the organizational structure is symmetrical, all of which can improve the quality of the sintering.

另外还归纳出有利于强度提高的工艺参数和操作制度。分析工业试验和水钢现行生产的矿物组成、结构表明，水钢烧结矿以他形晶磁铁矿为主，铁酸钙为主要的粘结相，多形成熔蚀结构、粒状结构和共晶结构，强度较高；而在台车边缘和表层，由于存在较严重边缘效应和点火温度较低，使该区域的烧结矿组织结构疏松，局部呈蜂窝状或薄壁大孔状，铁酸钙较少而硅酸二钙和玻璃质较多，形成骸晶状结构和磁铁矿连晶，强度较低，致使返矿升高。

The Al-Al2Cu eutectic were disorganized and furcated by high magnetic field, which in turn accumulated inner stress and gave rise to the apparent increase of the dislocation densities.

强磁场影响了定向凝固Al-Al2Cu共晶合金的生长过程，使其组织变得紊乱扭曲，晶粒内部应力增加，产生了大量位错。

This kind of defects can be eliminated by controlling S content, avoiding eutectic sulfide, improving sulfide distribution and meliorating quenching process to minish quenching stress.

可以通过控制硫的含量、避免产生共晶硫化物，改善其分布状态，改善淬火工艺以减小淬火应力来消除。

Through the morphological observation on silicon particles of Al-Si-Cu-Mg cast alloy, it is found, that during solution heat treatment the evolution of eutectic silicon morphology and their effect on mechanical property can be classified into three stages. In the initial stage, necking, stubbing and fragmentation of silicon particles results in an improvement in plasticity of the alloy. In the intermediate stage, the mechanical properties of the alloy attain peak values due to the spheroidization of silicon particles.

在固溶处理过程中，共晶硅相形貌发生了显著的变化，并对合金的性能产生了很大的影响；通过定量金相分析，共晶硅相形貌的演变及其对合金力学性能的影响可划分为三个阶段：固溶初期硅相的熔断和钝化使合金的塑性得到显著的提高；固溶中期以粒化为主，合金的力学性能达到了峰值；固溶后期硅相的粗化符合LSW粗化模型，硅相形貌呈现棱角小面特性，合金性能降低。

In all experimented cooling conditions the alloy with the addition of 0.15% Mg possesses the coarsest eutectic structure,while the alloy with the 0.3% Mg addition the finest structure in eutectics.

在试验范围内，Al-Si11.0合金中加入0.15%镁时，共晶组织变得较粗；而当镁的加入量增加到0.3%时，其共晶组织比Al-Si11.0合金细得多，分析了出现这一结果的原因。

However, as the name（read－only memory）implies, CD disks cannot be written onorchanged in any way.

然而，正如其名字所指出的那样，CD盘不能写，也不能用任何方式改变其内容。

Galvanizes steel pallet is mainly export which suits standard packing of European Union, the North America. galvanizes steel pallet is suitable to heavy rack. Pallet surface can design plate type, corrugated and the gap form, satisfies the different requirements.

镀锌钢托盘多用于出口，替代木托盘，免薰蒸，符合欧盟、北美各国对出口货物包装材料的法令要求；喷涂钢托盘适用于重载上货架之用，托盘表面根据需要制作成平板状、波纹状及间隔形式，满足不同的使用要求。