The main reason for protect invalidation of coating is the disfigurements existing in the surface and interior of coating, which can be decreased by improvement of electroless nickel plating solution and strict control over technological parameters.

导致Ni-P层防护失效的主要原因来自于试样表面及镀层内部的缺陷，通过改进化学镀镍工艺配方和严格控制工艺参数能减少镀层缺陷的产生。

Although talc has been widely used in coating formulations in Europe, its application for coating purposes in Asia still awaits development.

虽然滑石粉应用在涂布配方，在欧洲已非常普遍，但是在亚洲地区的使用仍待开发。

The properties of TCC with ATS were as good as the TCC with HTS, better that the requirement of standard GB8744-88 for semi-graphitic carbon block. As good as TCC with HTS in industrial cells, the TCC with ATS also reduces the sodium penetration to cathodic lining, no tear-off of the coating was found after starting up of the cells. As compared with reference cells, the operation of coating cells with ATS was also improved to keep good shape of cell chamber, reduce the formation of sludge on the cell bottom, and gain more uniform current distribution. The ohmic drop of TCC cell bottom was lessened by 11. 5mV. The current efficiency was increased by about 1. 48% in average. It was estimated that the TCC life could be 44 months. Obviously, the TCC with ATS could also improve the performance of industrial cells, save energy, and increase the cell life.

对常温固化涂层槽的考核表明，与高温固化涂层槽一样，阴极内衬对钠的吸收减少，钠渗透速度减缓，从而减小钠膨胀危害，减少了铝电解槽早期破损的几率；启动后，常温固化涂层不脱落，同样具有良好的粘接性能；与对比槽相比较，常温固化涂层槽正常生产后，阴极表面干净、光洁，无沉淀或结壳，炉膛规整，阴极、阳极电流分布均匀，炉底压降降低（平均降低11.5mV），电流效率提高（平均提高1.48％）；涂层在电解槽内存在的时间可达到44个月以上；常温固化涂层同样可以起到改善电解槽工作状态、节能降耗、延长槽寿命的作用。

The properties of TCC with ATS were as good as the TCC with HTS, better that the requirement of standard GB8744-88 for semi-graphitic carbon block.AbstractAs good as TCC with HTS in industrial cells, the TCC with ATS also reduces the sodium penetration to cathodic lining, no tear-off of the coating was found after starting up of the cells.As compared with reference cells, the operation of coating cells with ATS was also improved to keep good shape of cell chamber, reduce the formation of sludge on the cell bottom, and gain more uniform current distribution. The ohmic drop of TCC cell bottom was lessened by ll.SmV. The current efficiency was increased by about 1 .48% in average. It was estimated that the TCC life could be 44 months.Obvi

对常温固化涂层槽的考核表明，与高温固化涂层槽一样，阴极内衬对钠的吸收减少，钠渗透速度减缓，从而减小钠膨胀危害，减少了博士学位论文摘要铝电解槽早期破损的几率；启动后，常温固化涂层不脱落，同样具有良好的粘接性能；与对比槽相比较，常温固化涂层槽正常生产后，阴极表面干净、光洁，无沉淀或结壳，炉膛规整，阴极、阳极电流分布均匀，炉底压降降低(平均降低11.smv)，电流效率提高(平均提高1.48%)；涂层在电解槽内存在的时间可达到44个月以上；常温固化涂层同样可以起到改善电解槽工作状态、节能降耗、延长槽寿命的作用。

A container (1) containing a coating composition the container comprising a container body (21) and a lid (7), the lid comprising a collar (11) and a disc (12), the container body having an opening provided with a screw-thread (5) cooperable with a screw-thread (6) on the collar and closeable by said lid characterised in that the disc is formed of polyethylene terephthalate which is sufficiently transparent to allow the coating composition to be visible therethrough.

一种容纳涂敷组合物的容器(1)，该容器包括容器主体(21)和盖子(7)，该盖子包括套环(11)和盘(12)，该容器主体具有一设置有螺纹(5)的开口(2)，该螺纹可与该套环上的螺纹(6)配合使用，并且该容器主体可由该盖子封闭，其特征在于，该盘由聚对苯二甲酸乙二醇酯形成，其足够透明以便使得透过该盖子可看到该涂敷组合物。

The coating on the metal is about is divided into 2 type: thermoplastic coatings and thermosetting resin coating.

金属上的涂层大约分为2种：热塑性涂层和热固性树脂涂层。

The thermostability of the coating was investigated by thermal analysis, and the maximum sustainable temperature for the coating was as high as 280℃.

通过热分析手段考察了该涂层的热稳定性，涂层使用温度可达280℃。

The effects of pulse parameters such as pulse width Ton, pulse interval Toff, pulse frequency f, pulse current density J on the morphology ,grain size , hardness, internal stress and orientation of coating , and coherence of coating to sucbstrate have been examined .

研究了脉冲电镀参数：脉冲宽度Ton ，脉冲间隔Toff，脉冲频率f，脉冲电流密度 J对镀层微观形貌、颗粒大小、硬度、与基体结合力的影响，分析了镀层内应力、择优取向与脉冲参数的关系。

The electrochromic reaction of this coating in theliquid electrolyte is reversible.X-ray diffraction was used to analyse the coating,and the result shows that the original WO_3 film is triclinic WO_3 while the colouredlayer is orthorhomic H_...

X 光衍射实验发现，变色后的涂层由原来的三斜 WO_3晶体变成了 H_(0.1)WO_3斜方晶体。本文还用扫描电子显微镜对热处理前后涂层的表面形貌进行了分析。

The latest energy-saving environmental protection structure series waterproof coating applied to concrete, cement, masonry, metal, PVC and other materials, roofing, inside the wall, room, water-proof underground facilities, water works; anti-aging, can withstand long-term water immersion; high and low temperature resistance and ultra-violet radiation, yet energy-saving effect; no irritating smell, does not contain harmful substances; non-combustible; bonded resilient seamless, waterproof coating seamless.?

适用于混凝土、水泥、砖石、金属、PVC等材料的屋面、内外墙、卫生间、地下设施的防水、止水工程；抗老化，能长期抵御水的浸泡；耐高低温及紫外线照射，且具节能效果；无刺激性气味，不含有害物；不可燃；粘结力强，无接缝，防水涂层浑然一体。

However it can often be frust ating for a child when people are unable to pronounce their name.

但它往往可以令人沮丧的一个孩子当人们无法断言他们的名字。

All these compounds were obtained from this genus for the first time. Compound, 4-cumylphenol, was a new nature product.

所有化合物均为首次从本属海藻中分离得到，其中4cumylphenol为新天然产物。